Antonov, Stoichko

Publications and source records attributed to Antonov, Stoichko.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Creep Resistant Martensitic Steels for Operation at High-Temperatures in Power Generation Applications

Increasing the temperature capabilities of ferritic/martensitic 9-12% Cr steels can help in increasing the operating temperature of land-based turbines and minimize the use of expensive high-temperature alloys in the hot section. A creep resistant martensitic steel, JMP, was developed with the potential to operate at or above 650°C. The design of the alloys originated from computational modeling for phase stability and precipitate strengthening using fifteen constituent elements. Cobalt was used for increased solid solution strengthening, Si for oxidation resistance and different W and Mo concentrations for matrix strength and stability. The JMP steels showed increases in creep life compared to MARBN/SAVE12AD at 650°C for testing at various stresses between 138 MPa and 207 MPa. On a Larson-Miller plot, the performance of the JMP steels surpasses that of state-of-the-art MARBN steel. Approximately 21 years of cumulative creep data are reported for the JMP steels which encompasses various compositions. The relationships between composition-microstructure-creep properties are discussed including characterization of microstructures after >20,000 hours in creep.

Detrois, Martin↗
DOE OSTI2024

Inhomogeneous Distribution and Coarsening of y″ Precipitates in a Ni-Based Superalloy and Their Effect on Creep

It has been reported that the addition of Nb or Ta in the high Ti/Al ratio alloys promotes the formation of y″ precipitates solely and greatly contributes to the elevated temperature strength and resistance to creep deformation. In this study, the y''-dominant INCONEL alloy 725 (IN725) variants (named M725-Nb/Ta) modified with a high level of Nb/Ta additions and high Ti/Al ratio was chosen as a model alloy for microstructural observation of y'' variants upon creep. Following the high temperature aging (HTA), y'' was found to be the main strengthening precipitate with no detectable y’ in both M725 alloys. After creep, the grip/gage sections of the crept M725-Nb/Ta exhibited preferential coarsening and inhomogeneous distribution of y''. That is, one or two of the variants were preferentially coarsened at the expense of another variant, and sandwich-like structures, comprising of cubic y′ precipitates with small y″ discs on each face, were formed. This variant selection behavior taking place in the grip section with no stress applied was different from the typical stress-induced variant selection in previous literature. However, the sample with prior high temperature exposure (700 °C for 500 hours) with varying y″ characteristics demonstrated a similar trend of creep when compared with those in the HTA sample, suggesting that the coarsening and the inhomogeneous distribution of y'' was not the determinant of creep life in bulk M725-Nb/Ta alloys.

Hung, Chang-Yu↗
DOE OSTI2024

Inhomogeneous Distribution and Coarsening of γ″ Precipitates in a Ni-Based Superalloy and Their Effect on Creep

γ″ was found to be the main precipitate strengthening phase with no detectable g′ in both M725 alloys. After creep, the grip/gage sections of the crept M725-Nb/Ta exhibited preferential coarsening and inhomogeneous distribution of g″ platelets, and sandwich-like structures, comprising of cubic γ′ precipitates with small γ″ discs on each facet. This g″ variant selection behavior taking place in the grip section with no stress applied was different from the typical stress-induced variant selection reported in previous literature.

Hung, Chang-Yu↗
DOE OSTI2024

Influence of intermediate carbon content on the microstructure and high-temperature mechanical properties of cast and wrought Ni-based superalloy nimonic 105

NIMONIC® 105 variants with three different carbon concentrations were manufactured. Here, the medium carbon content variant shows inferior creep properties due to a bimodal grain size distribution and non-uniform carbides repartition leading to plastic strain accumulation between the two domains. Here, this eventually facilitated facile cracking and void formation during high-temperature creep.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Microstructure and Mechanical Properties of Ni-Based Superalloy Nimonic 105 with Varying Carbon Content

High carbon levels have been found to improve the fabricability of high-strength cast and wrought Ni-based superalloys, enabling the development of superior cast/wrought materials. However, carbon also strongly influences the microstructure and mechanical properties of the alloys. Nimonic 105 variants with three different carbon concentrations were manufactured. A bimodal grain size was found in the intermediate carbon content variant, while the high (low) carbon resulted in fine (coarse) grains thereby significantly affecting creep performance. The variations in grain structure were attributed to the primary carbides. An intermediate carbon level showed the best combination of strength and ductility in tension at high-temperature but little improvement in, or even inferior, creep performance. Discussion of the results will establish an understanding of the influence of carbon on the microstructure and mechanical properties of high strength cast and wrought superalloys, providing insights into obtaining high-quality alloys for future high-temperature applications.

Fang, Xiaotian↗
DOE OSTI2024

Enhancing Mechanical Properties of a Medium-Entropy Alloy by Regulating Mo Addition

Some multi-principal element alloys (MPEAs), including equiatomic, single-phase CrCoNi and CrCoFeMnNi are now widely recognized for their remarkable combinations of pronounced hardening rates, high ductility, and exceptional fracture toughness at room and cryogenic temperatures. To push the limit of hardenability of the medium-entropy alloy, the strategies associated with local lattice distortion or stacking fault energy (SFE) reduction that promote complex heterogeneity and defect dynamics require further investigation. The purposes of this study are to (1) further enhance the mechanical properties of a typical medium-entropy NiCoCr with alloying Mo, and (2) understand the strengthening mechanism of a Mo-added medium-entropy alloys.

Hung, Chang-Yu↗
DOE OSTI2024

Variations in γ′ formers and refractory elements for enhanced creep resistance and phase stability of an advanced Ni-based superalloy

The strong demands on increasing fuel efficiency have continuously driven the optimization of superalloys for high-performance applications. In this study, modifications to the chemistry and heat treatment of HAYNES® 282® alloy (H282) were performed by varying γ′ formers and refractory elements. It was found that increasing Ti and substituting W for some of the Mo in the newly designed alloy (Q) resulted in a significant improvement of creep resistance, up to 130% increase in creep life, compared to standard H282. It was found that Orowan loops and dislocation climb were the dominant creep deformation mechanisms in alloy Q, while extensive dislocation tangling as an additional configuration was observed in the baseline alloy. Moreover, phase stability investigations for up to 5000 h at 800 °C and 900 °C revealed a reduced formation of detrimental σ and μ phases in alloy Q when compared to H282. Atom-probe tomography (APT) revealed that the formation and growth of those phases were responsible for a decrease in Mo content in the matrix, thereby leading to a decrease in solid-solution strengthening in H282 over time. Furthermore, the coarsening of γ′ precipitates was retarded by the substitution of W for Mo, particularly under creep stress. The theoretical and experimental understanding of precipitation strengthening unraveled that higher optimal strengthening occurs at larger particle size for alloy Q, compared to the commercial formulation, further explaining the origin of enhanced creep resistance in the modified alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Tailoring the γ-γ'-γ" dual superlattice microstructure of INCONEL® 725 by high temperature aging and Nb/Ta additions for superior creep properties

Next-generation energy systems require superior resistance to creep deformation due to the considerably prolonged exposure times at operating stress and temperature. To improve the elevated temperature properties of INCONEL® 725 (IN725), a corrosion resistant alloy, several variants with different Ti/Al ratio and judicious amounts of Nb and Ta were made. Furthermore, a high temperature aging (HTA) heat treatment, designed to promote favorable precipitate phase formation, was explored. These adjustments allowed to tailor the amount and type of precipitate strengthening which led to significant increases in time to failure. The Ti/Al ratio was used to favor the formation of γ' or γ" precipitates. Compact morphology precipitates, consisting of γ' precipitates surrounded by a γ" shell, were formed in alloys with a low Ti/Al ratio. The HTA increased the creep life of various alloy formulations up to a maximum improvement of 371% as compared to the standard aging heat treatment. The Nb and Ta additions had a similar effect on increasing creep life by promoting and stabilizing γ" precipitation. The positive effect of the additions was even more pronounced when coupled with the HTA. A phase stability study with up to 10,000 h exposure at 700°C revealed that the compact morphology helped in slightly reducing coarsening of the γ' precipitates, although the effect on creep was not significant. The findings of this study enable design of dual superlattice alloys through microstructural engineering that yields superior performance and can be applied to a wide range of alloys in the IN718 and derivatives family.

Antonov, Stoichko↗
DOE OSTI2023

Variations in Creep Performance of P92 Steel Within Its Composition Range: Influence of N Solubility

Underspecified composition ranges often lead to alloys with unpredictable mechanical performance. To better understand the changes in microstructure and mechanical performance associated with variations of key elements, three versions of P92 are formulated within, or close to, the specified allowable for N, B, and C ranges. Chromium and Si are also varied to influence N solubility. Different service conditions (i.e., temperature and stress) are explored. It is observed that >80% decrease in creep life occurs at 625 °C and 155 MPa for the highest B and N containing alloy. Multiscale characterization reveals key changes due to the trace element variation. The high B and N containing alloy forms deleterious BN precipitates with morphology that promotes crack nucleation and damage accumulation, but this alloy additionally forms higher fractions of beneficial MX precipitates. The alloy with the lowest B and N concentrations but greater C content shows the best creep performance—a consequence of the refined M 23 C 6 carbide precipitate population and the absence of large-scale inclusions or BN precipitates. Calculations of creep activation energy reveal that the high B and N containing alloy is more prone to damage accumulation which causes an early onset of accelerating creep and greater minimum creep rate.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Variation of γ′ Formers and Refractory Elements for Enhanced Creep resistance and Phase Stability of HAYNES® 282® Alloy

Modifications to the chemistry of alloy 282 were performed to improve the alloy’s resistance to long term creep deformation as well as phase stability. Alloys were prepared using vacuum induction melting, computationally optimized homogenization heat treatment and hot working. Phase stability studies were carried out for up to 5,000 hours at 800°C and 900°C while creep testing was performed at conditions leading to lives past 7,000 hours for temperatures ranging from 740°C to 900°C. The formation of σ and μ phases were reduced in the modified alloy. Atom probe tomography (APT) was performed on the specimens from the phase stability study to investigate changes in the elemental partitioning to the γ and γ′ phases. Post deformation microstructures were analyzed using EBSD and TEM to study the influence of the detrimental phases on damage accumulation during creep.

Detrois, Martin↗
DOE OSTI2022

Exploring the Impact of N Solubility and Trace Elements on the Creep Properties of P92 Steel

Trace elements can have major consequences on the properties of creep resistant martensitic steels. To better understand the changes in microstructure and mechanical performance associated with the variation of trace elements and enable design of steels operating at more demanding conditions, we formulated three versions of P92 within the specified allowable N, B, C and Si ranges. Different service conditions were explored, and >80% decrease in creep life was observed at 625°C 155MPa for the highest B and N containing alloy. Multiscale characterization (OM, SEM, TEM) revealed key changes due to the trace element variation. The high trace content alloy formed deleterious BN precipitates with morphology that would promote crack nucleation, but also formed higher fractions of beneficial MX precipitates. The alloy with the lowest trace content showed the best creep performance – a result of the refined precipitate populations and the absence of large-scale inclusions and BN precipitates.

Antonov, Stoichko↗
DOE OSTI2022

Implications of carbon content for the processing, stability, and mechanical properties of cast and wrought Ni-based superalloy Nimonic 105

As the temperature and pressure requirements in land-based turbines for power generation increase, the shift towards more advanced alloys, e.g., Ni-based superalloys, requires improved understanding of their long-term stability and mechanical properties. Additionally, the larger size of the components also presents fabrication and cost-reduction problems. In this study, we investigated Nimonic 105 as a potential rotor material at two carbon content levels – the commonly used maximum of the alloy specification and a lower carbon content variant. Reducing the carbon content presented fabrication challenges, resulting in surface crack formation during hot working. Additionally, a lower M 6 C carbide fraction was present after fabrication/solutioning, leading to a significantly larger grain size. After the standard aging treatment, similar γ' populations formed in the two variants, however the M 6 C carbides in the high-carbon variant already started transforming to intergranular M 23 C 6 . Although we did not observe a noticeable effect on the tensile properties of the two variants, the lower carbon content alloy possessed a superior creep property – mainly due to the larger grain size as the microstructural stability was inferior. Further, upon prolonged thermal exposure, the M 6 C carbides in the low-carbon variant further decomposed to intergranular and intragranular σ and μ precipitates, as opposed to mainly M 23 C 6 as in the high-carbon variant.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Improved Creep and Tensile Properties of a Corrosion Resistant Ni-Based Superalloy Using High Temperature Aging and Nb/Ta Additions

Resistance to creep deformation is essential for cast and wrought Ni-based superalloys in next generation energy systems due to the considerable exposure times required at the operating temperature. Here the amount of precipitate strengthening was increased in variants to Inconel alloy 725 (IN725), a corrosion resistant alloy, to improve its elevated temperature mechanical strength. Additions of Nb or Ta coupled with a high temperature aging (HTA) heat treatment promoted the formation of γ" precipitates and grain boundary phases which led to significant increases in time to failure. The HTA increased the creep life of various alloy formulations as compared to the standard aging heat treatment with a maximum improvement of 371%. The Nb and Ta additions lowered the minimum creep rate (MCR) and had a similar effect on increasing creep life. The positive effect of the additions was more pronounced when coupled with the HTA which employed a higher temperature in the first step of the heat treatment to promote precipitate phase formation. The Ti/Al ratio was used to design alloys with preferential formation of ' or γ" precipitates. Compact morphology precipitates were formed in the alloys with a low Ti/Al ratio. While a low Ti/Al ratio was primarily associated with lower MCRs, the effect on the creep life was less evident than that of the HTA. By using additions of Nb or Ta and a HTA heat treatment, the creep life of IN725 for testing at 973 K (700 °C) and 483 MPa was improved by up to 256%.

36 MATERIALS SCIENCE↗