Metal–Organic Framework-derived Atomic Metal Sites Promoting Sulfur Cathode for All-Solid-State Lithium–Sulfur Batteries

Abstract

All-solid-state lithium–sulfur batteries (ASSLSBs) offer high energy density and intrinsic safety; however, they still face major challenges, including sluggish redox kinetics and poor sulfur utilization. Incorporating conductive materials into sulfur cathodes is an effective strategy to mitigate these limitations. Here, a highly conductive cobalt–nitrogen–doped carbon (Co–NC) derived from a metal–organic framework (MOF) is introduced to accelerate charge transfer and promote reversible sulfur conversion. Co−NC provides atomically dispersed Co–N sites and conductive carbon pathways that correlate with improved charge transfer, sulfur utilization, and rate capability. Co–NC@S cathode delivers 1499 mAh g–1 at C/20 with a high sulfur loading (5 mg cm–2) and retains 1292 mAh g–1 after five cycles (vs 443 mAh g–1 without Co–NC). Moreover, Co–NC derived ASSLSB achieves 903 mAh g–1 at 5C at 60 °C. This work provides a practical and effective approach to develop high energy, high-rate ASSLSBs.