DOE OSTI2026

Development of a Framework and Methodology for an Advanced Reactor Materials Environmental Effects Design Guide

Advanced non-light-water reactor components may operate at elevated temperature while experiencing cyclic loading, significant neutron irradiation, and exposure to reactor coolant. ASME Boiler and Pressure Vessel Code, Section III, Division 5, provides design rules for elevated-temperature service but does not include specific procedures to account for environmental effects on material properties. This report develops an initial framework and methodology for an Environmental Effects Design Guide (EEDG) focused on neutron irradiation; coolant-environment effects are reserved for future work. The proposed approach treats irradiation as a property-based overlay on the existing Division 5 design process, with two routes: a sparse-data route applying two reduction factors — FCR on creep-rupture strength and FF on fatigue life — for the creep-fatigue evaluations that typically control the design of advanced high-temperature reactor components, and a fuller framework developing the property-to-rule chain across the four Division 5 checks (primary load, strain limits and ratcheting, creep-fatigue, and buckling), together with swelling and weldments as scope items. Both routes are scoped by an in-pile qualification that restricts the use of post-irradiation-examination-derived properties in regimes where an in-pile mechanism could control the design outcome. Illustrative outputs derived on a compiled annealed Type 316 database — FCR ≈ 0.78–0.86 and FF ≈ 0.4 — demonstrate the calculation method within that specific dataset. The framework is an initial, testable design-rule concept; it identifies a practical path for preliminary design evaluations under sparse data and the material data and testing needed to develop the framework further.

Barua, Bipul (ORCID:0000000247184113)↗
DOE OSTI2024

High‐Loading Lithium‐Sulfur Batteries with Solvent‐Free Dry‐Electrode Processing

Abstract Lithium‐sulfur (Li‐S) batteries, with their high energy density, nontoxicity, and the natural abundance of sulfur, hold immense potential as the next‐generation energy storage technology. To maximize the actual energy density of the Li‐S batteries for practical applications, it is crucial to escalate the areal capacity of the sulfur cathode by fabricating an electrode with high sulfur loading. Herein, ultra‐high sulfur loading (up to 12 mg cm −2 ) cathodes are fabricated through an industrially viable and sustainable solvent‐free dry‐processing method that utilizes a polytetrafluoroethylene binder fibrillation. Due to its low porosity cathode architecture formed by the binder fibrillation process, the dry‐processed electrodes exhibit a relatively lower initial capacity compared to the slurry‐processed electrode. However, its mechanical stability is well maintained throughout the cycling without the formation of electrode cracking, demonstrating significantly superior cycling stability. Additionally, through the optimization of the dry‐processing, a single‐layer pouch cell with a loading of 9 mg cm −2 and a novel multi‐layer pouch cell that uses an aluminum mesh as its current collector with a total loading of 14 mg cm −2 are introduced. To address the reduced initial capacity of dry‐processed electrodes, strategies such as incorporating electrocatalysts or employing prelithiated active materials are suggested.

Chemistry↗
DOE OSTI2025

An attention-based neural ordinary differential equation framework for modeling inelastic processes

To preserve strictly conservative behavior as well as model the variety of dissipative behavior displayed by solid materials, we propose a significant enhancement to the internal state variable-neural ordinary differential equation (ISV-NODE) framework. In this data-driven, physics-constrained modeling framework internal states are inferred rather than prescribed. The ISV-NODE consists of: (a) a stress model dependent on observable deformation and inferred internal state, and (b) a model of the evolution of the internal states. The enhancements to ISV-NODE proposed in this work are multifold: (a) a partially input convex neural network stress potential provides polyconvexity in terms of observed strain while leaving the inferred state unconstrained, and (b) an internal state flow model uses common latent features to inform novel attention-based gating and drives the flow of internal state only in dissipative regimes. We demonstrated that this architecture can accurately model dissipative and conservative behavior across an isotropic, isothermal elastic-viscoelastic-elastoplastic spectrum with three exemplars, while maintaining fundamental principles by design.

97 MATHEMATICS AND COMPUTING↗
DOE OSTI2026

Virtual Growth of SRF Materials

Niobium's native surface oxide affects SRF cavity and superconducting qubit performance, motivating interest in controlling its crystalline structure. We combine a literature-derived machine-learning analysis with temperature-dependent XRD to study crystalline ordering in Nb2O5. Random Forest models, trained on 74 processing conditions from 17 papers and validated by leave-one-group-out cross-validation, predicted broad crystallinity outcomes well (balanced accuracy 0.809), but struggled with specific polymorph identity (0.577). Annealing temperature was the dominant predictor across all targets; oxygen partial pressure showed negligible importance, reflecting narrow literature coverage rather than physical irrelevance. Temperature-dependent XRD on anodized and H2O2-treated Niobium showed structural evolution consistent with the machine learning predictions. Our model and overall approach provide a data-driven framework for identifying and optimizing conditions that promote crystallization in initially amorphous oxides. This framework can guide the selection of growth and post-annealing conditions for Nb surfaces by narrowing the experimental parameter space, thereby reducing trial-and-error efforts in developing oxide structures relevant to SRF applications.

Tilkin, Anthony [Fermilab]↗
DOE OSTI2026

Fracture Analysis of Cohesive Zone Models for Modeling Residual Stress Induced Delamination in Composite Structures

A fracture study of coupon-scale composite cylinders with embedded defects was conducted with an objective to assess and validate a modeling approach using two available cohesive material models. The study included experimental and simulation evaluations of initiation of crack growth and progression. Interrupted thermal experiments used acoustic emissions monitoring to identify the onset of crack progression during each cooling interval and ultrasonic scanning provided images of defect growth. Verification, validation, and uncertainty quantification (VVUQ) processes were performed in the assessment of the simulation predicted temperature at which crack propagation begins (quantity of interest). The Sobol sensitivity analysis identified the hoop direction elastic modulus in the carbon fiber reinforced polymer (CFRP) plies as the most influential parameter for simulations using both cohesive models, accounting for at least 70% of the variation in the temperature at crack propagation. The UQ temperature range for the Tvergaard-Hutchinson model was higher (more conservative) than the experimental acoustic measurement indicators of crack progression, while the temperature range for the Thouless-Parmigiani model enveloped the experimental data points for the primary defect size of 0.75 x 1 in. The simulations could not capture the stable crack growth indicated in the experiments. This is likely due to the models’ inability to represent anisotropic fracture toughness attributed to the structure of the orthotropic fiber weave in a woven composite laminate.

42 ENGINEERING↗
DOE OSTI2025

Advancements in nanocomposites for enhancing the performance of rechargeable lithium-ion batteries

The benefits of nanotechnology have been realized in almost every component of lithium-ion batteries. From electrodes to electrolytes, the incorporation of nanoparticles as dopants and coatings has shown marked improvements in cell cycle life, efficiency, mechanical and thermal stabilities, and lithium-ion transport. The improvements realized depends on several factors, from processing methods, nanoparticle type, structure, and concentration, to the material into which the nanoparticulate will be incorporated. Regardless of these many factors, nanotechnology has vastly improved the performance of secondary lithium-ion batteries. Here we will highlight some of the works that demonstrate these improvements and the quantitative benefits of nanotechnology.

25 ENERGY STORAGE↗
DOE OSTI2025

Energy filtering–induced ultrahigh thermoelectric power factors in Ni 3 Ge

Traditional thermoelectric materials rely on low thermal conductivity to enhance their efficiency but suffer from inherently limited power factors. Innovative pathways to optimize electronic transport are thus crucial. Here, we achieve ultrahigh power factors in Ni 3 Ge-based systems through an unconventional thermoelectric materials design principle. When overlapping flat and dispersive bands are engineered to the Fermi level, charge carriers can undergo intense interband scattering, yielding an energy filtering effect similar to what has long been predicted in certain nanostructured materials. Via a multistep DFT-based screening method developed here, we find a family of L1 2 -ordered binary compounds with ultrahigh power factors up to 11 mW m −1 K −2 near room temperature, which are driven by an intrinsic phonon-mediated energy filtering mechanism. Our comprehensive experimental and theoretical study of these intriguing materials paves the way for understanding and designing high-performance scattering-tuned metallic thermoelectrics.

Science & Technology - Other Topics↗
DOE OSTI2025

Modeling phase transformations in Mn-rich disordered rocksalt cathodes with machine-learning interatomic potentials

Mn-rich disordered rocksalt (DRX) cathode materials exhibit a phase transformation from a disordered to a partially disordered spinel-like structure (δ-phase) during electrochemical cycling. Here, in this computational study, we use charge-informed molecular dynamics with a fine-tuned CHGNet foundation potential to investigate the phase transformation in LixMn 0.8 Ti 0.1 O 1.9 F 0.1 . Our results indicate that transition metal migration occurs and reorders to form the spinel-like ordering in an FCC anion framework. The transformed structure contains a higher concentration of nontransition metal (0-TM) face-sharing channels, which are known to improve Li transport kinetics. Analysis of the Mn valence distribution suggests that the appearance of tetrahedral Mn 2+ is a consequence of spinel-like ordering, rather than the trigger for cation migration as previously suggested. Calculated equilibrium intercalation voltage profiles demonstrate that the δ-phase, unlike the ordered spinel, exhibits solid-solution signatures at low voltage. A higher Li capacity is obtained than in the DRX phase. This study provides atomic insights into solid-state phase transformation and its relation to experimental electrochemistry, highlighting the potential of machine-learning interatomic potentials for understanding complex oxide materials.

Zhong, Peichen [University of California, Berkeley↗
DOE OSTI2025

Strategies for Fabricating Molybdenum Structures Using Laser Powder Bed Fusion

Advances in manufacturing techniques are viewed as enabling technologies for development of high performance nuclear fuel forms that couple high uranium density with improvements to key properties such as thermal conductivity unattainable through conventional fabrication routes. Additive manufacturing (AM) enables the fabrication of complex fuel geometries that are difficult or impossible to achieve using conventional manufacturing methods. Melting-based AM processes, such as laser powder bed fusion (LPBF), provide high geometric resolution (>200 µm depending on the feature) across a variety of metal alloys, including those suitable for high-temperature fuel cladding applications, such as Nb, W, and Mo. Molybdenum is particularly attractive due to its high thermal conductivity, low thermal expansion, and excellent mechanical stability at elevated temperatures. However, its high melting temperature and brittle nature at low temperatures pose significant challenges during LPBF processing. Rapid solidification inherent to LPBF induces high residual stresses, often leading to post-solidification cracking, which limits the manufacturability of Mo components via this method.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2026

Dynamic asymmetric strain imprinted into substrates by an oxide thin film

In film-substrate systems, the substrate role is often considered to be limited to providing static mechanical constraints. Dynamic film-substrate interactions when a structural change in the film modifies the substrate are generally disregarded. Here, using combined x-ray and electron microscopies, we observed that an electrically induced filament in a vanadium dioxide film created strong asymmetric strain in an underlying sapphire substrate. This asymmetric substrate strain fed back into the film and defined the filament expansion direction, revealing the importance of film-substrate dynamic interactions in determining film functionality. Furthermore, the strain imprint propagated at least tens of micrometers deep into the substrate, exceeding the film thickness by more than 200-fold, potentially enabling substrate functionalization as an active mechanical coupling media in three-dimensional integrated microelectronic architectures.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2025

Highly textured metal anodes for stable aqueous batteries: Fabrication and characterization

We report a purely mechanical “cold-compression flow” method for fabricating Zn, Sn, and In substrates with tunable crystallographic textures. Using textured Zn as a model system, we investigate Zn electrocrystallization and demonstrate correlated growth of crystalline films with correlation lengths from tens to hundreds of micrometers. At 5 milliamperes per square centimeter (mA/cm 2 ), capacities between 20 and 82 milliampere hours per square centimeter (mA·hour/cm 2 ) are achieved depending on substrate texture level. At higher currents (40 mA/cm 2 ), capacities reach up to 604 mA·hour/cm 2 . Rotating disk electrode studies show that dominantly (002) textured Zn substrates exhibit enhanced corrosion resistance and reduced interphase passivation. We introduce an effective Damköhler number (Da*) to concisely describe morphological evolution during electrocrystallization across substrates with different textures. High-texture (002) Zn substrates substantially enhance performance in high-capacity (~20 mA·hour/cm 2 ) symmetric Zn||Zn cells and full cells (Zn||δ-MnO 2 and Zn||I 2 ), enabling fast-charging and prolonged energy storage in coin and pouch rechargeable Zn battery formats.

Science & Technology - Other Topics↗
DOE OSTI2026

Atomistic Simulation of Glasses and Amorphous Materials: Challenges and Opportunities for the Next Decade

Atomistic simulations have become indispensable tools for understanding glass structure, dynamics, and properties, yet persistent challenges limit their predictive power. This perspective examines three interconnected issues, namely glass formation procedures, interatomic potential development, and machine learning applications, which emerged from the 5th International Workshop on Challenges of Atomistic Simulations of Glasses and Amorphous Materials. We identify convergent community priorities for (i) standardized validation protocols, (ii) curated benchmark datasets with complete metadata, and (iii) open repositories for glasses. A systematic was forward is provided by a hierarchical validation framework for assessing the structural fidelity, property prediction, and behavioral realism of simulation techniques. Looking ahead, transformative advances are promised by the fusion of classical techniques with machine learning based approaches, for instance, by integrating swap Monte Carlo with machine-learning (ML) potentials, leveraging foundation models through transfer learning, and finetuning ML potentials with experimental data. Progress depends on the community committing to validated models, reproducible protocols, and sustained data sharing.

Krishnan, N. M. Anoop↗
DOE OSTI2026

Kondo effect in ferromagnetic quantum critical CeRh 6 ⁢Ge 4

The mechanism of a pressure-induced quantum critical point in the heavy fermion ferromagnet CeRh 6 ⁢Ge 4 has attracted interest, as ferromagnetic quantum criticality in a clean itinerant Ce compound is typically avoided. The localized versus itinerant character of the 4⁢𝑓 electrons is a key aspect for understanding this behavior. We investigated the electronic structure of the 4⁢𝑓 shell in CeRh 6 ⁢Ge 4 using core-level photoelectron and x-ray absorption spectroscopy, demonstrating the hybridization of Ce 4⁢𝑓 with the conduction electrons. Linearly polarized x-ray absorption reveals a temperature-dependent linear dichroism consistent with the crystal-electric-field sequence as inferred from the static susceptibility. This dichroism cannot be described by an ionic full-multiplet model alone, but is reproduced by including the Kondo effect within a single-impurity Anderson model in the noncrossing approximation. The Kondo effect mixes higher-lying crystal-field states into a resulting multiorbital ground state with 4⁢𝑓 occupancy, 𝑛 𝑓 ∼ 0.9. Deviations at low temperatures between the measured linear dichroism and calculated dichroism suggest an orbital-dependent Kondo effect. A scenario in which there is a multiorbital ground state and orbital-dependent Kondo hybridization should be a starting point for a model of pressure-induced criticality in CeRh 6 ⁢Ge 4 .

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2025

Decoupling Failure Pathways in Li-O 2 Cells Operated Under Lean Electrolyte Conditions

The operation of lithium-oxygen (Li-O 2 ) batteries under lean electrolyte conditions offers higher energy density but leads to rapid degradation and short cycle life. Although cathode passivation and electrolyte decomposition occur in all regimes, we show that under lean electrolyte conditions, failure is primarily driven by progressive electrolyte consumption at the lithium/solid electrolyte interphase (SEI), rather than by irreversible cathode passivation. Poor wetting of the lithium surface results in heterogeneous SEI growth and high local current densities, which accelerate electrolyte loss and cell failure. Strategies aimed at improving interfacial stability, including optimized wetting and SEI forming additives, significantly extend cycle life without compromising energy density. Our results establish anode-electrolyte interactions as the dominant degradation mechanism under lean electrolyte conditions, and emphasize the need to engineer a stable Li/SEI interface for long-lasting Li-O 2 batteries.

Córdoba, Daniel [Argonne National Laboratory (ANL)↗
DOE OSTI2026

Improving creep resistance of Al-0.27Zr-0.08Sn (wt%) via cold swaging while maintaining high electrical conductivity

This study investigates the effect of mechanical cold work (0, 50, and 90% cross-sectional area reduction via swaging) on the creep properties of cast aluminum alloys with high electrical conductivity including high-purity Al (HP-Al), Al-0.15Zr (Al-Zr), and Al-0.27Zr-0.08Sn (Al-Zr-Sn, wt%). The Al-Zr alloy is strengthened by Zr in solid solution while the Al-Zr-Sn alloy is additionally strengthened by Al3Zr nanoprecipitates (8 nm diameter). After 90% cold swaging, the alloys exhibit grains elongated along the swaging direction with their widths ranging between 8 and 152 μm perpendicular to the swaging direction. Creep testing at 200 °C shows that the minimum creep rate of all 90% swaged alloys shows high sensitivity to stress, which can be modeled via a threshold stress σth. Increasing swaging magnitude from 0 to 50 to 90% in Al-Zr-Sn improves the creep resistance without reducing electrical conductivity. The formation of subgrains, increased dislocation density, and columnar grain structure in swaged alloys all enhance creep resistance. HP-Al swaged to 90% exhibits much lower creep resistance (σth = 18 MPa) due to subgrain coarsening and the absence of precipitates compared to Al-Zr (σth = 40 MPa) and Al-Zr-Sn (σth = 40 MPa), which maintain stable subgrain structures and benefit from solid solution strengthening and Al3Zr nanoprecipitates, respectively. Although Al3Zr precipitates are known to stabilize the deformed microstructure by pinning grain-boundaries, this work demonstrates that Zr in solid solution alone can effectively stabilize the deformed microstructure resulting in enhanced creep resistance. This effect of Zr solute on stabilizing grain boundaries for creep performance was not previously well-defined in the literature. Despite similar creep performances of Al-Zr and Al-Zr-Sn, the latter shows 70% higher room-temperature microhardness and slightly improved electrical conductivity (56%IACS (International Annealed Copper Standard) vs. 57%IACS, respectively). This work provides new insights into creep mechanisms of cold-worked Al–Zr alloys that will guide the design of heat-resistant Al conductors for high-demand applications.

Coello ramirez, Ismael [Northwestern University,]↗
DOE OSTI2026

Application of Ibuprofen Sodium Dihydrate for Thermochemical Energy Storage

Thermochemical energy storage (TCES) offers a transformative approach to address grid instability by harnessing reversible chemical reactions for efficient heat storage and release. Here, we introduce pharmaceutical organic salt hydrates as a class of materials with exceptional performance for low-grade waste heat recovery. We demonstrate ibuprofen sodium dihydrate (ISD) as an example organic hydrate exhibiting a dehydration temperature range of 60-110 °C and a remarkable dehydration enthalpy of up to 59.5 kJ/mol of water, ideally suited for capturing industrial and residential waste heat. Using rigorous multimodal characterization, including thermogravimetric analysis, differential scanning calorimetry, in-situ FTIR, in-situ PXRD, and NMR, we demonstrate ISD's superior thermal, chemical, and structural stability over 150 hydration-dehydration cycles, achieving an unprecedented cycling efficiency of ~99.9%. Compared to conventional inorganic salt hydrates like strontium chloride hexahydrate and calcium oxalate monohydrate, ISD showcases enhanced durability without deliquescence or pulverization, even under high-humidity conditions. In-situ analyses confirm the transition from ISD to ibuprofen sodium anhydrous (ISA) proceeds with structural reorganization, thereby combining the dehydration mechanism with phase transitions, resulting in higher energy storage capacity. Microstructural analyses reveal that repeated water intercalation and structural transitions aid in creating significant porosity that enhances water transport kinetics, further improving the hydration/dehydration performance. By combining the phase change and chemical dehydration mechanisms, ISD paves the way for designing a new class of organic salt hydrates, offering tunable properties to meet diverse thermal energy storage demands and supporting sustainable grid resilience.

Thangaraj, Kavin C.↗
DOE OSTI2026

Minimal dark 𝑆⁢𝑈⁡(2) origin of a massless Dirac neutrino

We propose a gauge-symmetry origin of a rank-two Dirac neutrino mass matrix that enforces one exactly massless neutrino, while being consistent with the oscillation data, as well as cosmological constraints. The mechanism relies on a minimal dark 𝑆⁢𝑈⁢(2) 𝐷 gauge symmetry under which one right-handed neutrinolike Weyl fermion is charged, thereby forbidding its Standard Model Yukawa coupling. Quantum consistency then fixes the minimal dark-sector completion: Cancellation of the Witten anomaly requires a second fermionic 𝑆⁢𝑈⁢(2) 𝐷 doublet, while a discrete 𝑍 4 symmetry that forbids Majorana masses allows the two dark doublets to form a vectorlike pair. This anomaly-free completion gives rise to a secluded, confining dark sector that can contain a potential dark matter candidate, linking the protected neutrino texture to dark infrared dynamics.

confinement↗