Tungsten fiber-reinforced nickel superalloy combines the strength of refractory metals with the oxidation resistance of superalloys. Knowledge of the relationship between fabrication technique, matrix compositions and fiber sizes minimized fiber-matrix reaction. Potential application includes high temperature turbine components.
High Cycle Fatigue (HCF) induced failures in aircraft gas-turbine and rocket engine turbopump blades is a pervasive problem. Single crystal turbine blades are being utilized in rocket engine turbopumps and jet engines throughout industry and NASA because of their superior creep, stress rupture, melt resistance and thermomechanical fatigue capabilities over polycrystalline alloys. Single-crystal materials have highly orthotropic properties making the position of the crystal lattice relative to the pan geometry a significant factor in the overall analysis. The failure modes of single crystal turbine blades is complicated to predict due to the material orthotropy and variations in crystal orientations. A fatigue failure criteria based on the maximum shear stress amplitude [delta t max] on the 30 slip systems, is presented for single crystal nickel superalloys (FCC crystal). This criteria reduces the scatter in uniaxial LCF test data, for four different specimen orientations, for PWA 1484 at 1200 F in air, quite well. A power law curve fit of the failure parameter, delta t max, vs. cycles to failure is presented.
Superalloy has 1000-hour strength of 37,000 psi at 2000 degrees F. The strength to density ratio of the composite is also greater, permitting applications where reduced weight rather than greater strength is desired.
Matrix composition, fabrication technique, and fiber diameter were selected to minimize fiber-matrix reaction and preserve composite strength. Composites may be used in place of superalloys where higher strength or greater strength-to-density ratios are advantageous, and will permit higher operating temperatures in particular applications.
Nickel-base superalloy has a strength of 20,000 psi at 2,200 degrees F, approximately double the strength of the strongest available cast nickel-base alloys. It is not subject to the formation of embrittling phases upon long time exposure at intermediate temperatures.
Nickel-based superalloys designed for use in gas turbine engines blades are difficult and expensive to properly machine without undue surface damage, due in part to their superior mechanical properties at high temperatures. Numerically controlled electrical discharge machining (EDM) has progressed to commonly be used as a machining process for initial sectioning, detailed roughing, and even some finishing operations. The objective of this study was to examine the effect of EDM on resulting surface conditions of superalloy 718 after slicing using typical rough, semi-finish, and finish condition sets with a typical wire EDM machine. Surface roughness, residual stress, and microstructures were compared for these conditions. The varied EDM conditions influenced surface roughness as intended. The residual stresses and surface roughness directly corresponding to the EDM steps were determined. While roughness decreased when progressing from rough to finish EDM conditions, tensile residual stresses unexpectedly increased. Brief assessments after EDM of two higher performance powder metallurgy disk superalloys ME209 and LSHR indicated this inverse relationship of roughness versus tensile residual stress was also present for these superalloys, where tensile residual stresses were significantly enhanced.
Nickel- (Ni-) base superalloy single crystals represent the state-of-the-art for turbine engine airfoil applications because they offer the best balance of properties under the high operating temperatures required for efficient engine operation. Current trends in alloy design take advantage of improved creep rupture strength with the addition of higher levels of refractory elements. In particular, the addition of significantly higher levels of rhenium in third-generation superalloys is key for both microstructural stability and creep rupture strength. Although refractories provide strength benefits, alloys tend to be unstable when their refractory content is high because of topologically close-packed (TCP) phases. The formation of these phases in sufficient amount is detrimental to the performance of these alloys because of their brittle nature and because they deplete the Nirich matrix of potent solid-solution strengthening elements.
Four cast nickel-base superalloys were oxidized at 1000 and 1100 C for times up to 100 hr in static air and a Mach 1 gas stream. The oxidation resistance was judged by weight change, metal thickness loss, depletion-zone formation, and oxide formation and morphology. The alloys which formed mostly nickel aluminate (NiAl2O4) and aluminum oxide (Al2O3) (B-1900, VIA, and to a lesser extent 713C) were more oxidation resistant. Poorer oxidation resistance was associated with the appearance of chromium sesquioxide (Cr2O3) and chromite spinel (738X). Refractory metal content had little effect on oxidation resistance. Refractory metals appeared in the scale as tapiolite (NiM2O6, where M represents the refractory metal). Thermal cycling in static air appeared to supply sufficient data for the evaluation of oxidation resistance, especially for alloys which form oxides of low volatility. For alloys of higher chromium levels with high propensities toward forming a chromium-bearing scale of higher volatility, testing under conditions of high gas velocity is necessary to assess fully the behavior of the alloy.
Nickel was substituted for Co to produce 0, 5, and the standard 10% versions of MAR-M247, a cast nickel-base superalloy. The microstructures of the alloys were examined in as-cast, heat treated, aged, and stress-rupture tested conditions using a variety of metallographic techniques and differential thermal analysis. As cobalt concentration was reduced from 10 to 0 wt %, the gamma-prime weight fraction decreased from 59 to 41%; W and Ti concentrations in the gamma-prime phase increased from 5 to 8 and 2 to 3 at.%, respectively; the mean gamma-prime particle size increased from 0.6 to 0.8 micron; Cr and Al concentrations in the gamma matrix decreased from 17 to 13 and 15 to 12 at.%, respectively; and the weight fraction of carbides increased by approximately 1%.
Single crystal nickel-base superalloys used as turbine engine blades can have much higher creep and fatigue resistance than many polycrystalline superalloys due to the absence of weak grain boundaries as well as the ability to orient the blades in the primary loading direction on to the low elastic modulus [001] orientation, which significantly lowers the stresses imposed on the blades. However, grain defects can occur in these crystals, impairing these advantages. In the present study, fatigue tests of a single crystal superalloy uncovered unexpected defective grains in the test specimens, which initiated premature fatigue failures. The characteristics of these defective grains and the associated failures were evaluated and related to the observed fatigue lives.
Single crystal nickel-base superalloys used as turbine engine airfoils can have much higher creep and thermal fatigue resistance required for blades and vanes than polycrystalline superalloys due to the absence of weak grain boundaries, as well as the low elastic modulus in the [001] single crystal growth direction (Refs. 1 and 2). This has allowed an increase in the turbine rim inlet temperatures for improved performance and efficiency. However, these advantages in performance require constraints on acceptable levels of single crystal defects, such as macroscopic grain boundaries at low angles to the primary grain (i.e., low angle boundaries or LAB), higher angle boundaries, small new grains nucleated at the blade surface (a.k.a. freckles), larger new grains, and also the single crystal blades’ orientation, typically degrees off of the [001] direction and the orientation of a transverse [010] direction with respect to blade geometry. Therefore, single crystal turbine airfoils, which are frequently used with as-cast surfaces, are grain etched and inspected before and after heat treatments to ensure these aspects conform to acceptability limits.
A nickel-based superalloy that resists embrittlement by hydrogen more strongly than does nickel alloy 718 has been developed. Nickel alloy 718 is the most widely used superalloy. It has excellent strength and resistance to corrosion as well as acceptably high ductility, and is recognized as the best alloy for many high-temperature applications. However, nickel alloy 718 is susceptible to embrittlement by hydrogen and to delayed failure and reduced tensile properties in gaseous hydrogen. The greater resistance of the present nickel-based superalloy to adverse effects of hydrogen makes this alloy a superior alternative to nickel alloy 718 for applications that involve production, transfer, and storage of hydrogen, thereby potentially contributing to the commercial viability of hydrogen as a clean-burning fuel. The table shows the composition of the present improved nickel-based superalloy in comparison with that of nickel alloy 718. This composition was chosen to obtain high resistance to embrittlement by hydrogen while maintaining high strength and exceptional resistance to oxidation and corrosion. The most novel property of this alloy is that it resists embrittlement by hydrogen while retaining tensile strength greater than 175 kpsi (greater than 1.2 GPa). This alloy exhibits a tensile elongation of more than 20 percent in hydrogen at a pressure of 5 kpsi (approximately equal to 34 MPa) without loss of ductility. This amount of elongation corresponds to 50 percent more ductility than that exhibited by nickel alloy 718 under the same test conditions.
Cast specimens of nickel-base superalloys 713C and Mar-M200 with nominal additions of 0, 0.5, and 1 wt% Si were evaluated for oxidation and corrosion resistance, tensile and stress-rupture properties, microstructure, and phase relations. Results are compared with those of an earlier study of the effects of Si in B-1900. Si had similar effects on all three superalloys. It improves oxidation resistance but the improvement in 713C and Mar-M200 was considerably less than in B-1900. Hot-corrosion resistance is also improved somewhat. Si is, however, detrimental to mechanical properties, in particular, rupture strength and tensile ductility. Si has two obvious microstructural effects. It increases the amount of gamma-prime precipitated in eutectic nodules and promotes a Mo(Ni,Si)2 Laves phase in the alloys containing Mo. These microstructural effects do not appear responsible for the degradation of mechanical properties, however.
New γ' strengthened nickel-base superalloy compositions are described that, when forged and properly heat treated, demonstrate superior resistance to fatigue crack growth accompanied by very good high temperature properties. Parts can be fabricated (e.g., using conventional cast and wrought processing) from these alloys without encountering difficulty in forging.
Specific weight changes of nickel-base superalloy B-1900 and B-1900 + 1% Si specimens were tested at 1273 K. B-1900 was losing weight at an increasing rate due to spalling of oxide scale while B-1900 + 1% Si was still gaining weight at low, nearly constant rate. Similar comparison in weight change was observed for specimens tested at 1373 K.
Forms of the nickel-base superalloy Rene95 produced by three processing methods were evaluated in tensile, low cycle fatigue and fatigue crack propagation tests at 540 and 650 C. Two powder-metallurgy (PM) forms, hot-isostatically-pressed and extruded-and-forged, and a conventionally cast-and-wrought form were all given the same heat treatment. The extruded-and-forged form showed superior fatigue life in low strain range tests though the two PM forms exhibited nearly identical mechanical behavior in all other respects. Further, this life difference could not be explained by significant differences in the types, sizes or shapes of the defects initiating failure. The cast-and-wrought Rene95, however, had lower strength, ductility and fatigue life, but higher fatigue crack propagation resistance because of a larger grain size. It did not exhibit the environmentally-assisted intergranular mode of propagation which occurs in PM Rene95 and other fine-grained superalloys at these test temperatures and frequencies.
Fourteen nickel-base superalloy single crystals containing 0 to 5 wt% chromium (Cr), 0 to 11 wt% cobalt (Co), 6 to 12 wt% molybdenum (Mo), 0 to 4 wt% rhenium (Re), and fixed amounts of aluminum (Al) and tantalum (Ta) were examined to determine the effect of bulk composition on basic microstructural parameters, including gamma' solvus, gamma' volume fraction, volume fraction of topologically close-packed (TCP) phases, phase chemistries, and gamma - gamma'. lattice mismatch. Regression models were developed to describe the influence of bulk alloy composition on the microstructural parameters and were compared to predictions by a commercially available software tool that used computational thermodynamics. Co produced the largest change in gamma' solvus over the wide compositional range used in this study, and Mo produced the largest effect on the gamma lattice parameter and the gamma - gamma' lattice mismatch over its compositional range, although Re had a very potent influence on all microstructural parameters investigated. Changing the Cr, Co, Mo, and Re contents in the bulk alloy had a significant impact on their concentrations in the gamma matrix and, to a smaller extent, in the gamma' phase. The gamma phase chemistries exhibited strong temperature dependencies that were influenced by the gamma and gamma' volume fractions. A computational thermodynamic modeling tool significantly underpredicted gamma' solvus temperatures and grossly overpredicted the amount of TCP phase at 982 C. Furthermore, the predictions by the software tool for the gamma - gamma' lattice mismatch were typically of the wrong sign and magnitude, but predictions could be improved if TCP formation was suspended within the software program. However, the statistical regression models provided excellent estimations of the microstructural parameters based on bulk alloy composition, thereby demonstrating their usefulness.
Formation of sigma phase in nickel base superalloy