SIR Glass Test Vehicle Designed to Characterize Process Materials

Abstract

The exposure to harsh environments can result in reliability issues on highly dense electronic packages and circuit assemblies. One area of concern is electrochemical failure mechanisms caused by electrolytic corrosion, electrochemical migration (dendrites), and leakage currents under humid conditions. These no-fault and no-trouble found failure points are challenging to detect and to perform process control during the assembly process. The focus of this research centers on metallizing glass surface insulation resistance test vehicles to characterize materials on electronic packages and components that exhibit the highest risk of failure due to material interactions and process residues. Glass test vehicles provide a visual representation of materials when they are exposed to moisture content in the air. Harsh environments can cause material interactions resulting in morphology changes, opening, and release of active components. A transparent test vehicle is highly functional for environmental stress testing under temperature, humidity, and bias. The designed experiment will evaluate the effects of material and process residues that can undergo changes in behavior during application, which leads to local failures.