Results for “accelerated aging” — Page 6

NASA NTRS2006

Nitrile/Buna N Material Failure Assessment for an O-Ring used on the Gaseous Hydrogen Flow Control Valve (FCV) of the Space Shuttle Main Engine

After the rollout of Space Shuttle Discovery in April 2005 in preparation for return-to-flight, there was a failure of the Orbiter (OV-103) helium signature leak test in the gaseous hydrogen (GH2) system. Leakage was attributed to the Flow Control Valve (FCV) in Main Engine 3. The FCV determined to be the source of the leak for OV-103 is designated as LV-58. The nitrile/Buna N rubber O-ring seal was removed from LV-58, and failure analysis indicated radial cracks providing leak paths in one quadrant. Cracks were eventually found in 6 of 9 FCV O-rings among the three Shuttle Orbiters, though none were as severe as those for LV-58, OV-103. Testing by EM10 at MSFC on all 9 FCV O- rings included: laser dimensional, Shore A hardness and properties from a dynamic mechanical analyzer (DMA) and an Instron tensile machine. The following test data was obtained on the cracked quadrant of the LV-58, OV-103 O-ring: (1) the estimated compression set was only 9.5%, compared to none for the rest of the O-ring; (2) Shore A hardness for the O.D. was higher by almost 4 durometer points than for the rest of the O-ring; and (3) DMA data showed that the storage/elastic modulus E was almost 25% lower than for the rest of the O-ring. Of the 8 FCV O-rings tested on an Instron, 4 yielded tensile strengths that were below the MIL spec requirement of 1350 psi-a likely influence of rubber cracking. Comparisons were made between values of modulus determined by DNA (elastic) and Instron (Young s). Each nitrile/Buna N O-ring used in the FCV conforms to the MIL-P-25732C specification. A number of such O-rings taken from shelf storage at MSFC and Kennedy Space Center (KSC) were used to generate a reference curve of DMA glass transition temperature (Tg) vs. shelf storage time ranging from 8 to 26 years. A similar reference curve of TGA onset temperature (of rubber weight loss) vs. shelf storage time was also generated. The DMA and TGA data for the used FCV O-rings were compared to the reference curves. Correlations were also made between the DMA modulus (at 22 C) and Shore A hardness for all 9 of the FCV O-rings used among the three Shuttle Orbiters. The radial cracking in the FCV O-rings was determined to be due to ozone attack, as nitrile/Buna N rubber is susceptible to such attack. Nitrile/Buna N material under MIL-P25732C should be used in a hydraulic fluid environment to help protect it from cracking. However, the FCV O-rings were used in an air only environment. The FCV design has as much as a 9-mil gap that allows the O.D. of the O-ring to be directly exposed to ozone, pressurized air and some elevated temperatures, accelerating the weathering process that leads to O-ring cracking. Space Shuttle flights will likely not continue past 2010. Therefore, Shuttle management decided to continue using the nitrile/Buna N material for the FCVs, but have each O-ring replaced after 3 years to minimize any chances for crack initiation.

Doug Wingard↗

NASA NTRSDate not supplied

An Overview of Experiments and Modeling of Polysiloxane-Coated Thermal Protection Systems for Missions to Mars, Titan, and Beyond.

Phenolic Impregnated Carbon Ablator (PICA) gained heritage during the historic Stardust mission, where it successfully returned samples from a comet’s tail and has since been instrumental in delivering payloads to the surface of Mars [1-3]. Most recently, PICA enabled the safe return of samples collected from asteroid Bennu as part of the OSIRIS-REx mission. This rich legacy underscores PICA’s critical role in allowing NASA’s most ambitious exploration missions. However, the friable nature of its phenolic phase presents challenges during handling and pre-launch activities. To mitigate this issue, PICA is coated with a polysiloxane resin system, which serves to suppress particulate dispersion and thereby safeguard spacecraft components. A comprehensive understanding of the polysiloxane resin’s behavior is imperative, as it profoundly shapes the material response of PICA during atmospheric entry by influencing its thermal and oxidative stability. This influence extends to thermocouple plugs embedded within thermal protection systems. These plugs have demonstrated their significance in missions such as Mars Science Laboratory (MSL) and Mars 2020, where the MEDLI and MEDLI2 instrumentation suites delivered in-valuable insights into the performance of thermal protection systems during entry into the Martian atmosphere [4]. Looking ahead, missions such as Dragonfly, set to descend into Titan’s dense atmosphere, aim to leverage advanced sensor technologies to further refine our understanding of thermal protection response [5]. Moreover, thermocouple plugs play an essential role in validating cutting-edge material response models, such as those pioneered under NASA’s Entry Systems Modeling Project (ESM), designed, in-part, to predict the operational integrity of thermal protection systems under the extreme stresses of atmospheric entry. To achieve these modeling goals, ground-based experiments are crucial to provide the foundational data necessary for developing and refining these predictive tools. To this end, an extensive test campaign was conducted at the Hypersonic Materials Environmental Test System (HyMETS) to investigate the high-temperature behavior of the polysiloxane resin in an air environment [6]. These experiments revealed critical phenomena, including the formation of a silicon oxycarbide layer that enhances oxidation resistance, moderates surface temperatures, and alters in-depth thermal response. Building on these findings, subsequent tests were designed to simulate atmospheric entry conditions in reactive gases, such as CO2 and N2, to mimic the environments of Mars and Titan, respectively, as well as non-reactive gases representing the atmospheres of the Ice Giants (Neptune and Uranus). A heating rate dependent decomposition mechanism has been identified for the polysiloxane resin under oxidizing conditions (Fig. 1). In the initial stage, the resin and the underlying thermal protection system undergo pyrolysis, rapidly generating a thin amorphous silicon oxycarbide interwoven with carbonaceous char and residual fibers from PICA. During the second stage, the nascent oxide layer establishes a robust, oxidation-resistant thermal barrier coating, which significantly impedes heat transfer to the underlying carbonaceous char, resulting in a stagnation of the surface temperature. A key factor contributing to this thermal resistance is the low recombination efficiency of atomic oxygen (γ), which further diminishes the heat load on the material’s interior layers [7]. Moreover, as the surface temperature stagnates, the silicon oxycarbide phase separates into distinct regions of silica and free graphite. Ultimately, when the heat flux reaches a critical threshold, a third stage is triggered, leading to the breakdown of the coating through carbothermal reduction, exposing the underlying char layer. This exposure leads to a dramatic surface temperature spike, driven by highly exothermic reactions between atomic oxygen and the char layer, further accelerating material degradation. A detailed mass and heat transfer model of PICA coated with polysiloxane resin was implemented in the Porous material Analysis Toolbox based on OpenFOAM, PATO [8]. The initial stage was considered negligible in this model because the resin decomposition occurs rapidly within a thin surface layer. Instead, the coating was directly considered as an oxygen-resistant thermal barrier coating. For the second stage, the thin amorphous silicon oxycarbide was treated as a pure silica surface to simplify the thermochemical behavior. The model ac-counts for surface equilibrium processes using representative elements of the coating-environment system. For the third stage, specific boundary conditions were developed to estimate the onset and progression of the coating removal. Two-dimensional material response simulations were conducted to compare uncoated and coated PICA using boundary conditions calibrated with HyMETS data. Fig. 2 illustrates that the simulations closely align with experimental data, successfully reproducing measured temperature profiles. This work will include the latest advancements in the coating model, including the calibration of recombination of atomic oxygen at the surface during the second phase. These simulated results will be further validated against additional CO2 data points from HyMETS, reinforcing the models’ predictive capabilities. These mechanisms and their effects on thermal protection systems, including thermochemical behavior and thermocouple probe performance in extreme environments, provide crucial insights for optimizing spacecraft designs that safeguard scientific payload and ensure mission success in future planetary exploration endeavors.

Active Oxidation↗