Microstructural evolution, defect mitigation, and precipitation behavior in AA6061 via laser powder bed fusion with high-temperature substrate heating

Defects, particularly solidification cracking, remain persistent challenges in the laser powder bed fusion (LPBF) processing of AA6061 aluminum alloy. This study systematically investigates defect mitigation, microstructural evolution, and mechanical properties associated with high-temperature substrate preheating at 500 °C. Comprehensive microstructural analyses, including characterization of defects, grain structures, and precipitation behavior, were performed on samples in both as-built and T6 heat-treated states. Elevated preheating substantially reduced solidification cracking across a wide processing window, while demonstrating decreased crack sensitivity to laser parameters. Columnar cracks along the build direction were observed despite substrate preheating. Lack-of-fusion and keyhole porosity were effectively eliminated, though gas-induced microporosity persisted at higher powers. In-depth characterization of two distinct laser power and speed conditions confirmed the formation of micron-sized, non-coherent Mg 2 Si precipitates under heated substrate conditions, alongside α-AlFeCrMnSi intermetallic phases indicative of in-situ thermal effects during fabrication. Subsequent T6 heat treatment revealed the formation of fine, coherent needle-shaped β″ strengthening precipitates. Despite substantial differences in processing parameters, comparable mechanical properties were measured in the as-built samples (∼52 MPa yield strength, ∼130 MPa tensile strength), primarily due to reduced strain hardening effects and consistent precipitation characteristics. Meanwhile, the T6 heat treatment led to significant improvement in properties, enhancing yield strength by over 400%, aligning closely with the performance of conventional wrought AA6061-T6. These findings underscore that high-temperature substrate preheating offers an effective means to suppress cracks, control precipitation, and enhance mechanical performance in LPBF-processed AA6061.

36 MATERIALS SCIENCE↗

Crack mitigation and wear performance of high-strength steel coatings deposited by high-speed laser cladding

This article investigates the fabrication of defect-free Rockit® 606, a high‑carbon, vanadium- and chromium-enriched precipitation-hardening martensitic steel coating, using high-speed laser cladding (HSLC). Compared to conventional laser cladding, HSLC offers higher deposition efficiency, improved coating quality, minimal thermal distortion, and a reduced heat-affected zone. Various HSLC parameters—including laser power, travel speed, powder feed rate, and overlap distance—were optimized to achieve superior coating properties. Microstructural analysis revealed solidification cracks in coatings deposited on carburized steel, regardless of processing parameters. However, preheating the substrate to 250 °C effectively eliminated cracking by reducing thermal gradients. The coatings exhibited a columnar dendritic microstructure, with coarser dendrites near the substrate and finer dendrites towards the surface. Hardness measurements confirmed that all coatings significantly exceeded the industry-specified threshold of 60 HRC, with preheating having minimal effect on overall hardness distribution. Reciprocating sliding wear tests demonstrated a substantial improvement in wear resistance for the defect-free HSLC coatings compared to baseline carburized steel. These findings underscore the potential of HSLC for producing high-performance, wear-resistant coatings suitable for industrial applications.

36 MATERIALS SCIENCE↗

System and method for large-area pulsed laser melting of metallic powder in a laser powder bed fusion application

The present disclosure relates to systems and methods for performing large area laser powder bed fusion (LBPF) to form a plurality of layers of a 3D part in a layer-by-layer fashion using meltable powder particles. In one implementation the system makes use of a first light source, which may be a diode laser subsystem, for generating a first light pulse of a first duration. The first light is used to preheat a substrate underneath a new layer of powder particles, wherein the substrate is formed from a previously fused quantity of the powder particles. A second light source, which may be a pulse laser, generates a second light pulse subsequent to the first light pulse. The second light pulse has a second duration shorter than the first duration by a factor of at least about 10, and fully melts the new layer of powder particles in addition to the substrate, to achieve a smooth printed layer. The wavelength of the first light pulse also differs from a wavelength of the second light pulse.

Khairallah, Saad A.↗