Stable, high-performing bifunctional electrodes for anion exchange membrane-based unitized regenerative fuel cells

Abstract

Anion exchange membrane unitized regenerative fuel cells (AEM-URFCs) are a promising technology for energy storage and electricity production; however, their efficiency is limited by the kinetics of the bifunctional oxygen electrode (BOE) where the oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) occur. A particular concern when designing the BOE is that the OER and ORR have differing catalytic requirements, which make it challenging to develop effective bifunctional electrocatalysts with single active sites. In this study, we focus on advancing the BOE performance using Pt-IrO x and Pt-NiCoO x electrocatalysts. Here, single-layer and dual-layer Pt-IrO x BOEs were made, with the dual-layer electrode leading to improved performance due to efficient catalyst utilization in both modes. Using the dual-layer oxygen electrode paired with a PtRu/C hydrogen electrode, a round trip efficiency (RTE) as high as 50% (62 %iR-free) was achieved at 500 mA/cm 2 and operation for more than 24 h, which included five one-hour-long H 2 generation and consumption cycles followed by one eight-hour-long cycle. To the best of our knowledge, this is the highest performance for AEM-URFCs reported to date. Lastly, the approach is extended to electrodes with a Pt loading of 0.5 mg/cm 2 and the IrO x substituted by NiCoO x .