DOE OSTI2025
This work investigates the effect of processing and heat treatment on defect evolution and irradiation response of laser powder bed fusion (LPBF) 316H stainless steel, with comparisons to LPBF 316L and wrought 316L/316H. Using in-situ and ex-situ ion irradiations across a wide parameter space—temperature (300–675 °C), dose (0.2–25 dpa), dose rate (10 -3 –10 -5 dpa/s), and helium co-implantation (20–2500 appm)—we correlated void swelling, dislocation loop evolution, and segregation behavior with pre-irradiation microstructures (as-built, stress-relieved, solution-annealed, and cold-worked). Results show that swelling is strongly controlled by dislocation density: intermediate densities maximize swelling, while solution annealing or cold working reduce susceptibility to levels comparable to wrought alloys. Low dose rates and helium both promote cavity nucleation and lower the incubation barrier, with helium suppressing the role of dislocation density and driving swelling behavior toward wrought-like response. Loop evolution in SA LPBF 316H resembles wrought 316L but shows localized denuded zones near low-angle grain boundaries. STEM-EDS mapping further revealed Ni segregation at voids and sparse Al-rich oxides, without evidence of Ni–Si precipitates. Collectively, these findings identify dislocation density, helium content, and dose rate as the factors governing swelling in LPBF 316H and provide mechanistic datasets for model validation, supporting LAIN and the qualification of AM austenitic steels for nuclear service.