Fatigue life prediction of powder bed fused–laser beam AlSi10Mg: Incorporating critical defects via crystal plasticity modelling

The current study provides a microstructurally-based computational framework to predict the fatigue life of additive manufactured (AM), i.e., powder bed fused–laser beam (PBF-LB), AlSi10Mg specimens using the crystal plasticity finite element method (CPFEM). The fractography analysis, electron backscatter diffraction (EBSD), uniaxial and cyclic responses, and fatigue life of specimens were used to inform the computational framework. CPFE simulation was used to compute fatigue indicator parameters (FIPs) as fatigue driving forces. A new fatigue criterion is introduced based on FIPs, which was calibrated using experimental fatigue data. The proposed fatigue measure was evaluated versus the specimens with critical defects of various sizes and locations subjected to different stress amplitudes. The results show that the developed framework can capture the fatigue life of samples with different critical defect locations and sizes along with different stress amplitudes for both high-cycle fatigue (HCF) and very high-cycle fatigue (VHCF) regimes.

Additive manufacturing↗
DOE OSTI2022

Stress-controlled fatigue of HfNbTaTiZr high-entropy alloy and associated deformation and fracture mechanisms

The stress-controlled fatigue tests are carried out at a stress ratio of 0.1 and a frequency of 10 Hz, and span both low-cycle and high-cycle regimes by varying the applied stress amplitudes. The high-cycle fatigue regime gives a fatigue strength of 497 MPa and a fatigue ratio of 0.44. At equivalent conditions, the alloy's fatigue strength is greater than all other high-entropy alloys (HEAs) with reported high-cycle fatigue data, dilute body-centered cubic alloys, and many structural alloys such as steels, titanium alloys, and aluminum alloys. Through in-depth analyses of crack-propagation trajectories, fracture-surface morphologies and deformation plasticity by means of various microstructural analysis techniques and theoretical frameworks, the alloy's remarkable fatigue resistance is attributed to delayed crack initiation in the high-cycle regime, which is achieved by retarding the formation of localized persistent slip bands, and its good resistance to crack propagation in the low-cycle regime, which is accomplished by intrinsic toughening backed up by extrinsic toughening. Additionally, the stochastic nature of the fatigue data is neatly captured with a 2-parameter Weibull model.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Additively manufacturing high-temperature aluminum alloy for automotive engine pistons

The purpose of the project was to evaluate DuAlumin-3D, an ORNL designed Al alloy, for additive manufacturing of high-performance automotive components. The project consisted of additively manufacturing a cylindrical block of representative material which was then heat treated before machining into test coupons. Testing included tensile tests as a function of temperature, high-cycle fatigue testing as a function of temperature, density and elastic modulus measurements, and thermophysical property measurements. Fractography was also performed on failed high-cycle fatigue specimens. The results were compared against benchmark AM Al alloys and current high-performance conventionally manufactured alloys. Overall, the DuAlumin-3D material outperformed the incumbent materials in mechanical properties, especially at elevated temperatures, while maintaining broadly similar thermophysical properties. The results of this study support further maturation of the material for additive manufacturing of high-performance automotive components.

36 MATERIALS SCIENCE↗
DOE OSTI2022

A cycle-jump acceleration method for the crystal plasticity simulation of high cycle fatigue of the metallic microstructure

For metallic materials, high-cycle fatigue life is sensitive to underlying microstructure features including secondary phases, textures, grains morphology, etc. The traditional, data-based safe-life approaches for modeling fatigue don’t explicitly consider the microstructure and can’t guide study in microstructure modification for improved fatigue property. Crystal plasticity-based simulation provides increased model fidelity at the expense of immense computation time, making it inapplicable for high cycle fatigue. In this work, an acceleration method based on cycle-jump approach (Lesne and Savalle, 1989) was developed for microstructure-based high-cycle FE simulation using crystal plasticity constitutive-model. We report this method demonstrated high efficiency in benchmark tests of various conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Implications of Fatigue-Crack Healing in Nanocrystalline Metals [Slides]

Under high-cycle fatigue conditions, a fatigue crack in nanocrystalline Pt was observed to undergo healing. The healing appears to occur by cold welding, facilitated by grain boundary migration, and also by local closure stresses. The healing may help explain several observations: role of air (or vacuum) on fatigue life, impeded subsurface fatigue cracking, apparent flaw healing in sub-critical cycling of ceramics, the existence of a fatigue threshold, and the role of vacuum on the fatigue threshold.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Enhancement in Mechanical Properties of Bulk Nanocrystalline Aluminum by Grain Boundary Strengthening Mechanism

In the present work, commercially pure aluminum (Al) powders were milled at cryogenic temperatures (a) without magnesium (Mg) and (b) with 5 wt.% Mg powders for different durations. The cryomilled powders were analyzed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and x-ray diffraction (XRD) to determine the changes in particle morphology, elemental composition, and crystallite size. The results showed a reduction in crystallite size with the increase in cryomilling duration. Thereafter, the spark plasma sintering (SPS) process was carried out to manufacture bulk samples. The mechanical properties of the bulk SPS samples were assessed by conducting microhardness, tensile, and fatigue tests. The Vickers microhardness tests showed improved hardness for the Al-Mg bulk samples as compared to pure Al. The Al-Mg samples also showed an increase in tensile strength with increasing cryomilling time. Fatigue test results showed an improvement in Al-Mg components' high-cycle fatigue response. Furthermore, the mechanism for the enhancement in mechanical properties as a result of crystallite size reduction and grain boundary strengthening by the addition of Mg dopant is also discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Physics-based Multiscale Additively Manufactured Superalloy Design for Optimized High Cycle Fatigue Life (Final Report)

The objectives of this project are to: (i) Gain fundamental understandings towards the microscopic damage mechanisms, as impacted by pertinent materials properties (e.g. stacking fault energy (SFE) and microstructure (e.g., grain size), leading to high-cycle fatigue (HCF) damage to AM Ni-based superalloy parts; (ii) Provide scientific insight into the effect of testing frequency on damage mechanisms and fatigue life of AM Ni-based superalloy parts under HCF regime, thereby establishing an appropriate correlation between accelerated testing and materials’ true service life; (iii) Devise an accurate, experimentally validated multiscale model across atomic, micro- and meso-scales, to predict the cyclic stress-strain responses and fatigue damage accumulation for AM Ni-based superalloys under various loading frequencies.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Surface smoothing for laser powder-bed Ti-6Al-4V by a transient liquid phase

Surface roughness is the primary driver of fatigue for additively manufactured metals. To address surface roughness, this work introduces a new method to smooth features beyond line-of-sight without material removal. The method applies a coating that triggers local surface remelting by activating a eutectic reaction during heat treatment. The associated liquid phase then wets and isothermally solidifies into a smoother surface. For Ti-6Al-4V fabricated with laser powder bed fusion, samples with and without TLP smoothing (using a Cu coating) were characterized with a suite of techniques, including mechanical testing, electron backscatter diffraction, synchrotron X-ray tomography, and fractography. TLP smoothing reduced surface roughness by 80% and amplified compressive residual stress at the surface by about 50%. With statistically equivalent virtual microstructures, crystal plasticity scrutinized the roles of phases, porosity, and surface roughness. Although the tensile strain-to-failure was reduced to 1% strain, the TLP smoothing process increased high-cycle fatigue strength by about 20% compared to control samples, pointing to future opportunities to optimize the new process through various coating compositions and heat treatment schedules. Overall, this work establishes a new paradigm for treating surfaces of materials for smoothness and compressive residual stress.

Additive manufacturing↗
DOE OSTI2025

Micropolar deep material network

This study extends the Deep Material Network (DMN), a physics-informed machine learning framework, to predict the homogenized mechanical response of composite materials with micropolar (Cosserat-type) constitutive behavior. This extension incorporates microstructure-dependent size effects, enabling accurate, efficient, and size-aware predictions for composites with complex internal architectures. While traditional, direct numerical simulation micropolar models effectively capture size effects by introducing extra local degrees of freedom, they bring significant computational challenges, particularly for multiscale analyses relevant to engineering applications. The micropolar DMN developed in this paper achieves high accuracy while significantly reducing computation time compared to micropolar direct numerical simulations. This advancement enables multiscale analyses and parameter studies that were previously impractical, such as high-cycle fatigue simulations and comprehensive investigations of internal length scale effects notably in size-dependent plastic response and the optimization of lattice structures. By uniting microstructure-sensitive modeling, physics-driven learning, and scalable surrogate modeling, the micropolar DMN paves the way for accelerated material design, large-scale parametric studies, and the reliable incorporation of size-dependent effects across a wide range of engineering applications, including optimization and next-generation composite design.

36 MATERIALS SCIENCE↗
DOE OSTI2023

The Physical and Engineering Limits of Coupled In situ TEM Experiments

Almost all future energy systems (advanced nuclear reactors, fusion energy system, concentrating solar-thermal power (CSP), and wind technologies) are limited by degradation of key material systems exposed to multiple environmental stressors. The degradation during exposure to high temperatures, radiation, mechanical loading, and chemical attack is often dictated by mechanisms active at the microstructural level. The nature of these mechanisms and the associated variations between sequential and concurrent interplay can be explored if the transmission electron microscope (TEM) is utilized as a toolbox for exploration [1]. One such tool developed at Sandia National Laboratories to couple several of these environments is the In situ Ion Irradiation TEM (I3TEM) [2]. Several studies over the last decade utilizing this tool have shown that the scientific intuition developed over decades of sequential experiments is not always a good indicator of concurrent mechanisms or failure routes. This presentation will highlight the recent and planned additions into the I3TEM facility of a Waviks gas injection system and Raman system, respectively, as can be seen in Fig. 1, permitting environmental degradation from gas species leaked into the pole piece region during quantitative mechanical loading (indentation, monotonic loading, high temperature creep, irradiation induced creep, and high-cycle fatigue); multi-beam ion irradiation (energies ranging from 1 keV to 48 MeV and species from H to Au); laser exposure (20 W and 1064 nm), or various combinations thereof that are already possible [3]. This addition permits the facility to explore both sequential or concurrently the four axes of stressors: thermal, mechanical, radiation, and chemical. This information can be directly coupled to modeling, expediting the refinement and validation of both atomistic and mesoscale models.

degradation↗
DOE OSTI2024

High Strength Aluminum Additive Manufacturing

High-strength aluminum alloys for elevated temperature applications are desirable to replace heavier and more expensive titanium alloys. However, most aluminum alloys lose a large fraction of their strength at temperatures above approximately 200°C. ORNL has designed DuAlumin-3D, an alloy with nominal composition Al-9Ce-4Ni-0.5Mn-1Zr (wt.%), which utilizes the high cooling rates in additive manufacturing (AM) to achieve a refined microstructure, and thermally stable mechanical properties. DuAlumin-3D was fabricated by laser powder bed fusion and tested for its tensile mechanical properties across a range of temperature, and for its room temperature high-cycle fatigue resistance. The alloy was tested in both the as-printed and heat treated conditions, and both parallel and perpendicular to the AM build direction. The alloy was found to have anisotropic mechanical behavior in the as-printed state, but the anisotropy significantly decreased (both for tensile and fatigue properties) following heat treatment. The tensile properties significantly out-performed benchmark wrought 2219-T61 across a wide temperature range. The room temperature fatigue performance was approximately similar to 2219-T61.

36 MATERIALS SCIENCE↗
DOE OSTI2024

High-Power Targetry R&D for Next-Generation Accelerator Target Facilities

Beam-intercepting devices such as beam windows and particle-production targets are critical components of accelerator target facilities for High Energy Physics (HEP) experiments. The high-power, pulsed structure of the particle beams used for these experiments leads to thermal shock and high-cycle fatigue in addition to radiation damage resulting from the accumulated particle fluence. This can lead to degradation of the target system s mechanical and thermal properties; considerably reducing their lifetimes and presenting substantial challenges to reliable operation of multi-MW class facilities. Recently several major accelerator facilities have been forced to operate at reduced power levels due to target survivability concerns. Furthermore, at Fermilab it is planned to increase the neutrino production beam power up to 2.4 MW in coming years. Therefore, timely R&D on the irradiated behavior of target system materials is critical to efficient operation of accelerator facilities and full utilization of recent accelerator power upgrades for HEP research. This talk will begin with an overview of high-power targetry, and the significant challenges presented by beam power increases expected for future HEP experiments. We will then cover several past materials irradiation studies that have been completed by the High-Power Targetry R&D group at Fermilab and its collaborators on common accelerator and target materials such as graphite, beryllium, titanium, and tungsten. Finally, we will conclude with a discussion of two novel materials investigations under way within the group; high-entropy alloys for beam window applications, and electrospun nanofibers to serve as particle production targets.

43 PARTICLE ACCELERATORS↗