DOE OSTI2025

Microwave Annealing for Fast and Effective Hydrogen Activation in Polycrystalline Silicon Passivating Contacts

Hydrogenation is a crucial step in the fabrication of high-efficiency silicon solar cells. In this study, the effectiveness of hydrogen activation is demonstrated via microwave annealing of hydrogen-rich dielectrics coated on poly-Si passivating contacts. This method is compared with conventional hydrogenation techniques, such as annealing in N2 in the presence of a hydrogen-rich source (such as hydrogenated aluminum oxide (AlOx:H), hydrogenated silicon nitride (SiNy:H), or a AlOx:H/SiNy:H stack). Key improvements observed include a reduction in J0 from 30 to <5 fA cm-2, an increase in iVoc from 690 to >730 mV, and an enhancement in effective lifetime (teff) from 0.6 to ~3.5 milliseconds on phosphorus-doped poly-Si/SiO2 passivating contact samples. With a very short annealing time of ~1-2 min, the samples passivated by AlOx:H, SiNy:H, or the stack show similar performance to samples subjected to 30 min of nitrogen annealing. Photoluminescence (PL) spectra corroborate the findings regarding the hydrogenation of the poly-Si layer and the c-Si substrate, with an increase in PL intensity after microwave annealing. Ultimately, this work suggests that microwave annealing could be a promising addition, offering flexibility to traditional firing hydrogenation processes.

hydrogenation↗

DOE OSTI2024

Passivation Mechanisms in Locally Etched P-Type Poly-Si on Silicon Nitride/Silicon Oxide Stack

Tunneling oxide passivated contacts are quickly becoming the industry standard for high-efficiency c-Si based photovoltaic cells. Further development of these structures is essential to enable higher efficiencies and better reliability of cells. By utilizing poly-Si/SixNy/SiOx stacks, very high efficiencies have been demonstrated on small area cells. In this work we investigate the cause of the excellent passivation seen by these structures and show that the primary reason of the excellent passivation seen is the blocking B diffusion to the SiOx/c -Si interface. We also show that the interface between the silicon nitride and polysilicon affects B diffusion through to the c-Si interface. Finally, we demonstrate that the composition of the nitride used is of great importance, and that an incorrect nitride composition leads to B diffusion, and is directly correlated to poor passivation performance.

industries↗

DOE OSTI2024

Recovery of Glass and Silicon Solar Cells from Si-Modules Through Laser Processing

This study demonstrates an innovative and environmentally friendly laser-based approach for the efficient recovery of glass and silicon solar cells, allowing the recycling of photovoltaic modules. The methodology involves the use of a high-power pulsed laser beam focusing at various interfaces within the modules. Specifically, the delivery of ultra-short pulse laser energy at the interfaces of glass and polymeric encapsulants, as well as at the encapsulants and silicon solar cells, facilitates the debonding of polymers from both glass and silicon cell surfaces. The debonding occurs through photothermal, ablation, chemical modification, and localized heat generation. The research successfully demonstrates the recovery of glass from commercial mini solar modules of size 11.5 x 6.8 cm 2 and a silicon wafer of size 3.0x1.6 cm 2 . Ongoing efforts aim to extend the effectiveness of this laser-based methodology to comprehensively recycle larger-size components. This innovative approach holds promise for addressing environmental concerns associated with the disposal of solar modules, contributing to sustainable practices in the renewable energy sector.

glass↗

DOE OSTI2024

Passivated Contacts for Direct Wafer Product (Final Technical Report)

This TCF project developed a thin-oxide (SiO 2 )/polycrystalline silicon (poly-Si) passivated contact solar cell on CubicPV's (formally 1366 Technologies, Inc.) Direct Wafer® Product (DWP) kerfless wafers. The project used two NREL-developed technologies described in U.S. Patent No. 9,911,873, Hydrogenation of Passivated Contacts and U.S. Patent Application Serial No. 15/890,172, Doped Passivated Contacts . The project was motivated by a potential higher efficiency cell (compared to a PERC cell) using passivated contacts on the ultra-low cost kerfless wafers grown using the Direct Wafer process. The hope was to accelerate market adoption of the cell and wafer by delivering the lowest LCOE in the PV industry. The project tested both n-type and p-type SiO 2 /poly-Si passivated contacts grown by thermal oxidation and plasma enhanced chemical vapor deposition (PECVD) of the poly-Si layer on DWP with varying wafer resistivities. Both deposition techniques are industry standards and thus economically viable methods for commercializing the contacts. The results indicated that both n-type and p-type poly-Si passivated contacts can be formed on polycrystalline DWP wafers, but implied open-circuit voltages (i Voc ) were limited to below 0.65 mV (compared with ~ 730 mV on n-Cz wafers). Diffusion of H to the Si/SiO 2 /poly-Si interface was key to obtaining high i Voc values. In this study, H was diffused from a high-temperature SiN x layer deposited over the poly-Si layer during a high-temperature firing step, similar to one used for screen printed metals. The study concluded that poly-Si passivated contacts on DWP wafers passivated the surface of the wafers as well as PERC passivated surfaces, which use a less expensive dielectric layer stack. The project showed that Direct Wafer Product wafers grown by CubicPV could produce high i Voc values (~0.647 mV), which could produce a cell over 20% efficient with proper processing and metallization. These cells, though not economically viable in 2024 as a stand-alone cell, could be integrated with a wide-bandgap top solar cell to form a two-junction tandem cell that could be viable under certain circumstances. This is because the bottom cell of a 30%, two-terminal tandem only needs to be a 20% cell under one-sun conditions. Thus, the DWP could be an ideal low-cost wafer for tandems. The project also revealed that a TOPCon type cell could be formed on a p-type DWP wafer using a P-diffused emitter and a p-type poly-Si contact. In fact, the p-type version of the poly-Si contact out-performed the n-type version for a variety of wafer resistivities, from highly doped to lowly doped. This curiosity requires more work to understand because on Cz wafers, the n-type poly-Si contact is of much higher quality than the p-type version.

14 SOLAR ENERGY↗

DOE OSTI2024

Towards Polymer-Free, Femto-Second Laser-Welded Glass/Glass Solar Modules

This project explores the use of femto-second (fs) lasers to form glass-to-glass welds for hermetically sealed, polymer-free solar modules. Low iron solar glass coupons were welded together without the use of glass filler using a fs laser with dedicated optics to elongate the focal plane parallel to the incident beam. The resulting welds were then stress tested to failure to reveal the critical stress intensity factor, KIc. These values were used in a structural mechanics model of a 1 m by 2 m glass/glass module under a simulated static load test. The results show that the fs laser welds are strong enough for a suitably framed module to pass the IEC 61215 static load test with a load of 5400 Pa. Key to this finding is that the module must be framed and braced, and the glass must be ribbed to allow pockets for the cells and welds inside the border of the module. The result is a module design that is completely polymer-free, hermetically sealed, has improved thermal properties, and is easily recycled.

femto-second laser welded↗

DOE OSTI2024

Crystalline Si Surface Passivation with Nafion for Bulk Defects Detection with Electron Paramagnetic Resonance

Here, in monocrystalline Si (c-Si) solar cells, identification and mitigation of bulk defects are crucial to achieving a high photoconversion efficiency. To spectroscopically detect defects in the c-Si bulk, it is desirable to passivate the surface defects. Passivation of the c-Si surface with dielectrics such as Al 2 O 3 and SiNx requires deposition at elevated temperatures, which can influence defects in the bulk. Herein, we report on the passivation of different Czochralski (Cz) Si wafer surfaces by an organic copolymer, Nafion. We test the efficacy of the surface passivation at temperatures ranging from 6 to 473 K to detect bulk defects using electron paramagnetic resonance (EPR) spectroscopy. By comparing with state-of-the-art passivation layers, including Al 2 O 3 and liquid HF/HCl, we found that at room temperature, Nafion can provide comparable passivation of n-type Cz Si with an implied open-circuit voltage (iV oc ) of 713 mV and a recombination current prefactor J o of 5 fA/cm 2 . For p-type Cz Si, we obtained an iV oc of 682 mV with a J o of 22.4 fA/cm 2 . Scanning electron microscopy and photoluminescence reveal that Nafion can also be used to passivate the surface of c-Si solar cell fragments scribed from a solar cell module by using a laser. Consistent with previous studies, analysis of the EPR spectroscopy data confirms that the H-terminated surface is necessary, and fixed negative charge in Nafion is responsible for the field-effect passivation. While the surface passivation quality was maintained for almost 24 h, which is sufficient for spectroscopic measurements, the passivation degraded over longer durations, which can be attributed to surface SiO x growth. These results show that Nafion is a promising room-temperature surface passivation technique to study bulk defects in c-Si.

14 SOLAR ENERGY↗

DOE OSTI2023

Self-Assembled Monolayer Patterning for PolySi/SiO2 Passivated Contacts

We utilize hexamethyldisilazane (HMDS) based self assembled monolayers to pattern polysilicon (polySi) passivated contacts. We find process conditions that allow for etching front side n/polySi between fingers; thereby increasing Jsc. Importantly, the Voc does not degrade indicating the additional process steps do not introduce defects or impurities. HMDS layers remain on the surface for metallization without detriment to transport.

degradation↗