DOE OSTI2021

Material migration in W and Mo during bubble growth and fuzz formation

Growth of helium (He) induced bubbles and fuzz in tungsten (W) and molybdenum (Mo) is investigated using samples of W films on Mo substrates and Mo films on W substrates exposed to He-containing plasma in the temperature range of 340 to 1075 K, fluence range of 1.0–14 × 10 25 He·m -2 , and incident ion energy of <50 eV. No fuzz (only up to 2 nm diameter bubbles) and no material transport occur in W films at ≤750 K, while precursors-of or fully-developed fuzz and material mixing occur in W and Mo films at ≥800 K. This suggests that fuzz forms in multi-material systems as long as one material meets the conditions for fuzz formation, namely T s / T m ~ 0.27–0.5 where T s and T m are the sample exposure and material melting temperatures, respectively. Larger He bubbles, more material mixing, and further-developed fuzz occur at higher temperature due to increased mobility of He atoms and small He clusters. Accumulation of substrate material at the surface of fuzzy W and Mo thin-film (<80 nm) samples suggests fuzz growth by material transport from the bubble layer in the bulk up to the fiber tip, likely by a two-step process: (i) diffusion of punched dislocation loops in the bulk toward the fuzz base and (ii) diffusion of adatoms along the fuzz base and fiber surface (with effective transport of adatoms upwards due to trapping of adatoms at curved surfaces of fiber tips and/or due to the continuous generation of adatoms at the fuzz base). While the bubble size and fuzz thickness increase with reduced W concentration in Mo thin-film samples at 838 K likely due to an increase in trap mutation and dislocation loop punching in Mo compared to W, the fuzz thickness decreases with reduced W concentration at 1075 K despite an increase in the bubble size likely due to slower diffusion of interstitial loops in Mo.

Physics↗
DOE OSTI2020

Material mixing during fuzz formation in W and Mo

Helium-induced fuzz formation in tungsten (W) and molybdenum (Mo) is investigated for a range of sample exposure temperatures from 838 K–1075 K (He fluence = 3.4 × 10 25 m -2 and ion energy <39 eV). Thin films of Mo deposited on W substrates show mixing of the film and substrate materials in the fuzz after He plasma exposure, including at 838 K (i.e. below the typical temperature range at which fuzz forms in pure W). Finally, the amount of material mixing increases with exposure temperature due to the increase in bubble size, and leads to significant accumulation of the substrate material at the fuzz surface at the highest temperature investigated, further supporting fuzz growth from the fiber tip outwards by material transport up the fibers.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Effects of elastic softening and helium accumulation kinetics on surface morphological evolution of plasma-facing tungsten

Based on a continuous-domain model, capable of accessing the spatiotemporal scales relevant to fuzz formation on the surface of plasma-facing component (PFC) tungsten, we report self-consistent simulation results that elucidate the effects of elastic softening and helium (He) accumulation kinetics on the surface morphological response of PFC tungsten. The model accounts for the softening of the elastic moduli in the near-surface region of PFC tungsten, including both thermal softening at high temperature and softening due to He accumulation upon He implantation. The dependence of the elastic moduli on the He content follows an exponential scaling relation predicted by molecular-dynamics simulations, while the He content in the near-surface region of PFC tungsten evolves according to a first-order saturation kinetics, consistent with experimental and simulation results reported in the literature. We establish that this elastic softening accelerates both nanotendril growth on the PFC surface and the onset of fuzz formation. We also explore the role of the rate of He accumulation to a saturation level in the near-surface region of irradiated tungsten in the onset of fuzz formation. For PFC tungsten surfaces such as W(110) where, under typical irradiation conditions, the characteristic time scale for stress-driven surface diffusion is comparable to the characteristic time scale for He accumulation, we find that accelerating the rate of He accumulation accelerates the growth rate of nanotendrils emanating from the surface. Additionally, we present a systematic parametric study of the PFC surface morphological response to explore its dependence on the He accumulation kinetics that is controlled by the irradiation conditions for low-energy implantation. Finally, we introduce an incubation time for nanotendril growth on the PFC surface, a concept equivalent to that of incubation fluence discussed in the literature, to predict and explain the minimum exposure time required to observe fuzz formation on PFC tungsten surfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Effects of surface vacancy-adatom pair formation on PFC tungsten surface morphological response

Abstract We report a simulation study of the effect of He-irradiation-induced surface vacancy-adatom pair formation on the surface morphological evolution of plasma-facing component (PFC) tungsten and examine a number of factors that impact such evolution. Our analysis is based on self-consistent dynamical simulations according to an atomistically-informed, continuum-scale surface evolution model that has been developed following a hierarchical multiscale modeling strategy and can access the spatiotemporal scales of relevance to fuzz formation. The model accounts for the flux of surface adatoms generated as a result of the surface vacancy-adatom pair formation effect upon He implantation, which contributes to the anisotropic growth of surface nanostructural features due to the different rates of adatom diffusion along and across step edges of islands on the tungsten surface. We have carried out atomic-scale computations of optimal diffusion pathways along and across island step edges on the W(110) surface and calculated Ehrlich–Schwoebel (ES) barriers in adatom diffusion along and across such step edges. This aspect of surface adatom diffusion contributes to anisotropic surface atomic fluxes, terrace and step diffusive currents, and has been incorporated into our PFC surface evolution model, which predicts the formation of preferentially aligned nanoridge stripe patterns on the PFC surface. We establish that these anisotropic diffusive currents accelerate nanotendril growth on the PFC surface and the onset of surface nanostructure pattern formation. We also explore systematically the dependence of the PFC surface morphological response on the surface temperature and He ion incident flux, characterize in detail the resulting surface topographies and growth kinetics, and compare the predicted surface morphologies with experimental observations. Our simulation predictions for the emerging surface nanostructure patterns under certain plasma exposure conditions are consistent with experimental findings in the literature.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Retention and surface morphology evaluation of fine-grain dispersion-strengthened tungsten for plasma-facing component applications

This study exposed novel fine-grain dispersion-strengthened tungsten (W) to high fluence, low energy deuterium (D) and helium (He) plasmas to evaluate how material microstructure and composition affect hydrogen retention and surface morphology. Tested materials included fine-grain dispersion-strengthened tungsten (DSW) with 3 wt% zirconium carbide (ZrC) dispersoids, fine-grain dense W without any dispersoids (FGW), and coarse-grained polycrystalline ‘ITER-grade’ W. Samples were exposed to D 2 + and He + plasmas at fusion-relevant fluences (∼10 25 m -2 ) and ion energies (75 eV) over a range of temperatures (200 °C, 300 °C, 450 °C for D, 850 °C for He). Helium ion microscopy was performed on the exposed samples to evaluate surface morphology changes and material integrity. After D plasma exposure, the ZrC dispersoids showed near-surface degradation at exposure temperatures above 300 °C, but no detrimental morphology changes were observed for the adjacent W grains. After He plasma-exposure, nano-structured fuzz formation was observed in the tungsten matrix of all samples. The ZrC dispersoids maintained their integrity despite the surrounding fuzz growth, with clear delineation between the W fuzz and dispersoid regions. Thermal desorption spectroscopy showed that ZrC DSW consistently retained more D than the FGW by about a factor of 2 across all temperatures. At 200 °C and 300 °C, the ITER-W displayed lower D retention than both the DSW and FGW, however at 450 °C ITER-W showed the highest retention, about 50% more than DSW. He retention was comparable across all samples, with the highest retention observed in the fine-grain W, only 26% higher than in ITER-W. These insights on retention behavior will inform further optimization of these novel fine-grained tungsten materials with and without dispersoid additives.

Dispersion-strengthened tungsten↗
DOE OSTI2023

The dependence of tungsten fuzz layer thickness and porosity on tungsten deposition rate and helium ion fluence

Abstract Fuzz formation on a heated tungsten surface in the presence of a helium-containing plasma and tungsten deposition source was investigated. Tungsten samples were exposed at 1123 K to pure helium plasma with ion incident energy of 76 eV, W/He ion flux ratio of ∼ 0.4 × 10 − 4 , and varied helium ion fluence from 0.18 to 3.4 × 10 26 m −2 . Fuzz thickness was measured by cross-sectional scanning electron microscopy to increase from 0.22 to 15 µ m with increasing helium ion fluence. No indication of saturation in fuzz thickness at high fluence was observed, in contrast to fuzz produced on a tungsten surface without tungsten deposition. Additional tungsten samples were exposed at 1123 K to pure helium plasma with ion incident energy of 76 eV, helium ion fluence of ∼ 3.4 × 10 26 m −2 , and varied W/He ion flux ratio from 0.26 to 3.0 × 10 − 4 . Fuzz thickness increased from 7.5 to 120 µ m with increasing W/He ion ratio. A final sample exposed at 1123 K to a mixed helium-deuterium plasma with ion incident energy of 76 eV, helium ion fluence of 0.18 × 10 26 m −2 , and W/He ion flux ratio of 2.2 × 10 − 4 developed nearly identical fuzz structures to that developed in a pure He plasma. As a function of deposited tungsten fluence, all results were found to trace out a single layer-growth curve given by a power law relation, indicating that fuzz thickness is independent of the W/He ion flux ratio in the range investigated and independent of any deuterium present in the plasma. As a result, for tungsten plasma facing walls in magnetic fusion devices at 1000–2000 K with 10 −4 W/He ion flux ratio, fuzz with thicknesses greater than hundreds of microns may form in as little as 10 4 s (in the absence of ELM-induced erosion or annealing), and may more significantly affect its thermophysical properties than fuzz generated without a tungsten deposition source.

Physics↗
DOE OSTI2020

In-Situ Helium Implantation and TEM Investigation of Radiation Tolerance to Helium Bubble Damage in Equiaxed Nanocrystalline Tungsten and Ultrafine Tungsten-TiC Alloy

The use of ultrafine and nanocrystalline materials is a proposed pathway to mitigate irradiation damage in nuclear fusion components. Here, we examine the radiation tolerance of helium bubble formation in 85 nm (average grain size) nanocrystalline-equiaxed-grained tungsten and an ultrafine tungsten-TiC alloy under extreme low energy helium implantation at 1223 K via in-situ transmission electron microscope (TEM). Helium bubble damage evolution in terms of number density, size, and total volume contribution to grain matrices has been determined as a function of He+ implantation fluence. The outputs were compared to previously published results on severe plastically deformed (SPD) tungsten implanted under the same conditions. Large helium bubbles were formed on the grain boundaries and helium bubble damage evolution profiles are shown to differ among the different materials with less overall damage in the nanocrystalline tungsten. Compared to previous works, the results in this work indicate that the nanocrystalline tungsten should possess a fuzz formation threshold more than one order of magnitude higher than coarse-grained tungsten.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Synergistic effects of W–Ta alloys exposed to various ELM-like fusion events

Abstract Recently tungsten alloys have shown capabilities in suppressing morphological changes when exposed to harsh fusion conditions. Morphological changes due to He + and D + ions at high temperatures (1000–2000 K) can lead to easier erosion and sputtering of tungten (W) particles towards quenching the fusion plasma. This study investigated W–3Ta alloy as potential plasma facing materials (PFMs) exposed to different edge-localized mode (ELM)-like energies and ion loadings. Performance of W–3Ta has been tested as a function of ELM-like energies (0.6–1.5 GW m −2 ) and varying He + and D + ion concentrations (100% He + , 50% He + :50% D + ,10% He + :90% D + (similar ELM-like reactor condition), and 100% D + ions). Early-stage fuzz formation and surface pores were observed during 100% He + ion irradiation and mixed ion loadings but not observed during 100% D + ion loadings. Pores decreased in quantity and increased in size with increasing transient heat loading. Grain boundaries acted as trapping sites of helium and deuterium atoms during dual beam ion irradiations, as observed through increased pore size along the grain boundary. Qualitative erosion estimates were measured using witness plates. Increased erosion was observed with increasing D + ion concentration, which is attributed to D supersaturation in the near surface region affecting thermal and mechanical properties. More erosion was observed for W–3Ta samples compared to pure W, evident through large (>10 µ m) cracks on the surface, and an increase in W metal x-ray photoelectron spectroscopy peaks under similar loading conditions. The slight enhancement in erosion is attributed to the slightly decreased thermal properties, ∼10% thermal diffusivity drop, of W–3Ta at high temperatures. The damage threshold was impacted by ion loading, where distinct cracking was observed for 100% He + at a lower heat loading. This matrix study using reactor-like loading supports the need for extensive studies on future W alloy PFMs before selecting one as an alternative.

Physics↗
DOE OSTI2021

Hole formation effect on surface morphological response of plasma-facing tungsten

We report simulation results on the effect of helium (He) bubble bursting-mediated surface hole formation on the surface morphological response of tungsten plasma-facing components (PFCs) in nuclear fusion devices. Our analysis is based on an atomistically informed, continuum-scale model, which is capable of accessing the spatiotemporal scales relevant to the fuzz nanostructure formation process on the surface of PFC tungsten. Our simulations account, in an empirical fashion, for two types of subsurface bubble dynamical phenomena in the nanobubble region of PFC tungsten during He plasma irradiation, involving bubble bursting and surface crater formation. We demonstrate that the hole formation effect on the PFC tungsten surface accelerates the growth rate of nanotendrils and the onset of fuzz formation. As a result, the predicted incubation time for surface nanotendril growth is shortened, in agreement with experimental data of incubation fluence at comparable plasma exposure conditions. We also explore systematically the dependence of the PFC surface morphological response on the areal density of holes introduced at regular time intervals onto the He-implanted tungsten surface, a parameter in our analysis that serves as a proxy for the rate of He bubble bursting. More importantly, our simulations capture fine surface features in the PFC tungsten surface morphology and predict that the average spacing between nanotendrils is on the order of 100 nm, consistent with the experimental findings.

Chen, Chao-Shou (ORCID:0000000307910042)↗
DOE OSTI2023

Helium bubble size effects on the surface morphological response of plasma-facing tungsten

Abstract We report a simulation study on the effects of helium (He) bubble size on the morphological evolution and pattern formation on the surface of tungsten used as a plasma-facing component (PFC) in nuclear fusion devices. We have carried out a systematic investigation based on self-consistent dynamical simulations of surface morphological evolution according to an atomistically-informed, 3D continuum-scale model that captures well the relevant length and time scales of surface nanostructure formation in PFC tungsten. The model accounts for PFC surface diffusion, driven by the biaxial compressive stress originating from the over-pressurized He bubbles in the near-surface region of PFC tungsten as a result of He plasma exposure, combined with the formation of self-interstitial atoms in tungsten that diffuse toward the PFC surface and the flux of surface adatoms generated as a result of surface vacancy-adatom pair formation upon He implantation; this transport of surface adatoms contributes to the anisotropic growth of surface nanostructural features due to the different rates of adatom diffusion along and across step edges of islands on the tungsten surface. Our detailed analysis reveals that varying the average He bubble size plays an important role in the PFC surface growth kinetics as well as the resulting surface topography. Specifically, we find that an increase in the He bubble size leads to a deceleration in the growth rate of the tungsten nanotendrils that emanate from the PFC surface. We also find that the separation distance between the resulting surface features increases with increasing He bubble size, as well as over time. This coarsening effect is a thermally activated process resulting in an accurate description of the temperature dependence of the average surface feature separation by an Arrhenius relation.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Enhanced resistance to helium irradiations through unusual interaction between high-entropy-alloy and helium

Finding high performance plasma-facing materials (PFMs) is one of the most important and challenging tasks for realizing the commercial application of fusion reactors. Herein, we found the CrMoTaWV high entropy alloy (HEA) is highly resistant to low-energy and high-flux He plasma exposure. The nanochannel HEA film has 20 times higher initial fluence for the formation of fuzz and a remarkable 8.9 times slower fuzz growth rate than those of W. Combining the in-situ TEM observation and the Molecular dynamics (MD) simulation of the He bubble growth process, a new mechanism for the enhanced radiation resistance in HEA with the unusual interaction between HEA and He is found, where, differing from traditional metal, bubble growth in HEA leads to non-directional emission of interstitial atoms while HEA greatly suppress the growth of He bubbles. Additionally, the special nanochannel structure further rise the radiation resistance through releasing He out of the HEA film and reducing the He concentration. This new nanochannel refractory HEA material presents a promising choice as the PFMs with excellent performance and a much longer serving lifetime for future commercial fusion reactors.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Interfaces enhanced plasma irradiation resistance in CrMoTaWV/W multilayer films through blocking He diffusion

The performance of plasma-facing materials (PFMs) is one of the key factors that significantly impact the stability of operation in fusion reactors. Herein, a new CrMoTaWV/W (high entropy alloy (HEA)/W) multilayer structure is designed as PFM to investigate its resistance to He plasma irradiation. It was observed that the introduction of the interfaces effectively absorbed plenty of He atoms, preventing them from diffusing into the material and delaying the formation of fuzz incubation zone, therefore, enhancing the resistance to plasma irradiation. The thickness transformed to fuzz in the HEA/W multilayer films was observed to be about two-thirds of those in the CrMoTaWV (HEA) film. Additionally, the fuzz growth rates in HEA/W multilayer films are lower than the average growth rate of bulk W and HEA films combined. These findings highlight a promising new avenue for the exploration of high-performance PFMs.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗
DOE OSTI2021

Stability and mobility of tungsten clusters on tungsten (110) surface: Ab initio and atomistic simulations

Quantifying the surface transport properties of tungsten (W) is of prime importance to understand the formation of nano-fuzz in fusion plasma-facing conditions. The stability and mobility of W adatom clusters (W n , n = 2-9) on the W(110) surface has been investigated by computer simulations, including ab initio calculations using density functional theory (DFT) and molecular statics (MS) simulations with multiple W interatomic potentials. The DFT results demonstrate that the sequential binding energy generally increases with number of W adatoms, except for the 5 th and 7 th W adatoms. The most common elemental migration steps of W n (n>2) clusters are observed to consist of monomer and dimer hops, while larger W n clusters can also diffuse by dissociation and recombination of smaller clusters. The threshold migration energy of W 9 is the highest, then followed by W 8 , W 4 , and W 6 , while W 3 , W 5 , and W 7 have similar migration energies. Compared to DFT, each interatomic potential evaluated overestimates the binding energies of W n clusters. Additionally, the embedded-atom potential developed by Juslin and Wirth adequately predicts the threshold migration energy of W n (n>2) clusters, although it predicts different underlying migration mechanisms. The results show that interaction mechanism between W adatoms controls the stability and mobility of W n clusters on the W(110) surface.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Helium plasma operations on ASDEX Upgrade and JET in support of the non-nuclear phases of ITER

For its initial operational phase, ITER has until recently considered using non-nuclear hydrogen (H) or helium (He) plasmas to keep nuclear activation at low levels. To this end, the Tokamak Exploitation Task Force of the EUROfusion Consortium carried out dedicated experimental campaigns in He on the ASDEX Upgrade (AUG) and JET tokamaks in 2022, with particular emphasis put on the ELMy H-mode operation and plasma-wall interaction processes as well as comparison to H or deuterium (D) plasmas. Both in pure He and mixed He + H plasmas, H-mode operation could be reached but more effort was needed to obtain a stable plasma scenario than in H or D. Even if the power threshold for the LH transition was lower in He, entering the type-I ELMy regime appeared to require equally much or even more heating power than in H. Suppression of ELMs by resonant magnetic perturbations was studied on AUG but was only possible in plasmas with a He content below 19%; the reason for this unexpected behaviour remains still unclear and various theoretical approaches are being pursued to properly understand the physics behind ELM suppression. The erosion rates of tungsten (W) plasma-facing components were an order of magnitude larger than what has been reported in hydrogenic plasmas, which can be attributed to the prominent role of He 2+ ions in the plasma. For the first time, the formation of nanoscale structures (W fuzz) was unambiguously demonstrated in H-mode He plasmas on AUG. However, no direct evidence of fuzz creation on JET was obtained despite the main conditions for its occurrence being met. The reason could be a delicate balance between W erosion by ELMs, competition between the growth and annealing of the fuzz, and coverage of the surface with co-deposits.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗
DOE OSTI2024

A comprehensive guide to CAN IDS data and introduction of the ROAD dataset

Although ubiquitous in modern vehicles, Controller Area Networks (CANs) lack basic security properties and are easily exploitable. A rapidly growing field of CAN security research has emerged that seeks to detect intrusions or anomalies on CANs. Producing vehicular CAN data with a variety of intrusions is a difficult task for most researchers as it requires expensive assets and deep expertise. To illuminate this task, we introduce the first comprehensive guide to the existing open CAN intrusion detection system (IDS) datasets. We categorize attacks on CANs including fabrication (adding frames, e.g., flooding or targeting and ID), suspension (removing an ID’s frames), and masquerade attacks (spoofed frames sent in lieu of suspended ones). We provide a quality analysis of each dataset; an enumeration of each datasets’ attacks, benefits, and drawbacks; categorization as real vs. simulated CAN data and real vs. simulated attacks; whether the data is raw CAN data or signal-translated; number of vehicles/CANs; quantity in terms of time; and finally a suggested use case of each dataset. State-of-the-art public CAN IDS datasets are limited to real fabrication (simple message injection) attacks and simulated attacks often in synthetic data, lacking fidelity. In general, the physical effects of attacks on the vehicle are not verified in the available datasets. Only one dataset provides signal-translated data but is missing a corresponding “raw” binary version. This issue pigeon-holes CAN IDS research into testing on limited and often inappropriate data (usually with attacks that are too easily detectable to truly test the method). The scarcity of appropriate data has stymied comparability and reproducibility of results for researchers. As our primary contribution, we present the Real ORNL Automotive Dynamometer (ROAD) CAN IDS dataset, consisting of over 3.5 hours of one vehicle’s CAN data. ROAD contains ambient data recorded during a diverse set of activities, and attacks of increasing stealth with multiple variants and instances of real (i.e. non-simulated) fuzzing, fabrication, unique advanced attacks, and simulated masquerade attacks. To facilitate a benchmark for CAN IDS methods that require signal-translated inputs, we also provide the signal time series format for many of the CAN captures. Our contributions aim to facilitate appropriate benchmarking and needed comparability in the CAN IDS research field.

97 MATHEMATICS AND COMPUTING↗
DOE OSTI2022

Intense cyclic heating effects on thermo-fracture and thermal shock of solid tungsten and open-cell tungsten foam

Here we investigate here the effects of transient (cyclic) arc-jet plasma and laser heating on fracture behavior of W-foam and solid tungsten. The two key parameters that control the foam thermomechanical response are its density and mean cell size expressed in Pores Per Inch (PPI). Tungsten foam samples were fabricated with Chemical Vapor Deposition (CVD) with variety of PPI and relative density. These were tested under two types of qualitatively different conditions: (1) high-enthalpy arc-jet, and (2) high-power cyclic laser heating. None of the foam samples showed macroscopic through-thickness cracks. However, distributed micro-cracks were observed on ligaments and their triple junctions. Under the same loading conditions, W-foam and solid tungsten showed similar crack network pattern and characteristic length-scale. However, Crack Opening Displacement (COD) was twice as large in solid W as compared to W-foam. Foam samples that have been previously exposed to a low-pressure helium plasma showed significant changes in their surface forming nano-texture fuzz which was removed by subsequent testing in the arc-jet. Extensive fracture and re-crystallization were observed in the thin solid W disk that was fully-constrained from expansion. Thicker and fully-constrained solid W disks did not display recrystallization, grain growth, and extensive cracking. However, thicker disks that were free to expand showed some recrystallization and extensive through-thickness cracks due to less effective cooling and thus higher temperatures. Laser beam testing showed no visible damage formation at 0.19 GW/m 2 and 0.38 GW/m 2 for both low-density (23%) and high-density (43%) foams at low pulses (100-1000). Micro-cracks were observed after 10,000 pulses at 0.19 GW/m 2 in both foams, and in low-density foam after 100,000 at 0.38 GW/m 2 . The nature of thermomechanical damage in W-foam exposed to extreme power (GW/m 2 ) short-duration laser pulses was found to be qualitatively similar to that of high power (MW/m 2 ) long-duration arc-jet.

36 MATERIALS SCIENCE↗
DOE OSTI2020

High Flux Helium Irradiation of Dispersion-Strengthened Tungsten Alloys and Effects of Heavy Metal Impurity Layer Deposition

Tungsten has been chosen as the plasma-facing material (PFM) for the divertor region in ITER and also a candidate PFM for future plasma-burning nuclear fusion reactors. During fusion device operation, PFMs will be exposed to low-energy He irradiation at high temperatures, resulting in sub-surface bubbles and surface morphology changes such as pores and fuzz. Carbide dispersion-strengthened W materials may enhance the ductility of W, but their behavior under high flux He irradiation remains unclear. In this work, the response of dispersion-strengthened tungsten materials to high flux, low energy He irradiation at high temperature is examined. Tungsten alloyed with 1, 5, or 10 wt. % tantalum carbide or titanium carbide exposed to these conditions result in surface pores, coral-like feature growth and sub-surface helium bubbles. Reactor-relevant helium irradiation (5 x 10 26 m -2 fluence) combined with high powered laser pulses to simulate off-normal reactor events does not significantly alter the surface morphology, as the surface nanostructures appear stable and cracks are only observed on a localized region of one sample. However, specimens show the development of an impurity layer on the surface, likely impurity deposition from the sample holder during irradiation, resulting in a mixed material layer on the surface. Helium bubbles exist in this impurity layer, and obscure conclusions about helium interactions with the carbide dispersoids. Nonetheless, it is clear that the dispersoid microstructure limits He bubble formation and subsequent surface nanostructuring, attributed to the dispersoid composition.

36 MATERIALS SCIENCE↗