NASA NTRS1981

Effects of erodant particle shape and various heat treatments on erosion resistance of plain carbon steel

Erosion tests were conducted on 1045 steel samples which had been subjected to different heat treatments. The weight of material removed upon erosion with glass beads and crushed glass was measured. The data show that there is no correlation between hardness and erosion resistance. The erosion rate was strongly dependent on the shape of erodant particles, being an order of magnitude higher for erosion with crushed glass than with glass beads. Heat treatment had a profound effect on the erosion resistance when the erodant particles were glass beads but little or no effect when the particles were crushed glass. It is thus concluded that different mechanisms of material removal are involved with these two erodants. This conclusion is supported by the surface morphology of annealed 1045 steel samples which had been eroded by these two types of erodant particles. SEM micrographs of the eroded surfaces show that for erosion with glass beads it is deformation induced fracture of surface layers.

Salik, J.↗

NASA NTRS1981

The structures of the sintered plaque in the nickel hydroxide electrode

The various failure mechanisms were identified for the nickel electrode. The nickel sinter is involved in all these failure modes. The first one, chemical attack by carbonate, nitrate or other electrolyte components, involves corrosion of the nickel sinters. The second is the physical mode, which involves swelling of the electrode and physical shifting of the sinter in the electrodes. The third is the mechanical failure mode, and is due to fatigue or to the oxygen pressure that causes deformation or fracture of the sinter.

Vyas, B.↗

NASA NTRS1980

Tribological properties of silicon carbide in metal removal process

This paper reviews material properties of adhesion, friction and wear of single-crystal silicon carbide in contact with metals and alloys involved in a metal removal process such as grinding. The tribological properties in the metal removal processes are divided into properties which remove metal by adhesion between sliding surfaces, and metal removal by silicon carbide sliding against a metal, indenting it, and plowing a series of grooves or furrows. The paper also deals with fracture and deformation characteristics of the silicon carbide surface; the adhesion, friction and metal transfer to silicon carbide is related to the relative chemical activity of the metals. Atomic size and content of alloying elements play a dominant role in controlling adhesion and friction properties of alloys. The friction and abrasive wear decrease as the shear strength of the bulk metal increases.

Miyoshi, K.↗

NASA NTRS1981

Microscopy and microstructure of Shuttle thermal protection system materials

Examples of the contribution of microstructural analysis to the development of the Space Shuttle tile insulation system are presented, with photographic examples of the scanning electron microscope (SEM) investigations. After the basic thermal protection system materials had been selected, it was neccessary to analyze the mechanical responses of the combined materials; which included: (1) the polymer strain isolation pad (SIP), (2) the room temperature-vulcanizing silicone rubber bond, (RTV), and (3) rigid ceramic fiber reusable surface insulation (RSI). Microstructural analysis was used to provide information on deformation and fracture mechanisms, load transfer mechanisms, and structural alterations occurring before final failure. Both quantitative and qualitative information was obtained in the open, three-dimensional fibrous structures of the ceramic tiles by means of novel techniques of encapsulation and dissolution.

Newquist, C. W.↗

NASA NTRS1984

Considerations in Friction and Wear

The abrasion of ceramic materials is discussed. The friction and wear properties of ceramics which arise primarily from adhesion between sliding surfaces in contact was examined. The role of chemical bonding in adhesion and friction and the influence of surface films, temperature, and crystallographic orientation effects on tribological response with respect to adhesion, friction, and wear are discussed. The complex interaction of various deformation and fracture mechanisms in ceramics, the effect of crystallographic orientation on abrasion, friction, and fracture behavior is addressed.

Miyoshi, K.↗

NASA NTRS1985

Fundamental Studies of Low Velocity Impact Resistance of Graphite Fiber Reinforced Polymer Matrix Composites

A study was conducted to relate the impact resistance of graphite fiber reinforced composites with matrix properties through gaining an understanding of the basic mechanics involved in the deformation and fracture process, and the effect of the polymer matrix structure on these mechanisms. It was found that the resin matrix structure influences the composite impact resistance in at least two ways. The integration of flexibilizers into the polymer chain structure tends to reduce the T sub g and the mechanical properties of the polymer. The reduction in the mechanical properties of the matrix does not enhance the composite impact resistance because it allows matrix controlled failure to initiate impact damage. It was found that when the instrumented dropweight impact tester is used as a means for assessing resin toughness, the resin toughness is enhanced by the ability of the clamped specimen to deflect enough to produce sufficient membrane action to support a significant amount of the load. The results of this study indicate that crossplied composite impact resistance is very much dependent on the matrix mechanical properties.

Bowles, K. J.↗

NASA NTRS1986

Re-examination of cumulative fatigue damage analysis: An engineering perspective

A method which has evolved in our laboratories for the past 20 yr is re-examined with the intent of improving its accuracy and simplicity of application to engineering problems. Several modifications are introduced both to the analytical formulation of the Damage Curve Approach, and to the procedure for modifying this approach to achieve a Double Linear Damage Rule formulation which immensely simplifies the calculation. Improvements are also introduced in the treatment of mean stress for determining fatigue life of the individual events that enter into a complex loading history. While the procedure is completely consistent with the results of numerous two level tests that have been conducted on many materials, it is still necessary to verify applicability to complex loading histories. Caution is expressed that certain phenomena can also influence the applicability - for example, unusual deformation and fracture modes inherent in complex loading - especially if stresses are multiaxial. Residual stresses at crack tips, and metallurgical factors are also important in creating departures from the cumulative damage theories; examples of departures are provided.

Manson, S. S.↗

NASA NTRS1985

Delamination and debonding of materials

The general topics consist of stress analysis, mechanical behavior, and fractography/NDI of composite laminates. Papers are presented on a dynamic hybrid finite-element analysis for interfacial cracks in composites, energy release rate during delamination crack growth in composite laminates, matrix deformation and fracture in graphite-reinforced epoxies, and the role of delamination and damage development on the strength of thick notched laminates. In addition, consideration is given to a new ply model for interlaminar stress analysis, a fracture mechanics approach for designing adhesively bonded joints, the analysis of local delaminations and their influence on composite laminate behavior, and moisture and temperature effects on the mixed-mode delamination fracture of unidirectional graphite/epoxy.

Johnson, W. S.↗

NASA NTRS1986

Re-examination of cumulative fatigue damage analysis - An engineering perspective

A method which has evolved in the laboratories for the past 20 yr is re-examined with the intent of improving its accuracy and simplicity of application to engineering problems. Several modifications are introduced both to the analytical formulation of the Damage Curve Approach, and to the procedure for modifying this approach to achieve a Double Linear Damage Rule formulation which immensely simplifies the calculation. Improvements are also introduced in the treatment of mean stress for determining fatigue life of the individual events that enter into a complex loading history. While the procedure is completely consistent with the results of numerous two level tests that have been conducted on many materials, it is still necessary to verify applicability to complex loading histories. Caution is expressed that certain phenomenon can also influence the applicability - for example, unusual deformation and fracture modes inherent in complex loading especially if stresses are multiaxial. Residual stresses at crack tips, and metallurgical factors are also important in creating departures from the cumulative damage theories; examples of departures are provided.

Manson, S. S.↗

NASA NTRS1989

Oxide scale stresses in polycrystalline Ni200

An X-ray diffraction method has been successfully used to measure the oxidation stresses at room temperature in annealed and electropolished samples of polycrystalline Ni200 coupons oxidized in the temperature range 760 to 982 C for 4 h. The stresses on the free surface of the oxide were compressive and the average stress through the thickness normal to the oxide layer was found to be tensile. Surface stresses on the oxides formed at temperatures up to 927 C were found to be isotropic and both surface stresses and the average normal stress increased with increasing temperature of oxidation. At 982 C, the surface stresses were lower and this was attributed to the deformation and fracture of oxide layer resulting in stress relation.

Jayaraman, N.↗

NASA NTRS1989

Oxidation effects on the mechanical properties of SiC fiber-reinforced reaction-bonded silicon nitride matrix composites

The room temperature mechanical properties of SiC fiber reinforced reaction bonded silicon nitride composites were measured after 100 hrs exposure at temperatures to 1400 C in nitrogen and oxygen environments. The composites consisted of approx. 30 vol percent uniaxially aligned 142 micron diameter SiC fibers in a reaction bonded Si3N4 matrix. The results indicate that composites heat treated in a nitrogen environment at temperatures to 1400 C showed deformation and fracture behavior equivalent to that of the as-fabricated composites. Also, the composites heat treated in an oxidizing environment beyond 400 C yielded significantly lower tensile strength values. Specifically in the temperature range from 600 to 1000 C, composites retained approx. 40 percent of their as-fabricated strength, and those heat treated in the temperatures from 1200 to 1400 C retained 70 percent. Nonetheless, for all oxygen heat treatment conditions, composite specimens displayed strain capability beyond the matrix fracture stress; a typical behavior of a tough composite.

Bhatt, Ramakrishna T.↗

NASA NTRS1992

Oxidation effects on the mechanical properties of a SiC-fiber-reinforced reaction-bonded Si3N4 matrix composite

The room-temperature mechanical properties of SiC fiber reinforced reaction bonded silicon nitride composites were measured after 100 hrs exposure at temperatures to 1400 C in nitrogen and oxygen environments. The composites consisted of approx. 30 vol percent uniaxially aligned 142 micron diameter SiC fibers in a reaction bonded Si3N4 matrix. The results indicate that composites heat treated in a nitrogen environment at temperatures to 1400 C showed deformation and fracture behavior equivalent to that of the as-fabricated composites. Also, the composites heat treated in an oxidizing environment beyond 400 C yielded significantly lower tensile strength values. Specifically in the temperature range from 600 to 1000 C, composites retained approx. 40 percent of their as-fabricated strength, and those heat treated in the temperatures from 1200 to 1400 C retained 70 percent. Nonetheless, for all oxygen heat treatment conditions, composite specimens displayed strain capability beyond the matrix fracture stress; a typical behavior of a tough composite.

Bhatt, Ramakrishna T.↗

NASA NTRS1992

Review of the physical and mechanical properties and potential applications of the B2 compound NiAl: Unabridged version of a paper published in International materials review

Considerable work has been performed on NiAl over the last three decades, with an extremely rapid growth in research on this intermetallic occurring in the last few years due to recent interest in this material for electronic and high temperature structural applications. However, many physical properties and the controlling fracture and deformation mechanisms over certain temperature regimes are still in question. Part of this problem lies in the incomplete characterization of many of the alloys previously investigated. Fragmentary data on processing conditions, chemistry, microstructure and the apparent difficulty in accurately measuring composition has made direct comparison between individual studies sometimes tenuous. Therefore, the purpose of this review is to summarize all available mechanical and pertinent physical properties on NiAl, stressing the most recent investigations, in an attempt to understand the behavior of NiAl and its alloys over a broad temperature range.

Noebe, Ronald D.↗

NASA NTRS1993

Energy loss partitioning during ballistic impact of polymer composites

The objective of this study is to determine the energy dissipation processes in polymer-matrix composites during impact of ballistic projectiles. These processes include heat, fiber deformation and breakage, matrix deformation and fracture, and interfacial delamination. In this study, experimental measurements were made, using specialized specimen designs and test methods, to isolate the energy consumed by each of these processes during impact in the ballistic range. Using these experiments, relationships between material parameters and energy dissipation were examined. Composites with the same matrix but reinforced with Kevlar, PE, and graphite fabric were included in this study. These fibers were selected based on the differences in their intrinsic properties. Matrix cracking was found to be one of the most important energy absorption mechanisms during impact, especially in ductile samples such as Spectra-900 PE and Kevlar-49 reinforced polymer. On the contrary, delamination dominated the energy dissipation in brittle composites such as graphite reinforced materials. The contribution from frictional forces was also investigated and the energy partitioning among the different processes evaluated.

Zee, Ralph H.↗

NASA NTRS1994

Physical and mechanical metallurgy of NiAl

Considerable research has been performed on NiAl over the last decade, with an exponential increase in effort occurring over the last few years. This is due to interest in this material for electronic, catalytic, coating and especially high-temperature structural applications. This report uses this wealth of new information to develop a complete description of the properties and processing of NiAl and NiAl-based materials. Emphasis is placed on the controlling fracture and deformation mechanisms of single and polycrystalline NiAl and its alloys over the entire range of temperatures for which data are available. Creep, fatigue, and environmental resistance of this material are discussed. In addition, issues surrounding alloy design, development of NiAl-based composites, and materials processing are addressed.

Noebe, Ronald D.↗

NASA NTRS1993

Physical and mechanical properties of the B2 compound NiAl

Noebe, R. D.↗

NASA NTRS1995

High temperature composites

The purpose of this paper is to review the current state of the development of new composite materials for advanced aircraft engines. The advantages and disadvantages of Ti-base, NiAl-base, and MoSi2-base composites as replacements for today's Ni-base superalloys are discussed from the standpoint of key technical issues, current status, and future directions. Results describing progress in both improved understanding of the mechanisms of deformation and fracture, and improved material performance will be covered.

Nathal, M. V.↗

NASA NTRS1994

Scanning and Transmission Electron Microscopy of High Temperature Materials

Software and hardware updates to further extend the capability of the electron microscope were carried out. A range of materials such as intermetallics, metal-matrix composites, ceramic-matrix composites, ceramics and intermetallic compounds, based on refractory elements were examined under this research. Crystal structure, size, shape and volume fraction distribution of various phases which constitute the microstructures were examined. Deformed materials were studied to understand the effect of interfacial microstructure on the deformation and fracture behavior of these materials. Specimens tested for a range of mechanical property requirements, such as stress rupture, creep, low cycle fatigue, high cycle fatigue, thermomechanical fatigue, etc. were examined. Microstructural and microchemical stability of these materials exposed to simulated operating environments were investigated. The EOIM Shuttle post-flight samples were also examined to understand the influence of low gravity processing on microstructure. In addition, fractographic analyses of Nb-Zr-W, titanium aluminide, molybdenum silicide and silicon carbide samples were carried out. Extensive characterization of sapphire fibers in the fiber-reinforced composites made by powder cloth processing was made. Finally, pressure infiltration casting of metal-matrix composites was carried out.

Source record↗