Publications and source records attributed to Zeng, Guosong.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Iridium Surface Oxide Affects the Nafion Interface in Proton-Exchange-Membrane Water Electrolysis

Proton-exchange-membrane water electrolyzer (PEMWE) catalyst layers consist of aggregates of catalyst particles (typically iridium) and ionomer (typically Nafion). Prior work suggests that the oxide form of Ir affects the kinetics of the oxygen-evolution reaction. However, because most catalyst-benchmarking studies are conducted ex situ in liquid electrolytes, it remains unclear how the ionomer is influenced by the catalyst oxide and affects overall cell performance. Using a suite of experimental techniques, we conduct fundamental investigations into model ink (catalyst and ionomer dispersed in solution) and thin-film systems to inform cell-level overpotential analysis as a function of three forms of Ir (metallic Ir m , oxyhydroxide IrOOH, and oxide IrO 2 ). Furthermore, nafion on Ir m has a high degree of phase separation and higher swelling, likely improving the ionic conductivity. Additionally, Nafion binds most strongly to IrOOH, likely yielding reduced kinetic overpotentials. These findings highlight the intricacies of the ionomer/Ir interface and provide insight into all catalyst-layer systems.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Oxynitrides enabled photoelectrochemical water splitting with over 3,000 hrs stable operation in practical two-electrode configuration

Solar photoelectrochemical reactions have been considered one of the most promising paths for sustainable energy production. To date, however, there has been no demonstration of semiconductor photoelectrodes with long-term stable operation in a two-electrode configuration, which is required for any practical application. Herein, we demonstrate the stable operation of a photocathode comprising Si and GaN, the two most produced semiconductors in the world, for 3,000 hrs without any performance degradation in two-electrode configurations. Measurements in both three- and two-electrode configurations suggest that surfaces of the GaN nanowires on Si photocathode transform in situ into Ga-O-N that drastically enhances hydrogen evolution and remains stable for 3,000 hrs. First principles calculations further revealed that the in-situ Ga-O-N species exhibit atomic-scale surface metallization. This study overcomes the conventional dilemma between efficiency and stability imposed by extrinsic cocatalysts, offering a path for practical application of photoelectrochemical devices and systems for clean energy.

14 SOLAR ENERGY↗
DOE OSTI2022

Best Practices in PEC Water Splitting: How to Reliably Measure Solar-to-Hydrogen Efficiency of Photoelectrodes

Photoelectrochemical (PEC) water splitting, which utilizes sunlight and water to produce hydrogen fuel, is potentially one of the most sustainable routes to clean energy. One challenge to success is that, to date, similar materials and devices measured in different labs or by different operators lead to quantitatively different results, due to the lack of accepted standard operating procedures and established protocols for PEC efficiency testing. With the aim of disseminating good practices within the PEC community, we provide a vetted protocol that describes how to prepare integrated components and accurately measure their solar-to-hydrogen (STH) efficiency (η STH ). This protocol provides details on electrode fabrication, η STH test device assembly, light source calibration, hydrogen evolution measurement, and initial material qualification by photocurrent measurements under monochromatic and broadband illumination. Common pitfalls in translating experimental results from any lab to an accurate STH efficiency under an AM1.5G reference spectrum are discussed. A III–V tandem photocathode is used to exemplify the process, though with small modifications, the protocol can be applied to photoanodes as well. Dissemination of PEC best practices will help those approaching the field and provide guidance for comparing the results obtained at different lab sites by different groups.

08 HYDROGEN↗
DOE OSTI2022

Long-Term Stability Metrics of Photoelectrochemical Water Splitting

Photoelectrochemical (PEC) water splitting, one of the most promising technologies for clean hydrogen generation, has drawn considerable attention over the past few decades. Achieving simultaneous highly efficient and stable unassisted PEC water splitting has been the “holy grail” in clean and renewable fuel generation. State-of-the-art photoelectrodes have shown relatively high efficiencies (∼10–20%). Still, their stability is limited due to photoelectrode chemical instability, electrolyte resistance, mass transfer issues, and an often unoptimized experimental setup. In this work, we present a framework and a set of protocols for conducting long-term stability experiments and further provide details on several critical factors such as light source calibration, choosing the right counter electrode, the configuration of the PEC cell, and photoelectrode sample preparation.

08 HYDROGEN↗
DOE OSTI2021

Nanoscale Confinement of Photo-Injected Electrons at Hybrid Interfaces

A prerequisite for advancing hybrid solar light harvesting systems is a comprehensive understanding of the spatiotemporal dynamics of photoinduced interfacial charge separation. Here, we demonstrate access to this transient charge redistribution for a model hybrid system of nanoporous zinc oxide (ZnO) and ruthenium bipyridyl chromophores. The site-selective probing of the molecular electron donor and semiconductor acceptor by time-resolved X-ray photoemission provides direct insight into the depth distribution of the photoinjected electrons and their interaction with the local band structure on a nanometer length scale. Our results show that these electrons remain localized within less than 6 nm from the interface, due to enhanced downward band bending by the photoinjected charge carriers. This spatial confinement suggests that light-induced charge generation and transport in nanoscale ZnO photocatalytic devices proceeds predominantly within the defect-rich surface region, which may lead to enhanced surface recombination and explain their lower performance compared to titanium dioxide (TiO 2 )-based systems.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Facet‐Selective Deposition of Ultrathin Al 2 O 3 on Copper Nanocrystals for Highly Stable CO 2 Electroreduction to Ethylene

Abstract Catalysts based on Cu nanocrystals (NCs) for electrochemical CO 2 ‐to‐C 2+ conversion with high activity have been a subject of considerable interest, but poor stability and low selectivity for a single C 2+ product remain obstacles for realizing sustainable carbon‐neutral cycles. Here, we used the facet‐selective atomic layer deposition (FS‐ALD) technique to selectively cover the (111) surface of Cu NCs with ultrathin Al 2 O 3 to increase the exposed facet ratio of (100)/(111), resulting in a faradaic efficiency ratio of C 2 H 4 /CH 4 for overcoated Cu NCs 22 times higher than that for pure Cu NCs. Peak performance of the overcoated catalyst (Cu NCs/Al 2 O 3 ‐10C) reaches a C 2 H 4 faradaic efficiency of 60.4 % at a current density of 300 mA cm −2 in 5 M KOH electrolyte, when using a gas diffusion electrode flow cell. Moreover, the Al 2 O 3 overcoating effectively suppresses the dynamic mobility and the aggregation of Cu NCs, which explains the negligible activity loss and selectivity degradations of Cu NCs/Al 2 O 3 ‐10C shown in stability tests.

Li, Hui↗
DOE OSTI2021

Facet-Selective Deposition of Ultrathin Al 2 O 3 on Copper Nanocrystals for Highly Stable CO 2 Electroreduction to Ethylene.

Catalysts based on Cu nanocrystals (NCs) for electrochemical CO 2 -to- 2+ conversion with high activity have been a subject of considerable interest, but poor stability and low selectivity for a single C 2+ product remain obstacles for realizing sustainable carbon-neutral cycles. In this study, we used the facet-selective atomic layer deposition (FS-ALD) technique to selectively cover the (111) surface of Cu NCs with ultrathin Al 2 O 3 to increase the exposed facet ratio of (100)/(111), resulting in a faradaic efficiency ratio of C 2 H 4 /CH 4 for overcoated Cu NCs 22 times higher than that for pure Cu NCs. Peak performance of the overcoated catalyst (Cu NCs/Al 2 O 3 -10C) reaches a C 2 H 4 faradaic efficiency of 60.4 % at a current density of 300 mA cm -2 in 5 M KOH electrolyte, when using a gas diffusion electrode flow cell. Moreover, the Al 2 O 3 overcoating effectively suppresses the dynamic mobility and the aggregation of Cu NCs, which explains the negligible activity loss and selectivity degradations of Cu NCs/Al 2 O 3 -10C shown in stability tests.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Nanoporous Iridium Nanosheets for Polymer Electrolyte Membrane Electrolysis

The growth of the hydrogen economy is predicated on advancements in electrochemical energy technologies, with water electrolysis as a key component to the technological portfolio. Much of the focus on anode catalyst development for polymer electrolyte membrane water electrolyzers (PEMWE) is centered on activity as controlled by compositional and morphological impacts on reactant/intermediate/product adsorption. However, the effectiveness of this strategy is found to be limited upon integration of these materials into PEMWE membrane electrode assemblies (MEA). Regardless of catalyst activity, the combination of electrode inhomogeneity, ionomer integration, and high density of oxide-oxide interfaces yields significant performance losses associated with poor catalytic electrode conductivity. Here many of these limitations are addressed through the development of a unique catalyst morphology composed of nanoporous Ir nanosheets (npIr(x)-NS) that exhibit high catalytic activity for the anodic oxygen evolution reaction and superior electrode electronic conductivity in comparison to a commercial IrO2 nanoparticle catalyst. The utility of the npIr(x)-NS is demonstrated through incorporation into PEMWE MEAs where their performance exceeds that of commercial catalyst coated membranes at loadings as low as 0.06 mg(Ir) cm(-2) while exhibiting a negligible loss in performance following 50 000 accelerated stress test cycles.

Polymer Electrolyte Membrane Electrolysis↗
DOE OSTI2021

CO 2 reduction on pure Cu produces only H 2 after subsurface O is depleted: Theory and experiment

Significance Electrochemical reduction of CO 2 to fuels and valuable chemicals is a global imperative to address energy and climate challenges. Despite enormous efforts, there is not yet a commercial process. The best catalyst remains Cu metal, but a great deal of controversy revolves around the role of the presence of oxygen in the material. We combine theory and experiments to show that pure Cu without subsurface oxygen leads to no organic products. Thus, maintaining substantial oxygen at Cu surfaces is essential for long-term reduction of CO 2 to organics.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 1a Raw Data

10 hours chronoamperometry (CA) testing under 1 sun illumination and constant bias at -0.6 V vs RHE, the corresponding Faradaic efficiency reveals a self-improving nature of GaN, inset: CA testing on bare Si for 5 hours under 1 sun illumination and -0.6 V vs RHE, this bare Si photocathode rapidly drops down to < 0.05 mA/cm2 within an hour. Both CA testing performed in 0.5 M H2SO4 (pH=0.4).

photocathode↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 1c Raw Data

Intermittent chronoamperometry (CA) testing was performed on Si/GaN photocathode in hourly manner. The LSV scan at 0 hour, 1 hour CA, 2 hours CA, 3 hours CA, 4 hours CA, 6 hours CA, 8 hours CA and 10 hours CA were recorded to track the changes of the photoelectrochemica (PEC) performance of the photocathode. The scan range was set to be 0V vs open circuit voltage (Eoc) to -0.7V vs RHE. Test was performed under one sun illumination in 0.5M H2SO4 (pH=0.4).

photocathode↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 1d Raw Data

Fig1d results were obtained using a 3-electrode configuration with IrOx as the counter electrode and saturated calomel electrode as the reference electrode. Two Si/GaN photocathodes were compared. Sample #1 (named as S#1) was the as-received sample, and sample #2 (named as S#2) was CA tested for 4 hours under same testing conditions described in Fig.1a. The PEC performance (J-V curve) was recorded for both samples. Then a photodeposition of Pt was performed on both samples, each loading time was set to be 5 minutes, then the J-V curve was recorded to track the changes of the performance. The Pt photodeposition was stopped until the J-V curve won't shift (the maximum onset potential was achieved). The results show that, S#1 needs at least 20 minutes of Pt photodeposition to achieve its best PEC performance while S#2, which is after CA testing, only needs 5 minutes of Pt photodeposition to achieve its best PEC performance.

photocathode↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 2b Raw Data

Photoconductive atomic force microscopy (PC-AFM) measurements were conducted on Si/GaN samples. PeakForce TUNA mode was used to acquire the morphology and current simultaneously. A PtIr conductive probe with spring constant of 2.8 Nm-1 was used for the scanning. A white light source was used to illuminate the surface during the acquisition. Line scan extracting the topography and photocurrent from a as-received Si/GaN sample. The topography mapping is 2 × 2 µm2. The sample bias was 0.4V and this photoconductive AFM measurement was performed under white light front illumination with an angle.

photocathode↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 2d Raw Data

After 10 hrs of chronoamperometry (CA) photoconductive atomic force microscopy (PC-AFM) measurements were conducted on Si/GaN samples using a commercial AFM system (Bruker Dimension Icon). PeakForce TUNA mode was used to acquire the morphology and current simultaneously. A PtIr conductive probe with spring constant of 2.8 Nm-1 was used for the scanning. A white light source was used to illuminate the surface during the acquisition. Line scan extracting the topography and photocurrent from this 10 hour CA tested Si/GaN sample. The topography mapping is 2 × 2 µm2. No sample bias was applied and this photoconductive AFM measurement was performed under white light front illumination with an angle.

photocathode↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 3c Raw Data

XPS after 0hr of chronoampometry. Surface chemical composition and valence band structure of GaN were obtained by X-ray photoemission spectroscopy (XPS) on a Kratos Axis Ultra DLD system at a takeoff angle of 0° relative to the surface normal. An Al Kα source (hν = 1486.6 eV) was used to excite the core level electrons. Pass energy of 20 eV was used for the narrow scan of core levels and valence band spectra, and step size of 0.05 eV and 0.025 eV, respectively. The Spectral fitting was conducted using CasaXPS analysis software. The binding energy scales of all core levels were corrected to the N 1s of Ga – N bond at 397.8 eV. XPS O1s core level spectra from as-received Si/GaN sample, and deconvolution shows O - Ga bond and OH - H2O bond.

photocathode↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 3d Raw Data

XPS of Si/GaN photocathode after 1 hour chronoamperometry (CA) testing. Surface chemical composition and valence band structure of GaN were obtained by X-ray photoemission spectroscopy (XPS) on a Kratos Axis Ultra DLD system at a takeoff angle of 0° relative to the surface normal. An Al Kα source (hν = 1486.6 eV) was used to excite the core level electrons. Pass energy of 20 eV was used for the narrow scan of core levels and valence band spectra, and step size of 0.05 eV and 0.025 eV, respectively. The Spectral fitting was conducted using CasaXPS analysis software. The binding energy scales of all core levels were corrected to the N 1s of Ga – N bond at 397.8 eV. X-ray photoemission spectroscopy (XPS) O1s core level spectra from 1 hour chronoamperometry (CA) tested Si/GaN sample, and deconvolution shows O - Ga bond, O - N - Ga bond, and OH - H2O bond.

photocathode↗
DOE OSTI2021

Photoelectrochemically Self Improving Si/GaN Photocathode: Figure 3f Raw Data

XPS of Si/GaN photocathode after 10 hour chronoamperometry (CA) testing. Surface chemical composition and valence band structure of GaN were obtained by X-ray photoemission spectroscopy (XPS) on a Kratos Axis Ultra DLD system at a takeoff angle of 0° relative to the surface normal. An Al Kα source (hν = 1486.6 eV) was used to excite the core level electrons. Pass energy of 20 eV was used for the narrow scan of core levels and valence band spectra, and step size of 0.05 eV and 0.025 eV, respectively. The Spectral fitting was conducted using CasaXPS analysis software. The binding energy scales of all core levels were corrected to the N 1s of Ga – N bond at 397.8 eV. XPS O1s core level spectra from 10 hours CA tested Si/GaN sample, and deconvolution shows O - Ga bond, O - N - Ga bond and OH - H2O bond.

photocathode↗