Contents include the following: 1. GSFC performance specifications requirements. 2. AEA philosophy: battery configuration. 3. AEA battery design: SONY cell, cell screening, 20Ah and 60Ah. 4. Testing: 20Ah battery qualification (environmental); 60Ah battery LEO life cycle. 5. Conclusion.: summary and lessons learned.
Long-term space operations that require exposure of material to the low earth orbit (LEO) environment must take into account the effects of this highly oxidative atmosphere on material properties and the possible contamination of the spacecraft surroundings. Ground-based laboratory experiments at Los Alamos using a newly developed hyperthermal atomic oxygen (AO) source have shown that not only are hydrocarbon based materials effected but that inorganic materials such as MoS2 are also oxidized and that thin protective coatings such as Al2O3 can be breached, producing oxidation of the underlying substrate material. Gas-phase reaction products, such as SO2 from oxidation of MoS2 and CO and CO2 from hydrocarbon materials, have been detected and have consequences in terms of spacecraft contamination. Energy loss through gas-surface collisions causing spacecraft drag has been measured for a few select surfaces and has been found to be highly dependent on the surface reactivity.
A detailed description of the space shuttle vehicle and associated subsystems is given. Space transportation system propulsion, power generation, environmental control and life support system and avionics are among the topics. Also, orbiter crew accommodations and equipment, mission operations and support, and flight crew complement and crew training are addressed.
Power availability remains one of the primary constraints for lunar surface science. This talk reviews power requirements from previously flown instruments to help prepare future payloads for upcoming CLPS opportunities and highlights the testing and environmental simulation capabilities at NASA JSC that enable reliable lunar payload development. It also outlines the power needs, environmental challenges, and emerging technologies required to support sustained human and robotic operations on the lunar surface as part of NASA’s Moon to Mars strategy. Key challenges include variable solar illumination at polar and equatorial regions, extreme thermal environments, and dust driven degradation that limit current surface power systems. The science data needed for resource identification and landing site planning will allow for the successful preparation of crewed Artemis activities and long-term presence. Building on recent missions, current test infrastructure, and emerging power technology pathways, this presentation equips industry, academia, and government teams with the information needed to design robust lunar payloads, reduce development risk, and fully leverage the increasing cadence of CLPS missions. These developments will form a critical technical foundation for long duration lunar presence and future Mars exploration.
Power availability remains one of the primary constraints for lunar surface science. This talk reviews power requirements from previously flown instruments to help prepare future payloads for upcoming CLPS opportunities and highlights the testing and environmental simulation capabilities at NASA JSC that enable reliable lunar payload development. It also outlines the power needs, environmental challenges, and emerging technologies required to support sustained human and robotic operations on the lunar surface as part of NASA’s Moon to Mars strategy. Key challenges include variable solar illumination at polar and equatorial regions, extreme thermal environments, and dust driven degradation that limit current surface power systems. The science data needed for resource identification and landing site planning will allow for the successful preparation of crewed Artemis activities and long-term presence. Building on recent missions, current test infrastructure, and emerging power technology pathways, this presentation equips industry, academia, and government teams with the information needed to design robust lunar payloads, reduce development risk, and fully leverage the increasing cadence of CLPS missions. These developments will form a critical technical foundation for long duration lunar presence and future Mars exploration.
The nickel-cadmium battery design developed for the Synchronous Meteorological Satellite (SMS) and Geostationary Operational Environmental Satellite (GOES) provided background and guidelines for future development, manufacture, and application of spacecraft batteries. SMS/GOES battery design, development, qualification testing, acceptance testing, and life testing/mission performance characteristics were evaluated for correlation with battery cell manufacturing process variables.
The High EneRgy Observatory for Imaging X-rays (HEROIX) is a next-generation broadband X-ray space telescope concept under development as a Medium-Class Explorer mission. Building on more than three decades of replicated NiCo shell technology at NASA’s Marshall Space Flight Center, HEROIX will deliver 5 arcsecond half-power-diameter imaging resolution in the hard X-ray band. The observatory will incorporate four co-aligned telescopes with advanced multilayer coatings, extending the bandpass into the hard X-ray regime and providing an integrated effective area of 380 cm² at 30 keV. A suite of focal plane detectors will enable imaging capability throughout its 1–80 keV bandpass. This combination of angular resolution and high-energy coverage will open new windows into non-thermal processes in extreme astrophysical environments. HEROIXwill deliver transformative science, advancing the astrophysics community’s understanding of supernova physics, the X-ray binary population of the Galactic Center, accretion-driven galaxy evolution, and the origin of the Cosmic X-ray Background.
Polymers and other oxidizable materials on the exterior of spacecraft in the low Earth orbit (LEO) space environment can be eroded from reaction with atomic oxygen (AO). Therefore, in order to design durable spacecraft it is important to know the extent of erosion that will occur during a mission. This can be determined by knowing the LEO AO erosion yield, E y (volume loss per incident oxygen atom), of materials susceptible to AO reaction. In addition, recent flight experiments have shown that the AO E y can vary with the AO fluence and/or solar exposure. Therefore, obtaining AO E y data for materials flown on various spaceflight missions is important. NASA Glenn Research Center has flown numerous experiments as part of the Materials International Space Station Experiment (MISSE) missions on the exterior of the International Space Station (ISS) to characterize the LEO E y of polymers, composites, protective coatings, and other spacecraft materials. Recently, four Glenn experiments with 365 flight (F) samples were flown on ISS’s MISSE-Flight Facility (MISSE-FF). These experiments are the Polymers and Composites Experiment-1 (PCE-1) flown as part of the MISSE-9 mission, the PCE-2 flown as part of the MISSE-10 mission, the PCE-3 flown as part of the MISSE-12 and MISSE-15 missions, and the PCE-4 flown as part of the MISSE-13 mission. Although each experiment had numerous sample objectives, the primary objective was to determine the LEO AO E y of various spacecraft materials as a function of solar irradiation and AO fluence. This paper provides a summary of the erosion data for the PCE 1-4 AO E y samples. The AO E y for 150 samples flown in either the LEO ram, wake, zenith or nadir directions are provided. The AO ram fluence varied from 2.97×10 20 atoms/cm 2 after 0.89 years of direct space exposure (with relatively high levels of Si contamination) on MISSE 12 to 3.93×10 20 atoms/cm 2 after 1.17 years of direct space exposure on MISSE-10. The ram AO E y values for uncoated polymers range from 3.81×10 –25 cm 3 /atom for polytetrafluoroethylene (M9R-C20 F) exposed to an AO fluence of 3.44×10 20 atoms/cm 2 on MISSE-9 to 4.43×10 –23 cm 3 /atom for AO etched low density polyimide aerogel (M12R-C21 F) exposed to an AO fluence of 2.97×10 21 atoms/cm 2 on MISSE-12. Because of the low AO fluence and relatively high Si contamination, a number of PCE-3 wake samples experienced mass gain. Thus, AO E y values are not provided for these samples. Although there are calculated AO E y values for the zenith, wake and nadir samples, the ram AO E y for a particular material is a more reliable value in terms of AO exposure because the zenith, wake and nadir directions were exposed to either no or very little AO fluence and thus other space environmental factors (i.e. vacuum, thermal extremes and thermal cycling, and/or various types of radiation) are responsible for the mass loss.
There is a growing body of theoretical and experimental evidence suggesting that the uniformity, rate, adhesion, quality, and other key properties of Chemical Vapor Deposition (CVD) diamond coatings are influenced by the gas mixing kinetics in the thermal plasma environment of the reaction chamber. The implementation of, for example, Microwave Plasma Enhanced Chemical Vapor Deposition (MPECVD) process in microgravity has, thus, been suggested. Such a diamond deposition system, which overcomes the limitations of present systems and which is distiguishable from them by the use of high pressure MPECVD and recirculation of the would be effluent hydrogen and carbon, is described. Given the key fact that there is nothing in the effluent of the MPECVD process that is truly a byproduct or 'waste', the system can, at least in principle, lend itself to being closed loop yet dynamic. The exhaust contains hydrogen and carbon species which can be recirculated to the plasma reactor, that is, since there are no unusable reaction byproducts, the effluent can be fed back to the reaction chamber with no detriment, thus allowing deployment in a microgravity environment.
A novel, in-situ, scanning electron microscope (SEM) mechanical testing capability for materials at the microscale which provides experimental validation to a machine learning (ML) toolset for full-field validation of physics-based micromechanics models is being developed by researchers at NASA Glenn Research Center. These are enabling technologies for the integration of multiscale digital twins for materials into system level models which will result in the improved performance, material discovery, reduced production cost and time, rapid characterization, and prognostic structural health monitoring (SHM) for materials and structures for extreme environments in support of NASA space exploration missions. In order to bridge the material structure-to-system gap for digital twins, physics-based models must be experimentally validated at multiple length scales. Seminal microscale experiments, conducted at the Air Force Research Laboratory (AFRL), were limited to transverse compression of single-layer, unidirectional thermoset polymer matrix composite (PMC) micropillar specimens [1]. The early phases of the current project followed those initial results and setup to reproduce the compression testing of PMC material on the custom-built piezoelectric actuated micromechanical testing rig built by MicroTesting Solutions LLC. In this work, samples of thermoplastic PMC material were first machined into 3 mm cubes, and then further machining and final milling was done using a Focused Ion Beam (FIB). The initial experiment was done on a pillar roughly 20 µm x 20 µm x 40 µm tall. Additional pillars were milled with final sizes ranging from 20 µm x 20 µm x 40 µm tall to 40 µm x 40 µm x 65 µm tall. A speckle pattern for in-situ full-field measurements using Digital Image Correlation (DIC) was applied with platinum, which was coated on the surface, and then the FIB was used to mill away some of the coating to produce an irregular pattern of Pt on the pillar surface. The samples were loaded into the custom testing rig and placed into the SEM and loaded under compression until failure. Images were collected in the SEM during testing. Post-processing of the images was conducted using DIC to obtain full-field displacement and strain measurements elucidating the role of the matrix as well as fiber-fiber interaction at the microscale within the composite subjected to compression loading well into the non-linear regime of the material. Moreover, the evolution of fiber-matrix debonding and matrix cracking is observed in-situ at the microscale. This data, along with images segmented with a newly developed ML toolset [2], was used to create and validate physics-based micromechanics models. An image of the failed micropillar is shown in Figure 1. The techniques developed in the initial compression experiment was tailored to the validation needs of the models and expanded to include different sized samples as well as possibly tension and fatigue.
Solar cells in space plasma conditions are known to arc into the plasma when the interconnects are at a negative potential of a few hundred volts, relative to plasma potential. For cells with silver-coated interconnects, a threshold voltage for arcing exists at about -230 V, as found in both ground and LEO experiments. The arc rate beyond the threshold voltage depends nearly linearly on plasma density, but has a strong power-law dependence on voltage, such that for small increments in operating voltage there is a large increment in arc rate. The arcs generate broadband radio interference and visible light. In ground tests, interconnects have been damaged by arcs in cells having insufficient isolation from a source of high current. Models for the arcs are highly dependent on the choice of interconnect conductor material exposed to the plasma and possibly on the geometry and choice of adjacent insulator material. Finally, new technology solar cells use copper for the cell interconnects, a material which may have a lower arcing threshold voltage than silver. It is expected, from ground tests of simulated solar cells, that any junction of conductor and insulator exposed to space plasma conditions will arc into the plasma at a few hundred volts negative potential, relative to the local plasma.
The report "High Efficiency Centrifugal Compressor for Rotorcraft Applications" documents the work conducted at UTRC under the NRA Contract NNC08CB03C, with cost share 2/3 NASA, and 1/3 UTRC, that has been extended to 4.5 years. The purpose of this effort was to identify key technical barriers to advancing the state-of-the-art of small centrifugal compressor stages; to delineate the measurements required to provide insight into the flow physics of the technical barriers; to design, fabricate, install, and test a state-of-the-art research compressor that is representative of the rear stage of an axial-centrifugal aero-engine; and to acquire detailed aerodynamic performance and research quality data to clarify flow physics and to establish detailed data sets for future application. The design activity centered on meeting the goal set outlined in the NASA solicitation-the design target was to increase efficiency at higher work factor, while also reducing the maximum diameter of the stage. To fit within the existing Small Engine Components Test Facility at NASA Glenn Research Center (GRC) and to facilitate component re-use, certain key design parameters were fixed by UTRC, including impeller tip diameter, impeller rotational speed, and impeller inlet hub and shroud radii. This report describes the design effort of the High Efficiency Centrifugal Compressor stage (HECC) and delineation of measurements, fabrication of the compressor, and the initial tests that were performed. A new High-Efficiency Centrifugal Compressor stage with a very challenging reduction in radius ratio was successfully designed, fabricated and installed at GRC. The testing was successful, with no mechanical problems and the running clearances were achieved without impeller rubs. Overall, measured pressure ratio of 4.68, work factor of 0.81, and at design exit corrected flow rate of 3 lbm/s met the target requirements. Polytropic efficiency of 85.5 percent and stall margin of 7.5 percent were measured at design flow rate and speed. The measured efficiency and stall margin were lower than pre-test CFD predictions by 2.4 percentage points (pt) and 4.5 pt, respectively. Initial impressions from the experimental data indicated that the loss in the efficiency and stall margin can be attributed to a design shortfall in the impeller. However, detailed investigation of experimental data and post-test CFD simulations of higher fidelity than pre-test CFD, and in particular the unsteady CFD simulations and the assessment with a wider range of turbulence models, have indicated that the loss in efficiency is most likely due to the impact of unfavorable unsteady impeller/diffuser interactions induced by diffuser vanes, an impeller/diffuser corrected flow-rate mismatch (and associated incidence levels), and, potentially, flow separation in the radial-to-axial bend. An experimental program with a vaneless diffuser is recommended to evaluate this observation. A subsequent redesign of the diffuser (and the radial-to-axial bend) is also recommended. The diffuser needs to be redesigned to eliminate the mismatching of the impeller and the diffuser, targeting a slightly higher flow capacity. Furthermore, diffuser vanes need to be adjusted to align the incidence angles, to optimize the splitter vane location (both radially and circumferentially), and to minimize the unsteady interactions with the impeller. The radial-to-axial bend needs to be redesigned to eliminate, or at least minimize, the flow separation at the inner wall, and its impact on the flow in the diffuser upstream. Lessons were also learned in terms of CFD methodology and the importance of unsteady CFD simulations for centrifugal compressors was highlighted. Inconsistencies in the implementation of a widely used two-equation turbulence model were identified and corrections are recommended. It was also observed that unsteady simulations for centrifugal compressors require significantly longer integration times than what is current practice in industry.
While the good oxidation and environmental resistance, high melting points, and comparatively low densities of such ordered intermetallics as Ti 3 Al, NiAl, FeAl, and NbAl 3 render them good candidates for advanced aerospace structures, their poor toughness at low temperatures and low strength at elevated temperatures have prompted the development of fiber-reinforced intermetallic-matrix composites (IMCs) with more balanced characteristics. Fabrication methods for continuous-fiber IMCs under development include the P/M 'powder cloth' method, the foil/fiber method, and thermal spraying. The ultimate success of IMCs depends on fibers truly compatible with the matrix materials.
The four trays of the M0003 materials experiment on LDEF contained 1274 samples from 19 subexperiments. The complete sample complement represented a broad range of materials, including thin film optical coatings, paints, polymer sheets and tapes, adhesives, and composites, for use in various spacecraft applications including thermal control, structures, optics, and solar power. Since some subexperiments included duplicate samples exposed on the leading and trailing edge trays, for 9 week, 19 week, 40 week, and 68 month durations on both the leading and trailing edges, comparisons provided a valuable time history of degradation. During the deintegration of the subexperiments from the M0003 trays, each sample was examined using bright field, dark field, and Normarski light microscopy techniques. Over 3,000 color macrographs and photomicrographs were made of the condition of M0003 trays and the individual samples. Records of the condition of the samples, photographic records, and all available references of publications on postflight analyses on each sample were collected in a database. The photographs provide a visual comparison of the response of materials common to various subexperiments in different LDEF environments. Aerospace Corporation is distributing the database records and photographs and written records on materials of interest from the database is given in this presentation.
The nature and mechanisms producing the chromophore agents that provide color to the upper clouds and hazes of the atmospheres of the giant planets are largely unknown. In recent times, the changes in red coloration that have occurred in large- and medium-scale Jovian anticyclones have been particularly interesting. In late June and early July 2008, a particularly color-intense red tropical oval interacted with the Great Red Spot (GRS) leading to the destruction of the red tropical oval and cloud dispersion. We present a detailed study of the tropical vortices, usually white but sometimes red, and a characterization of their color spectral signatures and dynamics. From the spectral reflectivity in methane bands we study their vertical cloud structure compared to that of the GRS and BA. Using two spectral indices we found a near-correlation between anticyclones cloud top altitudes and red color. We present detailed observations of the interaction of the red oval with the GRS and model simulations of the phenomena that allow us to constrain the relative vertical extent of the vortices. We conclude that the vertical cloud structure, vertical extent and dynamics of Jovian anticyclones are not the causes of their coloration. We propose that the red chromophore forms when background material (a compound or particles) is entrained by the vortex, transforming into red once inside the vortex due to internal conditions, exposure to ultraviolet radiation or to the mixing of two chemical compounds that react inside the vortex, confined by a potential vorticity ring barrier.
The High EneRgy Observatory for Imaging X-rays (HEROIX) Medium-Class Mission concept envisions a next-generation broadband X-ray observatory designed to meet the astrophysics community’s need for high-angular-resolution studies of the Cosmic X-ray Background. Building on the science legacy of NASA’s NuSTAR mission and more than 30 years of advances in replicated NiCo shell technology at NASA Marshall, HEROIX proposes a space observatory comprising four co-aligned telescopes achieving 5 arcsecond half-power diameter (HPD) angular resolution. This capability, approached by the resolution demonstrated in the FOXSI-4 sounding rocket mission and under development through the SuperHERO balloon mission, will be extended to energies up to 80 keV through multilayer coatings. Marshall’s inhouse precision optics manufacturing enables an integrated effective area of 380 cm² at 30 keV, which, combined with high-resolution optics, opens new windows into extreme astrophysical non-thermal processes.
An update of the 12 kW Advanced Electric Propulsion System (AEPS) qualification and flight thruster status is provided. Three flight thrusters completed acceptance testing in 2025 and have been delivered to NASA. Environmental qualification is complete and preparations are under way for long-duration life-demonstration testing. Programmatic lessons learned associated with risk management, contract oversight, and requirement definition during the fabrication and assembly are discussed. In addition, the extensibility of the AEPS thruster to enable a variety of NASA missions is presented.
An update of the 12 kW Advanced Electric Propulsion System (AEPS) qualification and flight thruster status is provided. Three flight thrusters completed acceptance testing in 2025 and have been delivered to NASA. Environmental qualification is complete and preparations are under way for long-duration life-demonstration testing. A brief overview of three of SEP’s programmatic lessons learned are discussed: risk management, contract oversight, and requirement definition. In addition, the extensibility of the AEPS thruster to enable a variety of NASA missions is presented.