Single‐photon emitters in PECVD‐grown silicon nitride films: from material growth to photophysical properties

Abstract

Abstract Silicon nitride (SiN) is a key material for quantum photonics due to its wide transparency window, high refractive index, low optical losses, and semiconductor foundry compatibility. We study the formation of single‐photon emitters in SiN films grown by plasma‐enhanced chemical vapor deposition (PECVD), exploring their photophysical properties and dependence on growth conditions. Emitters were observed across the entire range of nitrogen‐to‐silicon precursor ratios, from silicon‐rich to nitrogen‐rich conditions, enabled by the low background fluorescence. We demonstrate single‐photon emitters in SiN films with a higher refractive index (1.8–1.9) compared to our previous reports (∼1.7). Notably, nitrogen‐rich, thinner films yield particularly bright emitters with shorter emission lifetimes, likely due to more efficient annealing. Silicon‐rich SiN films exhibit red‐shifted emission, suggesting that composition may provide a mechanism for wavelength tuning. These findings establish the feasibility of emitters formation in foundry standard PECVD tools, advancing the scalability and lab‐to‐fab transition of SiN‐based quantum photonic technologies.