NASA NTRS · 20160014739

Composites for Exploration Upper Stage

Fikes, J. C.·Jackson, J. R.·Richardson, S. W.·Thomas, A. D.·Mann, T. O.·Miller, S. G.

View original source ↗Export metadata ↓

Abstract

The Composites for Exploration Upper Stage (CEUS) was a 3-year, level III project within the Technology Demonstration Missions program of the NASA Space Technology Mission Directorate. Studies have shown that composites provide important programmatic enhancements, including reduced weight to increase capability and accelerated expansion of exploration and science mission objectives. The CEUS project was focused on technologies that best advanced innovation, infusion, and broad applications for the inclusion of composites on future large human-rated launch vehicles and spacecraft. The benefits included near- and far-term opportunities for infusion (NASA, industry/commercial, Department of Defense), demonstrated critical technologies and technically implementable evolvable innovations, and sustained Agency experience. The initial scope of the project was to advance technologies for large composite structures applicable to the Space Launch System (SLS) Exploration Upper Stage (EUS) by focusing on the affordability and technical performance of the EUS forward and aft skirts. The project was tasked to develop and demonstrate critical composite technologies with a focus on full-scale materials, design, manufacturing, and test using NASA in-house capabilities. This would have demonstrated a major advancement in confidence and matured the large-scale composite technology to a Technology Readiness Level 6. This project would, therefore, have bridged the gap for providing composite application to SLS upgrades, enabling future exploration missions.

Explore related subjects

composites joints manufacturing

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Fikes, J. C., Jackson, J. R., Richardson, S. W., Thomas, A. D., Mann, T. O., Miller, S. G.. 2016-12-01. Composites for Exploration Upper Stage. https://ntrs.nasa.gov/citations/20160014739

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

NASA NTRS2026

Polymer Composite Material Testing for a Cryotank Application

Composite cryotanks will play a key role in enabling the next generation of efficient aircraft. Carbon fiber reinforced polymer (CFRP) composites have the benefits of reduced weight and potentially higher structural strength compared to traditional metallic fuel tanks. A material screening study was conducted to inform material selection for liquid hydrogen (LH2) fuel storage. Three composite materials were considered because of their aerospace grade toughness, strength, and existing data to compare against. These materials were a thermoplastic low-melt polyaryletherketone (LM-PAEK)/carbon fiber (CF), thermoset/CF, and hybrid thermoset/thermoplastic polyurethane (TPU) veil/CF composite. Mechanical screening tests included tension, compression, in-plane shear (IPS), and tensile-tensile fatigue (TTF). Each material was tested at both a baseline (no liquid nitrogen/LN2 cycling) and 100 LN2-cycled conditions to determine the knockdown factor, if any, of each material when exposed to environmental loading effects in a cryotank. Results show minimal effects of the LN2-cycling compared against baseline values. The three materials behaved similarly in tension; however, the thermoplastic/CF had the highest IPS toughness. The hybrid thermoset/TPU/CF composite had the lowest IPS strength, compressive strength, and toughness. LN2-cycling had minimal effects on tensile-tensile fatigue performance of the thermoplastic/CF material. Mechanical data was captured to guide material down selection for future commercially viable hydrogen aircraft design. In its current state, there does not exist a consolidated, publicly available database for CFRP composite material performance data at cryogenic temperatures. The next step in this work is to test the thermoplastic and thermoset CFRP composites, as well as the neat resins, at LH2 relevant temperature (20 K) to capture this crucial material property data. These results are essential to inform cryotank design and modeling efforts. The process to start this next round of testing has begun. Planned mechanical tests include toughness (single-edge notched beam), tension (unidirectional and quasi-isotropic), thermal expansion, and thermal conductivity. Some tests will also be conducted at an intermediate temperature of 111 K relevant to liquid natural gas (LNG), another attractive fuel choice. The ultimate goal is to manufacture a sub-scale cryotank part that can pass relevant burst, fatigue, permeation, and thermal cycling tests. This work is a part of NASA’s Commercially viable Hydrogen Aircraft for Robust Growth in Efficiency (CHARGE) Project under the larger NASA Subsonic Vehicle Technologies and Tools (SVTT) Project.

composites↗

DOE OSTI2025

Methodologies and strategies for detecting fiber orientation in polymeric fiber-reinforced composites

In this review paper different methods and techniques for representing fiber orientation in advanced polymer matrix composites are presented. A description of the effect of fiber orientation on processing, fabrication and mechanical properties of a composite material is presented. The paper discusses the mathematical modeling and modeling techniques for fiber structure representation in polymeric composites, with an emphasis on fiber orientation in a composite part. The paper is divided into two sections; namely—destructive techniques and non-destructive techniques. The capabilities and limitations of each technique with respect to fiber orientation detection and measurements are discussed.

composites↗

NASA NTRS2024

Out of Plane Stresses Using a Beam-Based Elastic Foundation Bonded Joint Model

Efficient, semi-analytical models of bonded joints are utilized for initial joint design and sizing due to their convenience and speed. Many of these models are based on beam and plate theories, which are most applicable when in-plane stresses/strains dominate. While this can be a sensible assumption for obtaining the deformations of the joint, out of plane (transverse) stresses are often of critical importance for failure in bonded joints composed of fiber reinforced composite materials. Since through-thickness strains are neglected in these semi-analytical theories, the present study shows a method to back-calculate the out of plane stresses based on stress balance equations, which use the in-plane stresses and displacements that have already been obtained. The method was implemented within the Joint Element Designer (JED) software, and verification and validation examples have been shown. As is typical for these types of models, corner stress singularities are not captured by the JED model, but the general trends of the stress and deformation fields agreed with a higher fidelity finite element model. As such, this method for obtaining out of plane stresses, when coupled with the JED code, is very useful for the complete stress analysis of bonded composite joints.

composites↗