Results for “IASCC”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

TEM Specimen Manufacturing to Support Analysis of IASCC Mechanisms in Irradiated Austenitic Steels – Light-Water– Relevant Materials

The present report describes the manufacturing of samples for advanced microstructure studies of mechanisms of irradiation-assisted stress corrosion cracking (IASCC) in the materials of light-water reactor (LWR) internal components. The samples were manufactured via FIB (focused ion beam milling) from 4-point-bend specimens subjected to oxidation and mechanical loading in a simulated LWR environment (primary water, PW). The corrosion tests were conducted at the University of Michigan (UM), and the tested specimens were transported to ORNL to perform FIB work. Finally, the manufactured FIB specimens were shipped back to the UM for microstructure characterization. Section 1 in the report provides a brief introduction; Section 2 describes materials, their in-service and irradiation history, and the geometry of specimens for IASCC testing. Section 3 documents typical work steps (specimen mapping) and reports the number of manufactured FIB objects. Section 4 briefly describes the preliminary results of microstructure analysis performed at the University of Michigan and highlights the key findings. The summary and conclusions section discusses future possible future steps and generalizes the obtained results, their unique character, and their importance for the nuclear industry.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2022

Examination Of IASCC In 304 Stainless Steel Core Shroud From A Commercial Boiling Water Reactor (BWR)

The 304 stainless steel core shroud and the accompanying weld material from a commercial boiling-water reactor (BWR) experienced an estimated dose of ~3.5 dpa neutron irradiation leading to irradiation-assisted stress corrosion cracking (IASCC). The resulting IASCC crack tips are examined with high-resolution analysis techniques, including scanning electron microscopy (SEM), scanning transmission electron microscopy (STEM), and atom probe tomography (APT), with select examples of directly correlated STEM/APT observations. Analytical observations reveal the crack morphology, composition, microstructure, and any associated corrosion-induced or radiation-induced segregation in the local metal grain boundaries ahead of the propagating SCC cracks. The observed oxide composition and structure were in-line with expectations, consisting of a Cr-rich inner oxide and a Fe-rich outer oxide, with the leading crack tip oxide being Cr-rich. In addition, the leading grain boundary exhibited typical radiation-induced segregation signatures that were largely unperturbed by the accompanying corrosion. Finally, the quantitative capabilities and limitations of STEM and APT in the context of corrosion fronts and grain boundary chemistry from the directly correlated measurements are discussed.

Olszta, Matthew J.↗
DOE OSTI2024

IASCC of 304 SS in BWR environments: Effects of post-irradiation annealing and surface condition

To investigate the impact of low-temperature post-irradiation annealing (PIA) on the stress corrosion cracking of neutron-irradiated 304 stainless steel, constant extension rate tests were conducted in simulated boiling water reactor normal water chemistry (BWR-NWC) and hydrogenated water chemistry (HWC) environments. Ten tensile samples, comprising five as-irradiated and five PIA specimens, were prepared by electropolishing the gauge section of electric discharge machined (EDM) samples. Here, the annealing treatment reduced the yield strength from approximately 550 MPa to around 425 MPa and significantly restored the ductility and the strain hardening capability of the alloy. Consequently, the susceptibility of this material to irradiation-assisted stress corrosion cracking (IASCC) was effectively mitigated, which is more prominent in HWC, as evident from fractography, which indicated a decreased propensity for intergranular (IG) fracture. Furthermore, it was observed that the polished surface facilitated crack initiation more readily than the EDM surface, suggesting that the EDM process suppressed crack initiation to some extent.

Crack initiation↗
DOE OSTI2024

In-service Oxidation and IASCC in High Fluence Baffle-Former Bolts Retrieved from a Westinghouse PWR

Baffle-former bolts (BFBs) are subjected to significant mechanical stress and neutron irradiation from the reactor core during the plant operation. Over the long operation period, these conditions lead to potential degradation and reduced load-carrying capacity of the bolts, and life extension of existing pressurized water reactors (PWRs) would only cause more damage to the bolt material. To this end, the Light Water Reactor Sustainability (LWRS) Program Materials Research Pathway (MRP) successfully harvested two high fluence BFBs from a Westinghouse two-loop downflow type PWR in 2016. In the same year, the two BFBs were received at the Westinghouse Churchill facility for inspection and specimen fabrication. The fabrication was completed in 2017 with specimens shipped to Oak Ridge National Laboratory (ORNL) for further testing. The objective of this project is to provide information that is integral to evaluating end of life microstructure and properties as a benchmark of international models developed for predicting radiation-induced swelling, segregation, precipitation, mechanical property degradation, and with the latest findings, susceptibility to irradiation-assisted stress corrosion cracking (IASCC).

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

Investigation of the irradiation effects in additively manufactured 316L steel resulting in decreased irradiation assisted stress corrosion cracking susceptibility

While additive manufacturing (AM) is an area of increasing interest to the nuclear industry, there are significant research and development needs prior to successful implementation of additively manufactured components into reactors. AM steel behaves differently than traditional wrought material, as has been observed in numerous mechanical testing studies. The nuclear industry must also understand the material response to irradiation. This work examines the irradiation damage and the irradiation assisted stress corrosion cracking behavior (IASCC) of both proton irradiated AM and wrought 316L steel. For IASCC testing, specimens were strained to 4% plastic strain in a simulated boiling water reactor environment (288°C, 0.2 µS/cm). Transmission and scanning electron microscopy, confocal microscopy, and X-ray computed tomography were used to examine coupons of the material as well as tensile bars used in the IASCC testing. This work found that the wrought 316L was more susceptible to IASCC than the AM steel, however, some IASCC was observed in the AM steel when tested with the tensile axis parallel to the build direction. Electron microscopy has shown significantly fewer radiation induced voids formed in the AM steel. While the pre-existing pore network in the AM steel may act as a sink to point defects, this is not expected to be the major factor in the reduced swelling observed in the AM steel. The lower density of radiation induced voids was expected to contribute to the IASCC resistance by decreasing the localization of deformation in the irradiated specimens, however, severity of localized deformation in AM steel, measured in dislocation channel spacing and height, was similar or more severe to that found in wrought. In conclusion, the presence of severe cracking in the wrought specimens did not allow for a direct comparison of localized deformation severities between the AM and wrought steel.

Additive manufacturing↗
DOE OSTI2024

Dislocation channel broadening–A new mechanism to improve irradiation-assisted stress corrosion cracking resistance of additively manufactured 316 L stainless steel

Additively manufactured (AM) 316 L stainless steel (SS) after hot isostatic pressing (HIP) was found to exhibit superior resistance to irradiation-assisted stress corrosion cracking (IASCC) in high-temperature water, as compared to wrought 316 L SS. The well-accepted IASCC factors of radiation-induced segregation (RIS) and radiation hardening are not accurate descriptions of IASCC susceptibility in this case. A decreased strain localization along grain boundaries, caused by dislocation channel broadening, was confirmed to suppress crack initiation. A unique distribution of irradiation-induced defects in HIP AM 316 L SS eased dislocation cross-slip compared to those in the wrought counterpart, thus increasing the channel width near the grain boundaries. Here for the first time, this study highlights the importance of dislocation channel broadening as a potential mechanism to further improve the IASCC resistance of 316 L SS and provides direct experimental evidence based on commercial-grade materials.

316L stainless steel↗
DOE OSTI2021

Radiation Effects Related to Repaired BWR Core Shrouds

The material properties of the core shroud and supporting tie rod components are important factors for Boiling Water Reactor (BWR) life extension considerations. Given the variability of nickel and boron content found in 304 stainless steel shroud plates, and XM-19 and Inconel X-750 tie rod materials, this paper combines the latest spectral information in the vicinity of the core shroud to calculate hydrogen and helium gas production limits as well as atomic displacement damage spanning 80 full-power years (FPY) using the SPECTER code. Results indicate that, whereas boron has little effect on the atomic displacement damage, helium production from boron can be important and must be included in weldability assessments. Since the boron concentration is uncertain, helium generation is calculated assuming a composition range based on specifications and reported measurements. The results show that helium production caused by transmutations in the 304 SS shroud material are dominated by the concentration of boron and will have a significant impact on weldability after only a few years of service. For tie rods, the susceptibility to irradiation-assisted stress corrosion cracking (IASCC) has been assessed by determining helium production in Inconel X-750 IASCC specimens irradiated in the Advanced Test Reactor (ATR) reactor and correlating with the helium produced in a BWR. As a tie rod material in a high thermal neutron flux environment, Inconel X-750 is more likely to be IASCC sensitive during service in a BWR due to helium than the XM-19 stainless steel alloy because of a greater nickel content and boron concentration. Weldability of the core shroud plate material, IASCC of the tie rod materials, and the gamma photon contribution to radiation damage are discussed.

radiation damage in materials, BWR↗
DOE OSTI2023

Irradiation-assisted Stress Corrosion Cracking of PWRirradiated Type 347 Stainless Steel (NSUF CINR 19-16567)

This document serves as the final report for NSUF Project 19-16567 (Reference 1) and its supporting contracts (References 2 and 3). It documents completion of testing of specimens fabricated as previously described in Reference 4. At a high level, the purpose of the testing is to generate data to support continued operation of light water reactors (LWR) and provide further understanding of irradiation-assisted stress corrosion crack (IASCC) initiation in baffle-former bolt materials. Baffle-former bolts that had been extracted from commercial pressurized water reactors (PWRs) were machined into miniature 4-point bend specimens and TEM samples at the Westinghouse Churchill Site hot cell facility. These samples were then shipped to the University of Michigan to undergo IASCC initiation testing in simulated PWR primary coolant containing either LiOH or KOH additions. Overall, 15 samples were tested, 8 in water with KOH additions and 7 in water with LiOH additions, until indications of cracking were observed. Crack initiation stress was similar in both water environments at 50-60% of the irradiated yield stress. Post-test examination of the cracking sites, including scanning electron microscopy and transmission electron microscopy, demonstrated that the crack initiation mechanism and crack initiation rates were similar between the two different water chemistries. A grain boundary oxidation and oxide fracture mechanism was observed to be responsible for crack initiation.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2024

How irradiation promotes intergranular stress corrosion crack initiation

Irradiation assisted stress corrosion cracking (IASCC) is a form of intergranular stress corrosion cracking that occurs in irradiated austenitic alloys. It requires an irradiated microstructure along with high temperature water and stress. The process is ubiquitous in that it occurs in a wide range of austenitic alloys and water chemistries, but only when the alloy is irradiated. Despite evidence of this degradation mode that dates back to the 1960s, the mechanism by which it occurs has remained elusive. Here, using high resolution electron backscattering detection to analyze local stress-strain states, high resolution transmission electron microscopy to identify grain boundary phases at crack tips, and decoupling the roles of stress and grain boundary oxidation, we are able to unfold the complexities of the phenomenon to reveal the mechanism by which IASCC occurs. The significance of the findings impacts the mechanical integrity of core components of both current and advanced nuclear reactor designs worldwide.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Experimental Methods for the Performance Test of Environment-Assisted Cracking (EAC) in Nuclear Industry and Examples through NSUF

Environmentally assisted cracking (EAC) is a critical failure mode in nuclear reactor environments, where materials are exposed to high temperatures, radiation, and corrosive media. Specific EAC studies in nuclear environments include stress corrosion cracking in primary water chemistry, irradiation-assisted stress corrosion cracking (IASCC) under neutron exposure, and hydrogen induced cracking (HIC) in reactor pressure vessels. The experimental methodologies of EAC include slow strain rate testing (SSRT), constant load, and cyclic loading techniques, conducted in autoclaves designed to simulate the reactor’s operational environments. This paper highlights several experimental case studies, especially on IASCC, conducted within the Nuclear Science User Facilities (NSUF).

36 - MATERIALS SCIENCE↗
DOE OSTI2023

Irradiation-assisted cracking of SA508-304L weldments with 308L groove filler and 309L butter in hot water immersion constant rate extension tests

Low alloy SA508 bainitic steel is often welded to 300 series austenitic stainless steel in nuclear power plants. These dissimilar metal weldments use 309L butter applied to the low alloy steel and 308L groove filler material to join the 309L to austenite. High alloy steels (such as the 308L and 309L material used here) have been identified as having greater susceptibility to irradiation-assisted stress corrosion cracking (IASCC). Evidence is presented here of cracking under tensile loads in 309L weldment butter in LWR hydrothermal conditions that correlates irradiation induced changes at δ ferrite–γ austenite phase boundaries and γ–γ grain boundaries; specifically intergranular Cr 23 C 6 precipitates. Cracking is not observed in irradiated 308L groove filler under the same conditions. Both the 309L butter and 308L filler material have a duplex or mixed δ–γ phase microstructure due to solidification during the welding procedure. We have performed constant extension rate autoclave immersion tests in BWR normal water chemistry hot water (288 °C, 10 MPa, 2000 wt. ppb dissolved oxygen, <100 nS/cm conductivity, neutral pH) of proton irradiated (2 MeV, approximately 3 displacements per atom at a depth of 10 μm) tensile specimens. Proton irradiation to the dpa levels used here induced Cr 23 C 6 carbide precipitation at γ–γ grain boundaries and δ–γ phase boundaries in the 309L butter but not the 308L filler. Cracking was observed in the proton-irradiated volume of 309L at these interfaces in the vicinity of the Cr 23 C 6 precipitates. We hypothesis the SA508 is the source of carbon in the 309L butter. Cr depletion at γ–γ grain boundaries was also observed and may also be a root cause of cracking. Furthermore, the 309L butter is under significant tensile residual stress in the weldment that adds to applied tensile loads and this too may be a contributing factor.

309L weld butter↗
DOE OSTI2023

Experimental and Computational Studies of Stress Corrosion Cracking of Alloys 308/309 and 82/182 Weldments in Corrosive and Radiation Environment

The goal of the project was to determine factors that influence SCC and IASCC in weldments found in LWR nuclear power plants. We focused on a SA508-304L SS weldment fabricated by EPRI using gas tungsten arc welding and used an aggressive BWR normal water chemistry (NWC) immersion environment. This weldment used 309L butter and 308L groove filler material. The microstructure of the 309L butter was non-uniform, exhibiting a 20–30μm thick martensitic layer closest to the SA508 interface, a 1–4 mm thick single γ austenite phase dilution zone, and a γ–δ duplex region extending to the 308L groove filler. The 308L groove filler had an entirely γ–δ duplex microstructure. Two approximately 1-inch thick 304L and SA508 plates approximately 12 by 6 square inches were joined using standard nuclear grade welding techniques. This included a post weld heat treatment of the 309L butter after application, a 0.32 cm fit-up root opening, and 57 bead lines of 308L groove filler applied in 18 layers. A 60 degree weld bevel angle was used and the 309L butter was 1.5 cm thick. Displacement cascade damage was induced using proton irradiation at the Michigan Ion Beam Laboratory. The incident proton energy was 2 MeV, the sample temperature was 360 ºC, and the calculated dpa value at 10 μm (60% of the Bragg peak depth of ~18 μm) was 5 dpa using the quick Kinchin-Pease model. Proton irradiation to this damage level required approximately 125 hours of beam time. Two types of samples were irradiated, tensile specimens and TEM bars. Samples were selected from all regions of the weldment, including the SA508-309L butter interface, the 309L-308L interface, and 308L-304L interface. The stainless steel alloys (304L, 308L, and 309L) within the heat affected zone are characterized by a duplex skeletal morphology of δ-ferrite and γ-austenite resulting from the recrystallization associated with weld fabrication. Approximately 7 to 8 mm of length along the specimen was irradiated. The gauge volume surfaces were mechanically polished and then electro-polished to remove mechanical damage from the mechanical polishing step prior to irradiation. Immersion tests were performed in a recirculating autoclave under BWR NWC conditions (2000 ppb wt. dissolved oxygen, neutral pH, 288 ºC, 10 MPa, and inlet water conductivity <100 nS/cm) to accelerate corrosion. Constant strain rate tests were performed either to failure or to approximately 5% strain. Strain rates of 10 -7 to 10 -6 mm/mm/s were used and typical immersion testing required four to six weeks to achieve failure or strains near 5%. Analysis primarily used advanced electron microscopy techniques of FIB lift out specimens.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Effects of Radiation-Induced Defects on Corrosion

The next generation of nuclear reactors will expose materials to conditions that, in some cases, are even more extreme than those in current fission reactors, inevitably leading to new materials science challenges. Radiation-induced damage and corrosion are two key phenomena that must be understood both independently and synergistically, but their interactions are often convoluted. In the light water reactor community, a tremendous amount of work has been done to illuminate irradiation-corrosion effects, and similar efforts are under way for heavy liquid metal and molten salt environments. While certain effects, such as radiolysis and irradiation-assisted stress corrosion cracking, are reasonably well established, the basic science of how irradiation-induced defects in the base material and the corrosion layer influence the corrosion process still presents many unanswered questions. In this review, we summarize the work that has been done to understand these coupled extremes, highlight the complex nature of this problem, and identify key knowledge gaps.

36 MATERIALS SCIENCE↗
DOE OSTI2025

SEM/EBSD Characterization of Baffle-Former Bolts Designated for High Energy X-ray Microscopy Studies at the Advanced Photon Source

This report documents the microstructural and surface characterization of two high-fluence baffle-former bolts (BFBs) harvested from a commercial pressurized water reactor (PWR) after nearly four decades of service. These bolts experienced extreme conditions including high neutron fluence, elevated temperatures, corrosive primary water, and sustained mechanical loads, all of which contribute to degradation mechanisms such as irradiation-assisted stress corrosion cracking (IASCC). Using scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD), the study assessed bulk and near-surface microstructures, grain boundary characteristics, and in-service oxide layers. The results revealed significant differences between bolts exposed to 41 dpa and 29 dpa, including differences in recrystallization extent, deformation structures, and oxidation morphology. These findings establish critical baseline data for integration with advanced synchrotron-based high-energy X-ray microscopy (HEXM) and computational crystal plasticity models. Ultimately, the work supports improved mechanistic understanding and predictive capability regarding the long-term performance of reactor core internal components.

Lach, Tim [Oak Ridge National Laboratory (ORNL), O↗
DOE OSTI2022

In-Cell Thermal Creep Frame Capability: Out-of-Cell Construction and Subsized Sample Testing

This report describes the activities related to the construction of an in-cell thermal creep test facility for small-scale specimens in the irradiation-assisted stress-corrosion cracking (IASCC) hotcell located at the Fuels and Applied Science Building (FASB) at INL. The whole project includes three stages: (i) conceptual design; (ii) out-of-cell demonstration tests; and (iii) in-cell demonstration testing. During the current fiscal year (FY)-2022, materials and equipment required to construct the conceptual design outlined in a previous report were procured. Frames for conducting out-of-cell testing have been constructed, and testing plans have been developed to assess the operation of the newly constructed frames. Preliminary testing of flat subsized tensile specimens on ASTM creep frames has also been completed for two sample thicknesses: 0.75 mm and 1.0 mm.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Impact of Irradiation on Microstructure and Mechanical Properties of Materials Produced by Advanced Manufacturing

Advanced non-light water reactor designs, known as Generation IV (Gen IV) reactors, typically operate at higher temperatures and under more extreme radiation conditions than conventional light water reactors. A critical aspect of the successful deployment and advancement of Gen IV reactor designs is the selection of appropriate structural materials for specific applications, which necessitates the timely development of new materials and manufacturing processes. Advanced manufacturing (AM) offers numerous opportunities for innovative designs, enabling the production of high-performance components with potentially shorter development cycles compared to traditional manufacturing methods. However, a significant challenge in deploying AM technologies in the nuclear energy sector is the current lack of data on the irradiation performance of AM-produced components. This presentation will discuss neutron and ion irradiation results of AM materials, including stainless steel 316L, Grade 91, SA508, Inconel 718, and Inconel 625 materials. The materials were manufactured by AM, such as Powder Metallurgy Hot Isostatic Pressing (PM HIP), Laser Powder Bed Fusion (LPBF) and Directed Energy Deposition (DED). The effects of neutron irradiation on microstructure (e.g., dislocations, loops, and nanoclusters), tensile properties (e.g., strength and ductility), and ion irradiation on Irradiation-Assisted Stress Corrosion Cracking (IASCC) will be explored. Results are collected from several projects supported by the Nuclear Science User Facilities (NSUF) program.

36 - MATERIALS SCIENCE↗