NASA NTRS2017

Current EBC Development and Testing at NASA

SiC SiC Ceramic Matrix Composites (CMCs) are a game changer for advanced power generation equipment because of their high temperature capability, oxidation resistance, and light weight that translate to significant reduction in fuel consumption and emission. Limitations of SiC SiC CMCs include surface recession and component cracking and associated chemical and physical degradation in the CMC. The solution pursued to mitigate surface recession of SiC SiC CMCs is the incorporation of coating systems that provide surface protection, which has become known as an Environmental Barrier Coating (EBC). The development of EBCs for the protection of SiC SiC CMCs was a continuation of coating development work for corrosion protection of silicon-based monolithics. The first and second generation EBCs developed in mid 1990s-early 2000s laid the foundation for current EBCs. Environmental degradation that limits EBC life includes surface recession by steam, oxidation in steam environments, and CMAS-EBC reactions. Many engine tests have been conducted since late 1990s and a first CMC component entered into service in 2016 in a commercial engine. The introduction of CMCs represents significant challenges as failure of the EBC means rapid reduction in component life. A reliable lifing method and engine-relevant testing methods to validate life need to be developed. This paper will current activities on EBC development and testing at NASA.

CMC↗
NASA NTRS2024

Effects of CMAS Application on the Isothermal and Gradient Thermal Cycling Behavior of a Yb 2 Si 2 O 7 EBC

Environmental barrier coatings (EBCs) are critical to the continued advancement of gas turbine hot section materials technology. EBCs are required to protect Si-based ceramics such as silicon carbide fiber-reinforced silicon carbide (SiC/SiC) ceramic matrix composites (CMCs) from oxidation and corrosion in the combustion environment. One of the current challenges concerning EBC lifetime is the thermochemical reactions between calcium-magnesium-aluminosilicate (CMAS) deposits and the EBC that leads to changes in both composition and stress state. These changes can severely reduce the integrity of the EBC leading to crack formation, delamination, and spallation. Current techniques for evaluating CMAS in the laboratory rely on the pre-application of CMAS. Two commonly used application methods to deposit CMAS on EBC materials are tape-casting and air spray. In both methods, the CMAS is applied to the EBC surface at ambient temperature, and then subject to a heat treatment process for binder burnout. The purpose of this study is to compare the tape-cast and air spray methods on the CMAS corrosion of an ytterbium disilicate (Yb 2 Si 2 O 7 ) EBC subject to isothermal, and gradient thermal cycling. The results highlight if any differences exist in the CMAS infiltration kinetics between the two application methods.

Environmental barrier coatings (EBCs)↗
NASA NTRS2001

Environmental Barrier Coatings (EBC) for Ceramic Matrix Composite (CMC) Materials

The upper use temperature of current Environmental Barrier Coatings (EBC's) based on mullite and BSAS (EPM EBC's) is limited to -255 F due to silica volatility, chemical reactions, and high thermal conductivity. Therefore, new EBC s having low CTE, good chemical compatibility, and high melting point (greater than 2700 F ) are being investigated. Sinter-resistant, low thermal conductivity EBC s are strongly desired to achieve the UEET EBC goal of 270 F EBC surface temperature and 30 F AT over long exposures (greater than 1000 hr). Key areas affecting the upper temperature limit of current EBC s as well as the ongoing efforts to develop next generation EBC s in the UEET Program will be discussed.

Lee,Kang↗
NASA NTRS2008

Impact Resistance of EBC Coated SiC/SiC Composites

Impact performance of 2-D woven SiC/SiC composites coated with 225 and 525 m thick environmental barrier coating (EBC) was investigated. The composites were fabricated by melt infiltration and the EBC was deposited by plasma spray. Impact tests were conducted at room temperature and at 1316 C in air using 1.59-mm diameter steel-balls at projectile velocities ranging from 110 to 375 m/s. Both microscopy and nondestructive evaluation (NDE) methods were used to determine the extent of damage in the substrate and coating with increasing projectile velocity. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. At projectile velocities less than 125 m/s, no detectable damage was noticed in the MI SiC/SiC composites coated with 525 m EBC. With increase in projectile velocity beyond this value, spallation of EBC layers, delamination of fiber plies, and fiber fracture were detected. At a fixed projectile velocity, the composites coated with 525 m EBC showed less damage than the composite coated with 225 m EBC. Both types of EBC coated composites retained a large fraction of the baseline properties of as-fabricated composites and exhibited non-brittle failure after impact testing at projectile velocities up to 375 m/s. Exposure of impact tested specimens in a moisture environment at 1316 C for 500 hr indicated that the through-the-thickness cracks in the EBC coating and delamination cracks in the substrate generated after impact testing acted as conduits for internal oxidation.

Fox, Dennis S.↗
NASA NTRS2012

Environmental Barrier Coating (EBC) Durability Modeling; An Overview and Preliminary Analysis

A study outlining a fracture mechanics based model that is being developed to investigate crack growth and spallation of environmental barrier coating (EBC) under thermal cycling conditions is presented. A description of the current plan and a model to estimate thermal residual stresses in the coating and preliminary fracture mechanics concepts for studying crack growth in the coating are also discussed. A road map for modeling life and durability of the EBC and the results of FEA model(s) developed for predicting thermal residual stresses and the cracking behavior of the coating are generated and described. Further initial assessment and preliminary results showed that developing a comprehensive EBC life prediction model incorporating EBC cracking, degradation and spalling mechanism under stress and temperature gradients typically seen in turbine components is difficult. This is basically due to mismatch in thermal expansion difference between sub-layers of EBC as well as between EBC and substrate, diffusion of moisture and oxygen though the coating, and densification of the coating during operating conditions as well as due to foreign object damage, the EBC can also crack and spall from the substrate causing oxidation and recession and reducing the design life of the EBC coated substrate.

Abdul-Aziz, A.↗
NASA NTRSDate not supplied

Thermochemical/Thermomechanical Synergies in High Temperature Solid Particle Erosion of CMAS-Exposed EBCs

Environmental barrier coatings (EBCs) are an enabling technology for the use of SiC-based ceramic matrix composites in next generation gas turbine engines. In the extreme engine environment, EBCs must be able to withstand a variety of individual damage mechanisms and their interactions with each other. Ingested particulates/debris can cause both thermochemical and thermomechanical degradation of EBCs. Siliceous debris primarily based on calcium magnesium aluminosilicates (CMAS) can melt and infiltrate and/or react with EBCs above >1200°C. Similarly, ingested debris can lead to mechanical damage and recession of coatings due to particulate erosion. Both modes of degradation can occur simultaneously during engine operation, and it is crucial to comprehensively understand the mechanisms of coating failure due to high-temperature particulate interactions. This study assesses the erosion durability of Yb2Si2O7-based EBCs exposed to CMAS of various loads in NASA Glenn’s Erosion Burner Rig Facility. CMAS exposures and erosion testing were carried out at 1316°C. The effects of CMAS loading and exposure time on EBC erosion durability were evaluated using Al2O3 as an erodent material.

EBC↗
NASA NTRSDate not supplied

Thermochemical/Thermomechanical Synergies in High-Temperature Solid Particle Erosion of CMAS-Exposed EBCs

Environmental barrier coatings (EBCs) are an enabling technology for the use of SiC-based ceramic matrix composites in next generation gas turbine engines. In the extreme engine environment, EBCs must be able to withstand a variety of individual damage mechanisms and their interactions with each other. Ingested particulates/debris can cause both thermochemical and thermomechanical degradation of EBCs. Siliceous debris primarily based on calcium magnesium aluminosilicates (CMAS) can melt and infiltrate and/or react with EBCs above 1200°C. Similarly, ingested debris can lead to mechanical damage and recession of coatings due to particulate erosion. Both modes of degradation can occur simultaneously during engine operation, and it is crucial to comprehensively understand the mechanisms of coating failure due to high-temperature particulate interactions. This study assesses the erosion durability of Yb 2 Si 2 O 7 -based EBCs exposed to CMAS of various loads in NASA Glenn’s Erosion Burner Rig Facility. CMAS exposures and erosion testing were carried out at 1316°C. The effects of CMAS loading and exposure time on EBC erosion durability were evaluated using Al 2 O 3 as an erodent material.

CMAS↗
NASA NTRSDate not supplied

Thermochemical/Thermomechanical Synergies in High Temperature Solid Particle Erosion of CMAS Exposed EBCs

Environmental barrier coatings (EBCs) are an enabling technology for the use of SiC-based ceramic matrix composites in next generation gas turbine engines. In the extreme engine environment, EBCs must be able to withstand a variety of individual damage mechanisms and their interactions with each other. Ingested particulates/debris can cause both thermochemical and thermomechanical degradation of EBCs. Siliceous debris primarily based on calcium magnesium aluminosilicates (CMAS) can melt and infiltrate and/or react with EBCs above >1200°C. Similarly, ingested debris can lead to mechanical damage and recession of coatings due to particulate erosion. Both modes of degradation can occur simultaneously during engine operation, and it is crucial to comprehensively understand the mechanisms of coating failure due to high-temperature particulate interactions. This study assesses the erosion durability of Yb 2 Si 2 O 7 -based EBCs exposed to CMAS of various loads in NASA Glenn’s Erosion Burner Rig Facility. CMAS exposures and erosion testing were carried out at 1316°C. The effects of CMAS loading and exposure time on EBC erosion durability were evaluated using Al2O3 as an erodent material.

EBC↗
NASA NTRS2020

Influence of Thermally-Grown Oxide (TGO) Layer on the Driving Forces Associated with Failure in Environmental Barrier Coating (EBC) Systems

Environmental barrier coatings (EBC) is an enabling technology for the successful application of ceramic matrix composites (CMCs) in air-breathing gas turbine engines. Spallation of environmental barrier coating (EBC) induced by thermally grown oxide (TGO) layer is a key EBC failure mode. The TGO layer, resulting from steam oxidation, grows either from a silicon bond coat layer (if present) or from the silicon carbide (SiC) based substrate itself. Critical thickness of the TGO layer for failure is in the range of 20-30 microns but it can vary due to exposure temperature, microstructure etc. Current work at NASA Glenn Research Center, under the Revolutionary Tools and Methods (RTM) project is aimed at addressing associated failure modes in EBC systems and developing robust analysis tools to aid in the design/analysis of these systems. The objective of the current work is to conduct a sensitivity study to examine the influence of uniformly and non-uniformly grown oxide layers with or without damage on the associated driving forces leading to spallation of the EBC when subjected to isothermal loading. Initial results indicate that the presence of damage (vertical cracks caused by in-plane stresses) enhances the stresses that are present due to non-uniformity. However, the presence of non-uniformity itself is still the main factor influencing the magnitude of peel and shear stresses in the TGO layer.

Mital, Subodh K.↗
NASA NTRS2017

Water Vapor Corrosion in EBC Constituent Materials

Environmental Barrier Coating (EBC) materials are sought after to protect ceramic matrix composites (CMC) in high temperature turbine engines. CMCs are particularly susceptible to degradation from oxidation, Ca-Al-Mg-Silicate (CMAS), and water vapor during high temperature operation which necessitates the use of EBCs. However, the work presented here focuses on water vapor induced recession in EBC constituent materials. For example, in the presence of water vapor, silica will react to form Si(OH)4 (g) which will eventually corrode the material away. To investigate the recession rate in EBC constituent materials under high temperature water vapor conditions, thermal gravimetric analysis (TGA) is employed. The degradation process can then be modeled through a simple boundary layer expression. Ultimately, comparisons are made between various single- and poly-crystalline materials (e.g. TiO2, SiO2) against those found in literature.

coating↗
NASA NTRS2015

Mechanical Properties of Air Plasma Sprayed Environmental Barrier Coating (EBC) Materials

Development work in Environmental Barrier Coatings (EBCs) for Ceramic Matrix Composites (CMCs) has focused considerably on the identification of materials systems and coating architectures to meet application needs. The evolution of these systems has occurred so quickly that modeling efforts and requisite data for modeling lag considerably behind development. Materials property data exists for many systems in the bulk form, but the effects of deposition on the critical properties of strength and fracture behavior are not well studied. We have plasma sprayed bulk samples of baseline EBC materials (silicon, ytterbium disilicate) and tested the mechanical properties of these materials to elicit differences in strength and toughness. We have also endeavored to assess the mixed-mode fracture resistance, Gc, of silicon in a baseline EBC applied to SiCSiC CMC via four point bend test. These results are compared to previously determined properties of the comparable bulk material.

Ceramic Matrix Composites (CMC's)↗
NASA NTRS2001

Degradation Of Environmental Barrier Coatings (EBC) Due To Chemical and Thermal Expansion Incompatibility

Current environmental barrier coatings (EBCs) consist of multiple layers, with each layer having unique properties to meet the various requirements for successful EBCs. As a result, chemical and thermal expansion compatibility between layers becomes an important issue to maintaining durability. Key constituents in current EBCs are mullite (3Al2O3-2SiO2), BSAS (BaO(1-x)-SrO(x)-Al2O3-2SiO2), and YSZ (ZrO2-8 wt.% Y2O3). The mullite-BSAS combination appears benign although significant diffusion occurs. Mullite-YSZ and BSAS-YSZ combinations do not react up to 1500 C. Thermally grown SiO2- BSAS and mullite-BSAS-YSZ combinations are most detrimental, forming low melting glasses. Thermal expansion mismatch between YSZ and mullite or BSAS causes severe cracking and delamination.

Lee, Kang N.↗
NASA NTRS2004

Foreign Object Damage Resistance of Uncoated and EBC Coated SiC/SiC Composites

SiC/SiC composites fabricated by the melt infiltration method are candidate materials for the turbine components such as combustor liners, nozzle vanes and blades because of their high temperature strength, and thermal conductivity. To avoid surface recession in a combustion environment containing moisture, these materials also require an environmental barrier coating (EBC). Under thermal loading condition alone, the EBC coated SiC/SiC components show microstructural and strength stability after -1 5000 hr exposure to 12OO0C in combustion environment. However, the stability of SiC/SiC composites under impact conditions is not fully understood. In this study, both uncoated and EBC coated SiC/SiC composite specimens were impact tested by steel-ball projectiles at room temperature and at 1300 C in air. After impact, the specimens were analyzed under a scanning electron microscope to assess coating damage, and then tensile and bend tested at room temperature to determine their residual strength. The extent of coating and substrate damage with increasing projectile velocity was imaged and analyzed using nondestructive evaluation (NDE) methods such as micro focus x-ray radiography, tomography, and thermal wave imaging. The mechanical property results of impacted specimens are correlated with the NDE results and the scanning electron microscopy (SEM) observations. Influence of projectile velocity on impact damage of the coating/substrate, and the implication coating damage on durability of the composite will be discussed.

Bhatt, R. T.↗
NASA NTRS2014

Damage Characterization of EBC-SiCSiC Ceramic Matrix Composites Under Imposed Thermal Gradient Testing

Due to their high temperature capabilities, Ceramic Matrix Composite (CMC) components are being developed for use in hot-section aerospace engine applications. Harsh engine environments have led to the development of Environmental Barrier Coatings (EBCs) for silicon-based CMCs to further increase thermal and environmental capabilities. This study aims at understanding the damage mechanisms associated with these materials under simulated operating conditions. A high heat-flux laser testing rig capable of imposing large through-thickness thermal gradients by means of controlled laser beam heating and back-side air cooling is used. Tests are performed on uncoated composites, as well as CMC substrates that have been coated with state-of-the-art ceramic EBC systems. Results show that the use of the EBCs may help increase temperature capability and creep resistance by reducing the effects of stressed oxidation and environmental degradation. Also, the ability of electrical resistance (ER) and acoustic emission (AE) measurements to monitor material condition and damage state during high temperature testing is shown; suggesting their usefulness as a valuable health monitoring technique. Micromechanics models are used to describe the localized stress state of the composite system, which is utilized along with ER modeling concepts to develop an electromechanical model capable of characterizing material behavior.

protective coatings (nonmetallic)↗
NASA NTRSDate not supplied

Thermochemical and microstructural contributions of high temperature particle erosion durability in CMAS exposed EBCs

Particulate/debris damage caused by ingestion of calcium magnesium aluminosilicates (CMAS) hinders the use of environmental barrier coatings (EBCs) to protect SiC-based ceramic matrix composite components in next generation gas turbine engines. Similarly, ingestion of any debris in the engine can lead to mechanical damage and recession of coatings due to particulate erosion. Investigating particulate interactions at relevant engine conditions is crucial in determining limiting mechanisms in the operating lifetime of EBCs. This study assesses the effects of extrinsic phase formation and microstructural changes due to CMAS interactions on the erosion durability of Yb 2 Si 2 O 7 -based EBCs in NASA Glenn’s Erosion Burner Rig Facility. CMAS exposures and erosion testing were carried out at 1316°C. Using 60 µm Al 2 O 3 particles as the erodent material, the effects of CMAS loading on erosion durability at various impingement angles were evaluated.

Jamesa L. Stokes↗
NASA NTRS2017

Cyclic Fatigue Durability of Uncoated and EBC Coated 3D SiC/SiC Composites Under Thermal Gradient Conditions at 2700F in Air

Ceramic matrix composites (CMCs) such as SiCSiC are currently being designed and implemented in high temperature sections of aerospace turbine engines. Such components will be subject to through-thickness thermal gradients, which may affect the durability. In this study, SiCSiC CMCs with a hybrid chemical vapor infiltrated (CVI) and polymer infiltration and pyrolysis (PIP) matrix were loaded in tension while one surface was heated with a laser and the opposite surface was cooled. The samples were each coated with an environmental barrier coating (EBC), which was produced by electron beam physical deposition (EBPVD). Results for CMCs tested with and without the EBC be discussed.

Ceramic matrix composite↗
NASA NTRS2020

Experimental Setup and Parameters for Testing Uncoated and EBC-Coated CMCs under Thermal Gradients Induced by Laser Heating and Backside Air Cooling

An experimental setup to induce through thickness thermal gradients in ceramic matrix composite (CMC) specimens without and with an applied environmental barrier coating (EBC) is described in detail. Components of the experimental set up include a laser for the heat source on the front of the specimen, a cooling air nozzle on the back of the specimen with pyrometers to measure temperatures on both sides, and a full-field thermal image camera to ensure uniformity of the temperature distribution in the gage section of the specimen. Test specimen is loaded in a servohydraulic system, which can superimpose either static or dynamic loads on the specimen to investigate creep and fatigue behaviors of CMCs under through thickness thermal gradient conditions. Mechanical strains on the front and backsides of the test specimen were measured during the thermal gradient tests with superimposed mechanical loading using two contact extensometers. Selected through thickness thermal gradient test results generated with the experimental setup under different nominal front side temperatures and multiple constant laser power levels on uncoated and EBC coated CMCs and procedures used to generate those results are described in this report. Two examples of tests conducted using the test system on uncoated CMCs under creep and sustained-peak, low-cycle fatigue with through thickness thermal gradient conditions are provided.

ceramic matrix composite, environmental barrier co↗
NASA NTRSDate not supplied

Exploring the Effect of EBC Composition on CMAS Wetting Behavior

Rare-earth disilicate (REDS) materials are existing materials used in environmental barrier coating (EBC) for the protection of structural materials in the hot-section of turbine engines. REDS interactions with molten calcium-magnesium-aluminosilicate (CMAS) debris are of interest to understand molten CMAS attack and improve CMAS mitigation strategies. This work assesses the effect of REDS composition on CMAS wetting by investigating wetting angle, spreading, and reactivity. Freestanding atmospheric plasma spray (APS) REDS coatings (for RE = Y, La, Nd, Gd, Yb, Lu) were exposed to 10 mg of CMAS (Ca33-Mg9-Al13-Si45 in single cation mol%) in stagnant lab air at 1250C. APS YbDS was compared to a dense spark plasma sintered (SPS) phase-pure Yb2Si2O7 and a nominal 20 vol% phase-mixture of Yb 2 SiO 5 in Yb 2 Si 2 O 7 (20YbMS/YbDS). CMAS mass was held constant but specimen surface areas varied, yielding a range of loading between ~6 and 10 mg/cm2. CMAS was loaded as a cylindrical rod atop the specimen surface, polished to 4000 grit, and heated to temperature in a Linseis L74/HS/1700 heating microscope. The heating microscope measured the evolution of molten CMAS diameter, height, and contact angle. Molten CMAS diameter at 1150C and contact angle measurements after two hours of exposure at 1250C yielded a positive trend with rare-earth cation size. There was no statistically significant difference in CMAS wetting behavior between SPS YbDS and 20YbMS/YbDS. Post-exposure specimens were examined in plan view and cross-section with XRD, SEM, and EDS. CMAS spreading was cross-examined using plan view SEM, while reactivity utilized plan view XRD and cross-sectional SEM/EDS.

Clark Luckhardt↗