Biosynthesized Thermoplastic/Regolith Composites for Closed-Loop In-Space Manufacturing

In-Space Manufacturing (ISM) is vital to supporting a sustained human presence on the Moon or Mars. With payload launch prices ranging from $4,000 to more than $1 million per kg, reducing payload mass is of critical interest. Using in-situ resources for ISM is particularly attractive as it allows for a system of Earth-independent manufacturing for the Lunar surface, reducing the initial payload mass that is required for current ISM systems that rely on terrestrially synthesized materials. This talk presents new composite materials made from Lunar and Martian regolith and Poly(3-hydroxybutyrate) (PHB), a thermoplastic that offers the ability to be biosynthesized in space using various in-situ resources like organic waste or atmospheric CO2 as feedstock. The addition of regolith provides a route to creating materials with a diverse set of properties which will be discussed. The development of these materials represents the first step in creating a system of closed-loop ISM, which is critical to establishing a lasting human presence in space.

In situ resource utilization↗

NASA NTRSDate not supplied

Polymer/Regolith Composites for In-Space Manufacturing on the Moon and Mars

In-Space Manufacturing (ISM) is vital to supporting a sustained human presence on the Moon or Mars. With payload launch prices ranging from $4,000 to more than $1 million per kg, reducing payload mass is of critical interest. Using in-situ resources for ISM is particularly attractive as it allows for a system of Earth-independent manufacturing for the Lunar surface, reducing the initial payload mass that is required for current ISM systems that rely on terrestrially synthesized materials. This talk presents new composite materials made from Lunar and Martian regolith and Poly(3-hydroxybutyrate) (PHB), a thermoplastic that offers the ability to be biosynthesized in space using various in-situ resources like organic waste or atmospheric CO2 as feedstock. The addition of regolith provides a route to creating materials with a diverse set of properties which will be discussed. The development of these materials represents the first step in creating a system of closed-loop ISM, which is critical to establishing a lasting human presence in space.

In-situ resource utilization↗

NASA NTRS2025

Erosion Behavior of Ti-hBN Multifunctional Coatings in A Custom-Made Planetary Test Rig at Extreme Lunar Temperatures

Spacecraft landings and takeoffs on the lunar surface, along with extreme temperature variations between day and night (-196 to 150° C), cause high-velocity dust impacts and erosion, resulting in the premature failure of structures. Ti/2 vol% hBN coatings were deposited using atmospheric (APS) and vacuum plasma spray (VPS) using cryo-milled powder feedstock to protect the structural components. The erosion performance of coatings at extreme lunar temperature regimes (-150 to 150° C) was evaluated in a custom-made planetary erosion test rig (PETR) at low (50 mph) and high impact velocities (250 mph). The mass loss of VPS coatings was reduced by 50% compared to the APS coatings and 40% compared to the Ti6Al4V substrate. The cryogenic temperature induces brittleness in the material, rendering it susceptible to extreme conditions of material loss. The particle impact-deformation behavior was captured using a high-speed camera to study the erosion mechanism. This analysis revealed chipping in substrates and brittle APS coatings, while particles rebounding and embedding were observed in VPS coatings. Energy calculations, aided by particle trajectory tracking from the high-speed camera, have conclusively shown that VPS coatings absorb 5–10% more energy than APS coatings during erosion tests. A modified erosion index was developed incorporating the fracture toughness and temperatures. New erosion models for brittle and ductile target materials are proposed for developing erosion-resistant material systems.

Abhijith Kunneparambil Sukumaran↗

NASA NTRS2026

A Dispersion-Strengthened Low-Density Niobium Alloy and Its Elevated Temperature Mechanical Performance

In response to the elevated-temperature and weight-reduction demands of modern aerospace applications, a novel oxide-dispersion-strengthened low-density niobium alloy (LDNb-ODS) was fabricated using laser powder bed fusion (L-PBF). To overcome powder procurement barriers, L-PBF feedstock was produced by blending commercial Nb521, Ti64, and Cr powder with Y2O3 nanoparticles via resonant acoustic mixing. Following L-PBF and a 1400°C vacuum heat treatment, the alloy achieved a density of 6.73 g/cc and a fine mean grain size of 4.62 µm stabilized by uniform ~30 nm yttria dispersoids. Microstructural analysis revealed a chemically inhomogeneous build with lack-of-fusion defects and a titanium (Ti) shift from a nominal 31.5 wt% in the starting powder blend to 24.8 wt% in the printed part due to preferential Ti loss during printing. Elevated-temperature tensile testing demonstrated that LDNb-ODS maintained a superior specific yield strength of 60-85 MPa/(g/cc) up to 800°C, outperforming nickel-based alloys Ni625, Ni230, and GRX-810. Between 870°C and 950°C, its specific strength surpassed both Ni718 and Ni625. In rapid stress-rupture testing at 1093°C and 20.7 MPa, uncoated LDNb-ODS survived 21.4 hours (a tenfold increase over legacy C-103) while an R512E silicide coating extended rupture life to 84.8 hours, confirming that oxidation accelerates low-stress failure. These findings demonstrate that additive manufacturing of LDNb-ODS provides a viable, lightweight alternative to nickel-based superalloys for high-temperature (>850°C) aerospace components.

Low Density Niobium Alloy↗