Statistical fracture behavior of doped UO 2 using a ball-on-ring equibiaxial flexure test method

Metal oxide dopants, such as titanium and chromium oxides, have garnered considerable attention for their potential to increase grain size (≥ 30 µm) in UO 2 fuel, purportedly enhancing fission gas retention during reactor operation. Fuel performance is significantly impacted by fuel fracture behavior, so it is important to understand the effects of enhanced grain size and dopant content on UO 2 fuel fracture. UO 2 pellets were doped with 0.1 wt% TiO 2 and 0.3 wt% Cr 2 O 3 to alter density and grain size. Inductively coupled plasma mass spectroscopy measured dopant levels pre- and post-sintering. X-ray diffraction revealed lattice changes and microstrain via Rietveld refinement. Field emission scanning electron microscopy determined grain sizes of approximately 30 µm for TiO 2 doping and 7 µm for Cr 2 O 3 doping. Transverse rupture strength tests were performed on over 30 samples per dataset to obtain characteristic strength and Weibull modulus. Results indicate no statistical difference in fracture strength between 0.1 wt% TiO 2 doped UO 2 and undoped UO 2 , while 0.3 wt% Cr 2 O 3 doped UO 2 exhibited a 20% decrease in fracture strength. Doped UO 2 samples also showed reduced Weibull modulus compared to undoped UO 2 , suggesting increased scatter in fracture strength. This study's findings suggest that titanium and chromium oxide doping in UO 2 , regardless of grain size, induce residual stresses, decreasing fracture strength and increasing variability in fracture behavior.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Equibiaxial flexural strength determination of UO 2 using a ball-on-ring test

To increase nuclear fuel performance and reliability, their mechanical properties require an accurate and statistically relevant assessment. Biaxial flexural strength tests provide an alternative to bend bar techniques for assessing mechanical behavior; namely, the transverse rupture strength (TRS) of ceramic samples. Biaxial test samples require simple geometries and minimal surface preparation, reducing fabrication costs and handling hazards. This study investigated the TRS of polycrystalline UO 2 fuel forms at room temperature using a ball-on-ring test fixture. Here, pellets were fabricated from UO 2 powder using conventional powder processing and sintering techniques. The TRS and Weibull parameters were obtained through Weibull statistics on over 60 UO 2 samples tested under equibiaxial flexure. The larger sample size in this study enabled a more robust Weibull statistical analysis than alternative test methods, which may not capture the stochastic failure of typical ceramics. Furthermore, two different loading ball diameters were employed to assess the impact of contact damage on fracture strength. While Hertzian contact damage was observed with the smaller loading ball, the fracture strength remained unaffected. A fracture analysis of the tested UO 2 samples indicated a mixture of intergranular and transgranular fracture that transitions to transgranular fracture with increasing distance from the fracture origin. The characteristic strength of the combined data sets was determined to be 148 MPa, and the Weibull modulus was determined to be 9.1. The TRS values and Weibull parameters were close to values found in the literature for alternative testing techniques using samples with similar microstructure and density. The findings in this study validate the ball-on-ring method used to obtain the TRS of UO 2 with a sample geometry more representative of nuclear fuels. Additionally, experimental TRS results from this study can be implemented in modeling codes to predict fuel performance, which is critical to fuel burnup extension and advanced nuclear fuel technologies.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Microstructural characterization and equibiaxial flexural strength of CeO 2 and Ti-doped CeO 2

In this study, the synthesis of CeO 2 and titanium dioxide (TiO 2 ) doped CeO 2 (TDC) monoliths are investigated, and their fracture strength is assessed using an equibiaxial flexure testing technique at room temperature. Pellets were synthesized using conventional powder processing and sintering methods to produce the desired characteristics. The TiO 2 dopant concentration was optimized at 0.1 wt % TiO 2 to obtain dense, solid-solution pellets with an enhanced grain microstructure. A ball-on-ring fixture was used to obtain the TRS and Weibull parameters of over 30 pellets for CeO 2 and 0.1 wt % TDC to compare fracture behavior. The TRS of CeO 2 pellets ranged from 88 to 160 MPa and the TRS of 0.1 wt % TDC pellets ranged from 102 to 171 MPa, both being consistent with published values. Weibull parameters, such as characteristic strength and Weibull modulus, were extracted as 129 MPa and 8.5 for CeO 2 and 150 MPa and 9.3 for 0.1 wt % TDC, respectively. Although Hertzian contact damage was observed on compressive surfaces, failure initiation occurred on the tensile surfaces of both types of samples. Fracture surface analysis for CeO 2 indicated a predominantly intergranular fracture while 0.1 wt % TDC had a predominantly transgranular fracture mode. Finally, the TRS of 0.1 wt % TDC resulted in increased Weibull parameters when compared to CeO 2 , indicating sample chemistry and microstructure impact mechanical behavior for these samples.

36 MATERIALS SCIENCE↗