NASA NTRS2016

Modifying a Commercial Centrifuge to Reduce Electromagnetic Interference and Evaluating Functionality of Ultrasound Equipment

The Project Management and Engineering Branch (SF4) supports the Human Health and Performance Directorate (HH&P) and is responsible for developing and supporting human systems hardware for the International Space Station (ISS). When a principal investigator's (PI) medical research project on the ISS is accepted, SF4 develops the necessary hardware and software to transport to the ISS. The two projects I primarily worked on were the centrifuge and ultrasound projects. Centrifuge: One concern with spacecraft such as the ISS is electromagnetic interference (EMI) from onboard equipment, typically from radio waves (frequencies of ~3 kHz to ~300 GHz), which can negatively affect nearby circuitry. Standard commercial centrifuges produce EMI above safety limits, so my task was to help reduce EMI production from this equipment. Two centrifuges were tested: one unmodified as a control and one modified. To reduce EMI below safety limits, one centrifuge was modified to become a Faraday shield, in which significant electrical contact was made between all regions of the centrifuge housing. This included removing non-conductive paint, applying conductive fabric to the lid and foam sealer, adding a 10,000 μF decoupling capacitor across the power supply, and adding copper adhesive-mount gaskets to the housing interior. EMI testing of both centrifuges was performed in the EMI/EMC Control Test and Measurement Facility. EMI for both centrifuges was below safety limits for frequencies between 10 MHz and 15 GHz (pass); however, between 14 kHz and 10 MHz, EMI for the unmodified centrifuge exceeded safety limits (fail) as expected. Alternatively, for the modified centrifuge with the Faraday shield, EMI was below the safely limit of 55 dBμV/m for electromagnetic frequencies between 14 kHz and 10 MHz. This result indicates our modifications were successful. The successful EMI test allowed us to communicate with the vendor what modifications they needed to make to their commercial unit to meet our specifications and to understand what needs to be done in lab to the new centrifuge. Our modifications will provide a standard for readying centrifuges for future missions. Once the new modified centrifuge arrives by the vendor, it will need to undergo EMI testing again for validation. The centrifuge is also in the process of compatibility testing with a custom stowage drawer, which is an ongoing project in SF4. Both of these items will be payloads on future missions to the ISS for various research purposes. Ultrasound: ISS currently has an onboard ultrasound (Ultrasound 2 system) for research and medical purposes. Every piece of medical flight hardware has an equivalent ground-unit so instrumentation can be routinely evaluated and transported to the ISS if necessary. The ground-unit ultrasound equipment must be evaluated every six months using a task performance sheet (TPS). A TPS is a document, written by the appropriate scientists and engineers, which describes how to run equipment and is written in such a way that astronauts with unspecialized training can follow the tasks. I was responsible for performing six TPSs on a combination of three ultrasounds and two video power converters (VPCs). Performing a TPS involves checking out and computationally documenting each piece of equipment removed from storage locations, setting up hardware and software, performing tasks to verify functionality, returning equipment, and logging items back into the computerized system. My work revealed all ground-unit ultrasounds were functioning properly. Because of proper function, a discrepancy report (DR) did not have to be opened. The TPS was then passed along to the Quality Engineering (QE) for review and ultimately given to Quality Assurance (QA). Other projects: In addition to my main projects, I participated in other tasks including troubleshooting an EEG headband, volunteering for an ultrasound training research study, and conformal coating printed circuit boards. My internship at SF4 has helped me understand how space systems hardware development for the ISS fits into NASA's mission and vision.

Greening, Gage J.↗

NASA NTRS2017

An Introduction to Atomic Layer Deposition

Atomic Layer Deposition has been instrumental in providing a deposition method for multiple space flight applications. It is well known that ALD is a cost effective nanoadditive-manufacturing technique that allows for the conformal coating of substrates with atomic control in a benign temperature and pressure environment. Through the introduction of paired precursor gases, thin films can be deposited on a myriad of substrates from flat surfaces to those with significant topography. By providing atomic layer control, where single layers of atoms can be deposited, the fabrication of metal transparent films, precise nano-laminates, and coatings of nano-channels, pores and particles is achievable. The feasibility of this technology for NASA line of business applications range from thermal systems, optics, sensors, to environmental protection. An overview of this technology will be presented.

ALD↗

NASA NTRS2019

Applications of Atomic Layer Deposition in the Modification of Carbon Nanotubes

Atomic Layer Deposition (ALD) is a cost-effective nanoadditive-manufacturing technique that allows for conformal coating of substrates with atomic control in a benign temperature and pressure environment. Using paired precursor gases, thin films can be deposited on flat or textured surfaces ranging from glass, polymers, aerogels, and metals. Through atomic layer control, where single layers of atoms are deposited, fabrication of metal transparent films, nano-laminates, and coatings of nano-channels and pores is achievable. Reaction mechanisms in ALD are normally self-limiting, allowing for atomically accurate control of nanometer (nm) thicknesses. Therefore, high uniformity and precise thickness control make ALD an attractive process for the creation of novel nano-scale devices. Decreases in resistivity and density of electrical wire are needed to improve the function of electronics, electric motors and cables. Such improvements may be accomplished by adding ballistically conducting, metallic carbon nanotubes (CNT) to Cu. ALD was used to coat multiple substrates including CNT with Cu in an effort to make CNT-Cu composites which is more conductive and less dense than Cu. In addition, ALD can be used to as a method to deposit the catalyst layer seed layer for CNT growth using Ni. The ALD of copper metallic films can follow multiple reaction pathways depending on the ALD precursors used. For this work the reaction pathway was deposition of copper oxide and then post process annealing in a hydrogen environment. Copper(II) diacetylacetonate (Cu(acac)2) and ozone are used as precursors for copper oxide. As-deposited copper oxide films prepared at 180°C resulted in a growth per cycle of 1.0 A/cycle with low film resistivity.

Dwivedi, Vivek H.↗

NASA NTRS2023

A Multi-Sensor, Low Volume, Automated Culture System for Space Biology Experiments

Optical density (absorbance) is commonly used in microbiology to measure cell concentration and other colorimetric indicators. It is the main type of bioscience data returned from the BioSentinel small spacecraft mission, which was recently launched as a secondary payload on Artemis I. The flight unit takes absorbance measurements of yeast cultures at 570 nm, 630 nm, and 850 nm to track cell concentration and oxidation-reduction (redox) state of the metabolic indicator dye alamarBlue over time [1]. Because the data returned from a small spacecraft mission is necessarily limited, BioSentinel uses a specialized ground-based experiment apparatus to map the absorbance data onto several other parameters. This culture apparatus is composed of a polycarbonate base and lid which contain ports for several commercial sensors, including a standard 12 mm dissolved oxygen probe, gaseous CO2, fluid pressure, and two micro-probes for measuring pH and redox potential. It also contains a pressure relief valve, a rubber membrane for culture interaction, and a 12mm port for the custom optical probe designed to match in-flight measurements. Modules in two corners expand the culture volume into narrow columns, enabling solid-state optical density measurement and dielectric spectroscopy. The apparatus can be fit to a plate for magnetic stirring. The apparatus’s optical probe allows mapping between the flight unit’s optical data and the additional parameters measured by the ground-based experiments. Within the probe, a linear actuator pulls a plunger, drawing culture volume into the optical path. The actuator then pushes out the plunger and culture volume, cleaning any stray yeast from the inside surface of the probe. The probe chassis is 3D-printed from biocompatible resin with the optoelectronics cured inside an optically clear conformal coat which functions as a lens. To optimize the probe’s dimensions, including optical path, a test harness was developed to manipulate and measure distance while the LED light sources and photodiode detector are in operation. The test harness was composed of two 3/64” thick polycarbonate plates mounted to a set of calipers. The LEDs and photodiode were mounted on the outside of each plate. A cuvette of sample fluid was then clamped between the plates in line between the LEDs and photodiode. The test harness generated a 78% signal change between water and a dye standard for the green (570 nm) LED, a 90% signal change for the red (630 nm) LED, and a 25% signal change between water and overgrown yeast for the infrared (850 nm) LED. The improvements to the ground experiment apparatus (culture volume reduction, inclusion of an optical probe to measure flight-like optical data, and magnetic stirring for culture homogeneity) allow for more flight-like measurements to be taken and more accurate mapping of these additional parameters to the optical data returned from the flight unit. This enhancement to mission science return will give insight into how deep space radiation may affect human biology for future long-term space exploration.

Multi-Sensor↗

NASA NTRS1991

A conformal oxidation-resistant, plasma-polymerized coating

A comparative study was made of the surface recession (etching) of thin films of plasma polymerized tetrafluoro ethylene (PPTFE), polytetrafluoro ethylene (PTFE), and ion-beam sputter deposited polytetrafluoro ethylene (SPTFE) exposed to ground-state atomic oxygen downstream from a nonequilibrium radio-frequency O2 plasma. At 22 C, the etch rates for PTFE, SPTFE, and PPTFE were in the ratio of 8.7:1.8:1.0. A thin, conformal coating of PPTFE (etch rate of 0.3 nm/h at 22 C) was found to protect an underlying cast film of a reactive polymer, cis-1,4 polybutadiene, against ground-state atomic oxygen attack for the time required to fully etch away the PPTFE coating. From ESCA analysis, PTFE exhibited only minor surface oxidation (uptake of 0.5 atom percent O) upon etching, its F/C ratio decreasing slightly from 2.00 to 1.97; PPTFE exhibited considerable surface oxidation (uptake of 5.9 atom percent O) intermediate between those of PTFE and PPTFE, with a decrease in F/C ratio from 1.73 to 1.67. A plasma-polymerized fluorocarbon coating such as PPTFE might be useful for space applications to protect polymers that are vulnerable to oxidation or degradation by oxygen atoms.

Golub, Morton A.↗

NASA NTRS2013

Medicine Delivery Device with Integrated Sterilization and Detection

Sheam, Michael J.↗

NASA NTRS2013

Medicine Delivery Device with Integrated Sterilization and Detection

Sterile delivery devices can be created by integrating a medicine delivery instrument with surfaces that are coated with germicidal and anti-fouling material. This requires that a large-surface-area template be developed within a constrained volume to ensure good contact between the delivered medicine and the germicidal material. Both of these can be integrated using JPL-developed silicon nanotip or cryo-etch black silicon technologies with atomic layer deposition (ALD) coating of specific germicidal layers. The application of semiconductor processing techniques and technologies to the problems of fluid manipulation and delivery has enabled the integration of chemical, electrical, and mechanical manipulation of samples all within a single microfluidic device. This approach has been successfully applied at JPL to the automated processing, detection, and analysis of minute quantities (parts per trillion level) of biomaterials to develop instruments for in situ exploration or extraterrestrial bodies. The same nanofabrication techniques that are used to produce a microfluidics device are also capable of synthesizing extremely high-surface-area templates in precise locations, and coating those surfaces with conformal films to manipulate their surface properties. This methodology has been successfully applied at JPL to produce patterned and coated silicon nanotips (also known as black silicon) to manipulate the hydrophilicity of surfaces to direct the spreading of fluids in microdevices. JPL's ALD technique is an ideal method to produce the highly conformal coatings required for this type of application. Certain materials, such as TiO2, have germicidal and anti-fouling properties when they are illuminated with UV light. The proposed delivery device contacts medicine with this high-surface-area black silicon surface coated with a thin-film germicidal deposited conformally with ALD. The coating can also be illuminated with ultraviolet light for the purpose of sterilization or identification of the medicine itself. This constrained volume that is located immediately prior to delivery into a patient, ensures that the medicine delivery device is inherently sterile. An additional benefit to integrating a high-surface-area template within the fluid channel of a medicine delivery device is that one can envision a number of different functional coatings that could facilitate the capture and analysis of either microbial contaminants or the medicine itself. For example, one could attach antibodies or some other binding agent with a specific affinity to the silicon nanotip template. Once a target molecule or microbe is bound to the high-surface- area template, one could use an optical analytical technique such as fluorescence or adsorption to determine the identity and potentially the concentration of the species of interest. By illuminating the bound species from the back, it may also be possible to probe only the molecules with an evanescent wave, making detection of the species from the front side of the device much simpler.

Shearn, Michael J.↗

NASA NTRS2009

Multiscale Computer Simulation of Tensile and Compressive Strain in Polymer- Coated Silica Aerogels

While the low thermal conductivities of silica aerogels have made them of interest to the aerospace community as lightweight thermal insulation, the application of conformal polymer coatings to these gels increases their strength significantly, making them potentially useful as structural materials as well. In this work we perform multiscale computer simulations to investigate the tensile and compressive strain behavior of silica and polymer-coated silica aerogels. Aerogels are made up of clusters of interconnected particles of amorphous silica of less than bulk density. We simulate gel nanostructure using a Diffusion Limited Cluster Aggregation (DLCA) procedure, which produces aggregates that exhibit fractal dimensions similar to those observed in real aerogels. We have previously found that model gels obtained via DLCA exhibited stress-strain curves characteristic of the experimentally observed brittle failure. However, the strain energetics near the expected point of failure were not consistent with such failure. This shortcoming may be due to the fact that the DLCA process produces model gels that are lacking in closed-loop substructures, compared with real gels. Our model gels therefore contain an excess of dangling strands, which tend to unravel under tensile strain, producing non-brittle failure. To address this problem, we have incorporated a modification to the DLCA algorithm that specifically produces closed loops in the model gels. We obtain the strain energetics of interparticle connections via atomistic molecular statics, and abstract the collective energy of the atomic bonds into a Morse potential scaled to describe gel particle interactions. Polymer coatings are similarly described. We apply repeated small uniaxial strains to DLCA clusters, and allow relaxation of the center eighty percent of the cluster between strains. The simulations produce energetics and stress-strain curves for looped and nonlooped clusters, for a variety of densities and interaction parameters.

Good, Brian↗

NASA NTRS2020

Mitigation of Silver Ion Loss from Solution by Polymer Coating of Metal Surfaces, Part II

“Spacecraft potable water systems require a biocidal agent that effectively provides both immediate and residual disinfection over long periods of time. Ionic silver (Ag+) is a leading candidate for this application, but suffers from rapid concentration loss due to interactions with the metal storage containers and tubing. In order to maintain biocidal efficacy in systems with long periods of dormancy and to reduce the required rate of Ag+ injection, it is necessary to develop alternative materials and coatings for certified metal alloys that significantly reduce the Ag+loss.”1In this work, we continue our investigation of vapor-deposited parylene (AF4, and now C) polymers as conformal barrier coatings under long-term (ca. 1-year) immersion in ca. 400 ppb Ag+. The performanceof internal coatings in tubing/two-ferrule fitting systems is characterized. We report successful “aging” and high concentration Ag+pretreatment of parylene coatings for quantitative reduction of Ag+loss rates. In addition, we observe long-term blister-free adhesion of mechanically anchored parylene-AF4 on nano-structured Ti-6Al-4V alloy and chemically bonded parylene-C on 316L stainless steel. Finally, we report preliminary experiments with mechanical and chemical anchoring of laboratory-deposited parylene-C on 316L.

Silver↗

NASA NTRS1999

Nanometer X-ray Lithography

New developments for X-ray nanomachinging include pattern transfer onto non-planar surfaces coated with eletrodeposited resists using synchrotron radion X-rays through extremely high-resolution masks made by chemically assisted focused ion beam lithography.

X-rays↗

NASA NTRS2005

Polymer Crosslinked 3-D Assemblies of Nanoparticles: Mechanically Strong Lightweight Porous Materials

In analogy to supramolecular assemblies, which are pursued because of properties above and beyond those of the individual molecules, self-standing monolithic three-dimensional assemblies of nanoparticles also have unique properties attributed to their structure. For example, ultra low-density 3-D assemblies of silica nanoparticles, known as silica aerogels, are characterized by large internal void space, high surface area and very low thermal conductivity. Aerogels, however, are also extremely fragile materials, limiting their application to a few specialized environments, e.g., in nuclear reactors as Cerenkov radiation detectors, in space (refer to NASA's Stardust Program) and aboard certain planetary vehicles (thermal insulators on Mars Rovers in 1997 and 2004). The fragility problem is traced to well-defined weak points in the aerogel skeletal framework, the interparticle necks. Using the surface functionality of the nanoparticle building blocks as a focal point, we have directed attachment of a conformal polymer coating over the entire framework, rendering all necks wider. Thus, although the bulk density may increase only by 3x, the mesoporosity (pores in the range 2-50 nm) remains unchanged, while the strength of the material increases by up to 300... Having addressed the fragility problem, aerogels are now robust materials, and a variety of applications, ranging from thermal/acoustic insulators to catalyst supports, to platform for sensors, and dielectrics are all within reach. Our approach employs molecular science to manipulate nanoscopic matter for achieving useful macroscopic properties, and in our view it resides at the core of what defines nanotechnology. In that spirit, this technology is expandable in three directions. Thus, we have already crosslinked successfully amine-modified silica, and we anticipate that more rich chemistry will be realized by been creative with the nanoparticle surface modifiers. On the other hand, although we do not expect orders-of-magnitude increase in strength, nevertheless, by varying the polymer we expect to impart other properties such as hydrophobicity, thermal stability and perhaps electrical conductivity. Besides polymers, crosslinkers will include metals and ceramics (e.g., through POSS precursors). Finally, network morphology directs load dissipation, and of approximately 30 different crosslinked oxide aerogels, vanadia, whose structure is fibrous rather than particulate, yields a much stronger (by 4..) material than silica of the same density. It seems imperative to implement control of network morphology, even through templating.

Leventis, Nicholas↗

NASA NTRS2006

Chemical, Physical, and Mechanical Characterization of Isocyanate Cross-linked Amine-Modified Silica Aerogels

We describe a new mechanically strong lightweight porous composite material obtained by encapsulating the skeletal framework of amine-modified silica aerogels with polyurea. The conformal polymer coating preserves the mesoporous structure of the underlying silica framework and the thermal conductivity remains low at 0.041 plus or minus 0.001 W m(sup -1 K(sup -1). The potential of the new cross-linked silica aerogels for load-carrying applications was determined through characterization of their mechanical behavior under compression, three-point bending, and dynamic mechanical analysis (DMA). A primary glass transition temperature of 130 C was identified through DMA. At room temperature, results indicate a hyperfoam behavior where in compression cross-linked aerogels are linearly elastic under small strains (less than 4%) and then exhibit yield behavior (until 40% strain), followed by densification and inelastic hardening. At room temperature the compressive Young's modulus and the Poisson's ratio were determined to be 129 plus or minus 8 MPa and 0.18, respectively, while the strain at ultimate failure is 77% and the average specific compressive stress at ultimate failure is 3.89 x 10(exp 5) N m kg(sup -1). The specific flexural strength is 2.16 x 10(exp 4) N m kg(sup -1). Effects on the compressive behavior of strain rate and low temperature were also evaluated.

Katti, Atul↗

NASA NTRS2006

Mechanically Strong, Polymer Cross-linked Aerogels (X-Aerogels)

Aerogels comprise a class of low-density, high porous solid objects consisting of dimensionally quasi-stable self-supported three-dimensional assemblies of nanoparticles. Aerogels are pursued because of properties above and beyond those of the individual nanoparticles, including low thermal conductivity, low dielectric constant and high acoustic impedance. Possible applications include thermal and vibration insulation, dielectrics for fast electronics, and hosting of functional guests for a wide variety of optical, chemical and electronic applications. Aerogels, however, are extremely fragile materials, hence they have found only limited application in some very specialized environments, for example as Cerenkov radiation detectors in certain types of nuclear reactors, aboard spacecraft as collectors of hypervelocity particles (refer to NASA's Stardust program) and as thermal insulators on planetary vehicles on Mars (refer to Sojourner Rover in 1997 and Spirit and Opportunity in 2004). Along these lines, the X-Aerogel is a new NASA-developed strong lightweight material that has resolved the fragility problem of traditional (native) aerogels. X-Aerogels are made by applying a conformal polymer coating on the surfaces of the skeletal nanoparticles of native aerogels (see Scanning Electron Micrographs). Since the relative amounts of the polymeric crosslinker and the backbone are comparable, X-Aerogels can be viewed either as aerogels modified by the templated accumulation of polymer on the skeletal nanoparticles, or as nanoporous polymers made by remplated casting of polymer on a nanostructured framework. The most striking feature of X-Aerogels is that for a nominal 3-fold increase in density (still a ultralighweight material), the mechanical strength can be up to 300 times higher than the strength of the underlying native aerogel. Thus, X-Aerogels combine a multiple of the specific compressive strength of steel, with the the thermal conductivity of styrofoam. X-Aerogels have been demonstrated with several polymers such as polyurethanes/polyureas, epoxies and polyolefins, while crosslinking of approximately 35 different oxide aerogels yields a range of dimensionally stable, porous lightweight materials with unique combinations of structural, magnetic and optical properties. The main theme in materials development for space exploration is multifunction. For example, use of one material for thermal insulation/structural component will free weight for useful payload. In that regard, X-aerogels are evaluated at NASA for cryogenic fuel storage tanks and for spacesuits. Along the same lines, major impact fro X-Aerogels is also expected in commercial applications for thermal/acoustic insulation, in catalytic reformers and converters, in filtration membranes and membranes for fuel cells, as platforms for optical, electrical and magnetic sensors, and as lightweight structural component for aircraft and satellites.

Leventis, Nicholas↗

NASA NTRS2006

The Compressive Behavior of Isocyanate-crosslinked Silica Aerogel at High Strain Rates

Aerogels are low-density, highly nano-porous materials. Their engineering applications are limited due to their brittleness and hydrophilicity. Recently, a strong lightweight crosslinked silica aerogel has been developed by encapsulating the skeletal framework of amine-modified silica aerogels with polyureas derived by isocyanate. The mesoporous structure of the underlying silica framework is preserved through conformal polymer coating, and the thermal conductivity remains low. Characterization has been conducted on the thermal, physical properties and the mechanical properties under quasi-static loading conditions. In this paper, we present results on the dynamic compressive behavior of the crosslinked silica aerogel (CSA) using a split Hopkinson pressure bar (SHPB). A new tubing pulse shaper was employed to help reach the dynamic stress equilibrium and constant strain rate. The stress-strain relationship was determined at high strain rates within 114-4386/s. The effects of strain rate, density, specimen thickness and water absorption on the dynamic behavior of the CSA were investigated through a series of dynamic experiments. The Young's moduli (or 0.2% offset compressive yield strengths) at a strain rate approx.350/s were determined as 10.96/2.08, 159.5/6.75, 192.2/7.68, 304.6/11.46, 407.0/20.91 and 640.5/30.47 MPa for CSA with densities 0.205, 0.454, 0.492, 0.551,0.628 and 0.731 g/cu cm, respectively. The deformation and failure behaviors of a native silica aerogel with density (0.472 g/cu cm ), approximately the same as a typical CSA sample were observed with a high speed digital camera. Digital image correlation technique was used to determine the surface strains through a series of images acquired using high speed photography. The relative uniform axial deformation indicated that localized compaction did not occur at a compressive strain level of approx.17%, suggesting most likely failure mechanism at high strain rate to be different from that under quasi-static loading condition. The Poisson s ratio was determined to be 0.162 in nonlinear regime under high strain rates. CSA samples failed generally by splitting, but were much more ductile than native silica aerogels.

Luo, H.↗

NASA NTRS2006

Thermal Cycle Reliability of PBGA/CCGA 717 I/Os

Status of thermal cycle test results for a nonfunctional daisy-chained peripheral ceramic column grid array (CCGA) and its plastic ball grid array (PBGA) version. both having 560 I/Os. were presented in last year's conference. Test results included environmental data for three different thermal cycle regimes (-55 C/125 C, -55 C/100 C, and -50 C /75 C). Update information on these - especially failure type for assemblies with high and low solder volumes-were presented. The thermal cycle test procedure followed those recommended IPC-9701 for tin-lead solder joint assemblies. Revision A of this specification covers guideline thermal cycle requirements for Pb-free solder joints. Some background information discussed during release of this specification with its current guideline recommendations were also presented. In a recent reliability investigation a fully populated CCGA with 717 I/Os was also considered for assembly reliability. evaluation. The functional package is a field-programmable gate array that has much higher processing power than its previous version. This new package is smaller in dimension, has no interposer, and has a thinner column wrapped with copper for reliability improvement. This paper will also present thermal cycle test results for this package assembly and its plastic version with 728 I/Os. both of which were exposed to three different cycle regimes. Two cycle profiles were those specified by IPC- 9701A for tin-lead, i.e. -55 to 100 C and -55 to 125 C and one was a cycle profile specified by Mil-Std-883, i.e.. -65 C/150 C which is generally used for ceramic hybrid packages. Per IPC-9701 A, test vehicles were built using daisy chain packages and were continuously monitored. The effects of many process and assembly variables-including corner staking commonly used for improving resistance to mechanical loading such as drop and vibration loads--were also considered as part of the test matrix. Optical photomicrographs were taken at various thermal cycle intervals to document damage progress and behavior. Representative samples of these along with cross-sectional photomicrographs at higher magnification taken by scanning electron microscopy (SEM) to determine crack propagation and failure analyses for packages are also presented.

staking↗

NASA NTRS2008

Di-Isocyanate Crosslinked Aerogels with 1, 6-Bis (Trimethoxysilyl) Hexane Incorporated in Silica Backbone

Silica aerogels are desirable materials for many applications that take advantage of their light weight and low thermal conductivity. Addition of a conformal polymer coating which bonds with the amine decorated surface of the silica network improves the strength of the aerogels by as much as 200 times. Even with vast improvement in strength they still tend to undergo brittle failure due to the rigid silica backbone. We hope to increase the flexibility and elastic recovery of the silica based aerogel by altering the silica back-bone by incorporation of more flexible hexane links. To this end, we investigated the use of 1,6-bis(trimethoxysilyl)hexane (BTMSH), a polysilsesquioxane precursor3, as an additional co-reactant to prepare silica gels which were subsequently cross-linked with di-isocyanate. Previously, this approach of adding flexibility by BTMSH incorporation was demonstrated with styrene cross-linked aerogels. In our study, we varied silane concentration, mol % of silicon from BTMSH and di-isocyanate concentration by weight percent to attempt to optimize both the flexibility and the strength of the aerogels.

Vivod, Stephanie L.↗

NASA NTRS2006

Manufacture of Regularly Shaped Sol-Gel Pellets

An extrusion batch process for manufacturing regularly shaped sol-gel pellets has been devised as an improved alternative to a spray process that yields irregularly shaped pellets. The aspect ratio of regularly shaped pellets can be controlled more easily, while regularly shaped pellets pack more efficiently. In the extrusion process, a wet gel is pushed out of a mold and chopped repetitively into short, cylindrical pieces as it emerges from the mold. The pieces are collected and can be either (1) dried at ambient pressure to xerogel, (2) solvent exchanged and dried under ambient pressure to ambigels, or (3) supercritically dried to aerogel. Advantageously, the extruded pellets can be dropped directly in a cross-linking bath, where they develop a conformal polymer coating around the skeletal framework of the wet gel via reaction with the cross linker. These pellets can be dried to mechanically robust X-Aerogel.

Leventis, Nicholas↗

NASA NTRS2009

Gratings Fabricated on Flat Surfaces and Reproduced on Non-Flat Substrates

A method has been developed for fabricating gratings on flat substrates, and then reproducing the groove pattern on a curved (concave or convex) substrate and a corresponding grating device. First, surface relief diffraction grating grooves are formed on flat substrates. For example, they may be fabricated using photolithography and reactive ion etching, maskless lithography, holography, or mechanical ruling. Then, an imprint of the grating is made on a deformable substrate, such as plastic, polymer, or other materials using thermoforming, hot or cold embossing, or other methods. Interim stamps using electroforming, or other methods, may be produced for the imprinting process or if the same polarity of the grating image is required. The imprinted, deformable substrate is then attached to a curved, rigid substrate using epoxy or other suitable adhesives. The imprinted surface is facing away from the curved rigid substrate. As an alternative fabrication method, after grating is imprinted on the deformable substrate as described above, the grating may be coated with thin conformal conductive layer (for example, using vacuum deposition of gold). Then the membrane may be mounted over an opening in a pressured vessel in a manner of a membrane on a drum, grating side out. The pressure inside of the vessel may be changed with respect to the ambient pressure to produce concave or convex membrane surface. The shape of the opening may control the type of the surface curvature (for example, a circular opening would create spherical surface, oval opening would create toroidal surface, etc.). After that, well-known electroforming methods may be used to create a replica of the grating on the concave or convex membrane. For example, the pressure vessel assembly may be submerged into an electro-forming solution and negative electric potential applied to the metal coated membrane using an insulated wire. Positive electric potential may be then applied to a nickel or other metal plate submerged into the same solution. Metal ions would transfer from the plate through the solution into the membrane, producing high fidelity metal replica of the grating on the membrane. In one variation, an adhesive may be deposited on the deformable substrate, and then cured without touching the rigid, curved substrate. Edges of the deformable substrate may be attached to the rigid substrate to ensure uniform deformation of the deformable substrate. The assembly may be performed in vacuum, and then taken out to atmospheric pressure conditions to ensure that no air is trapped between the deformable and rigid substrates. Alternatively, a rigid surface with complementary curvature to the rigid substrate may be used to ensure uniform adhesion of the deformable substrate to the rigid substrate. Liquid may be applied to the surface of the deformable substrate to uniformly distribute pressure across its surface during the curing or hardening of the adhesive, or the film may be pressed into the surface using a deformable object or surface. After the attachment is complete, the grooves may be coated with reflective or dielectric layers to improve diffraction efficiency.

Content, David↗