A Polymer-Assisted Spinodal Decomposition Strategy toward Interconnected Porous Sodium Super Ionic Conductor-Structured Polyanion-Type Materials and Their Application as a High-Power Sodium-Ion Battery Cathode

Abstract

A general polymer-assisted spinodal decomposition strategy is used to prepare hierarchically porous sodium super ionic conductor (NASICON)-structured polyanion-type materials (e.g., Na 3 V 2 (PO 4 ) 3 , Li 3 V 2 (PO 4 ) 3 , K 3 V 2 (PO 4 ) 3 , Na 4 MnV(PO 4 ) 3 , and Na 2 TiV(PO 4 ) 3 ) in a tetrahydrofuran/ethanol/H 2 O synthesis system. Depending on the boiling point of solvents, the selective evaporation of the solvents induces both macrophase separation via spinodal decomposition and mesophase separation via self-assembly of inorganic precursors and amphiphilic block copolymers, leading to the formation of hierarchically porous structures. We find that the resulting hierarchically porous Na 3 V 2 (PO 4 ) 3 possessing large specific surface area (≈77 m 2 g -1 ) and pore volume (≈0.272 cm 3 g -1 ) shows a high specific capacity of 117.6 mAh g -1 at 0.1 C achieving the theoretical value and a long cycling life with 77% capacity retention over 1000 cycles at 5 C. This method presented here can open a facile avenue to synthesize other hierarchically porous polyanion-type materials.