Nanostructured Composite Alloys for Extreme Environments

Abstract

Accumulative Roll Bonding was used to process nanolayered Cu/Nb and Zr/Nb composites with varying individual layer thickness. Mechanical tests show remarkable strength as the average layer thickness decreases. Relatively high strength is preserved even at elevated temperatures. Despite differences in texture between rolling paths (longitudinally rolled-RL and cross rolled-CR) Cu/Nb, flow stresses between the resultant materials were similar. In addition, thermal conductivity does not change significantly as the interface density increases. The alloys show remarkable resistance to irradiation damage at very high doses due to stability of the interfaces. The results on Zr/Nb indicate that liquid phase chemistry resulting from thermal spikes play an important role and should be taken into account when designing alloys for extreme environments.